Self-Lubricating PTFE-Based Composites with Black Phosphorus Nanosheets
- 176 Downloads
Black phosphorus (BP), a newly emerging two-dimensional material, has recently received considerable attention. Our recent work suggested that BP nanosheets exhibit extraordinary mechanical and lubrication properties. In the present work, the tribological properties of polyetheretherketone (PEEK)/polytetrafluoroethylene (PTFE) and carbon fiber (CF)/PTFE composites with BP nanosheets have been investigated. The morphologies and surface element distribution of the worn tracks of the tribopair surfaces were examined by different analytical techniques. The results show that the coefficients of friction (COFs) of both the PEEK/PTFE and CF/PTFE composites decreased dramatically after the addition of BP nanosheets, and the minimum COF of the composite was 0.04, which was a quarter of that of the PTFE composite without BP nanosheets. After BP nanosheets were added into the composites, the wear rate of the PTFE/PEEK composite decreased dramatically, while that of the CF/PTFE composite increased significantly with the increase in the filler concentration. The analysis of the lubrication mechanism of the PTFE composite with BP nanosheets suggested that BP nanosheets could be constantly supplied into the contact area and gradually formed a BP film composed of phosphorus oxide and phosphoric acid on the counterpart surface instead of the formation of PTFE transfer film. The formed BP transfer film promoted the friction reduction and the disappearance of the adhesive wear.
KeywordsPTFE composite Black phosphorus PEEK Carbon fiber Friction and wear
This work was financially supported by the National Natural Science Foundation of China (Grant Nos. 51527901, 51475256, 51605249), and Beijing Natural Science Foundation of China (Grant No. 3182010).
- 1.Lewis, M.W.J.: Friction and wear of PTFE-based reciprocating seals. Lubr. Eng. 42, 152–158 (1986)Google Scholar
- 10.Wang, Q., Song, F., Zhang, X., Zhao, G., Wang, T.: Impact of fillers and counterface topography on wear behavior of PTFE polymers for ultrasonic motor. J. Appl. Polym. Sci. 134, 44835(44831)–44835(44810) (2017)Google Scholar
- 12.Shi, Y.J., Feng, X., Diao, X.S., Wang, H.Y., Lu, X.H.: Tribological and mechanical properties of carbon nanofiber-filled PTFE composites. Key Eng. Mater. 121–123, 975–978 (2007)Google Scholar
- 17.Qu, S., Penaranda, J., Wang, S.-S.: Tribological behavior of PTFE/PEEK composite. In: Technical Conference (2016)Google Scholar
- 28.Xia, F., Wang, H., Jia, Y.: Rediscovering black phosphorus as an anisotropic layered material for optoelectronics and electronics. Nat. Commun. 5, 4458 (2014)Google Scholar
- 30.Jiang, J.W., Park, H.S.: Negative poisson’s ratio in single-layer black phosphorus. Nat.Commun. 5, 4727 (2014)Google Scholar