Novel Pt Electrocatalysts: Multifunctional Composite Supports for Enhanced Corrosion Resistance and Improved CO Tolerance
- 116 Downloads
The electrochemical peculiarities of novel 20 wt% Pt electrocatalysts supported on Ti0.6Mo0.4O2–C composite materials in low-potential CO oxidation reaction (LPCOR) were investigated. The oxidation of CO on the Mo-containing Pt-based catalyst commences at exceptionally low potential values (ca. 100 mV). The results suggest that only CO adsorbed on specific Pt sites, where Pt and Mo atoms are in atomic closeness, can be oxidised below 400 mV potential. When the weakly bounded CO is oxidized, some hydrogen adsorption can take place on the released surface, although this amount is much smaller than in the case of a CO-free Pt surface. The Pt/Ti0.6Mo0.4O2–C catalyst loses its activity in LPCOR when Mo becomes oxidized (above ca. 400 mV). Accordingly, presence of Mo species in lower oxidation state than 6+ is supposed to have crucial role in CO oxidation. Nevertheless, re-reduction of oxidized Mo species formed above 400 mV is strongly hindered when adsorbed CO species are still present. Note that COads species can be completely removed only above 550 mV. Oxidized Mo species can be re-reduced and the activity in the LPCOR can be restored if the platinum surface is CO-free. Clear correlation between the so-called “pre-peak”, the molybdenum redox phenomenon and the CO tolerance of the 20 wt% Pt/Ti0.6Mo0.4O2–C system was established. Better performance of the Pt/Ti0.6Mo0.4O2–C electrocatalyst compared to commercially available reference Pt/C and state-of-art CO-tolerant PtRu/C (Quintech) catalysts was also demonstrated.
KeywordsConducting Ti-based mixed oxides TiMoOx Composite materials Pt electrocatalysts CO-tolerance
The research within project No. VEKOP-2.3.2-16-2017-00013 was supported by the European Union and the State of Hungary, co-financed by the European Regional Development Fund. Financial support by the OTKA-project [Grant Number K112034 (István Bakos)] is greatly acknowledged.
- 13.Subban CV, Zhou Q, Hu A, Moylan TE, Wagner FT, DiSalvo FJ (2010) Sol-gel synthesis, electrochemical characterization, and stability testing of Ti0.7W0.3O2 nanoparticles for catalyst support applications in proton-exchange membrane fuel cells. J Am Chem Soc 132:17531–17536CrossRefPubMedGoogle Scholar
- 35.Wang Y, Fachini ER, Cruz G, Zhu Y, Ishikawa Y, Colucci JA, Cabrera CR (2001) Effect of surface composition of electrochemically codeposited platinum/molybdenum oxide on methanol oxidation. J Electrochem Soc 148:C222-C226Google Scholar
- 39.Borbáth I, Pászti Z, Gubán D, Vass Á, Tompos A (2015) CO-toleráns anódoldali elektrokatalizátor fejlesztése PEM tüzelőanyag-cellákhoz. Magyar Kémiai Folyóirat 121:80–88Google Scholar
- 42.Fairley N (2006) CasaXPS: Spectrum Processing Software for XPS, AES and SIMS, Version 2.3.13. Casa Software Ltd, Cheshire, http://www.casaxps.com
- 44.Guillén-Villafuerte O, García G, Rodríguez JL, Pastor E, Guil-López R, Nieto E, Fierro JLG (2013) Preliminary studies of the electrochemical performance of Pt/X@MoO3/C (X = Mo2C, MoO2, Mo0) catalysts for the anode of a DMFC: influence of the Pt loading and Mo-phase. Int J Hydrogen Energy 38:7811–7821CrossRefGoogle Scholar
- 62.Anderson AB, Neshev NM (2002) Mechanism for the electro-oxidation of carbon monoxide on platinum, including electrode potential dependence. J Electrochem Soc 149:E383-E388Google Scholar
- 65.Lu J, Li WS, Du JH, Fu JM (2005) Co-deposition of Pt-HxMoO3 and its catalysis on methanol oxidation in sulfuric acid solution. J New Mat Electrochem Syst 8:5–14Google Scholar