Catalytic peroxide fractionation processes for the green biorefinery of wood
- 2 Downloads
A kinetic study and optimization of pine wood peroxide fractionation in the medium acetic acid–water over TiO2 catalyst were accomplished for the first time. Kinetic regularities and the product composition of green processes of catalytic peroxide fractionation of softwood (pine, abies, larch) and hardwood (aspen, birch) over 1 wt% TiO2 catalyst in the acetic acid–water medium were compared at the temperature range 70–100 °C. For all type of wood, the processes of peroxide delignification are described by the first order equations and their activation energies are varied at the range 76–94 kJ/mol. According to FTIR, XRD, SEM, NMR data, the cellulosic products of peroxide delignification have a structure similar to microcrystalline cellulose regardless of the nature of wood. Soluble products are presented by organic acid and monosaccharides. The scheme of green biorefinery of pine wood based on extractive-catalytic fractionation of wood biomass on microcrystalline cellulose, hemicelluloses, aromatic and aliphatic acids, monosaccharides, turpentine and rosin was developed. Green and non-toxic reagents and solid catalyst are used in the developed scheme of biorefinery.
KeywordsSoftwood Hardwood Peroxide fractionation Catalyst TiO2 Kinetics Optimization Green biorefinery
This work is a part of GDRI “Biomass” between France and Russia.
- 1.Introduction to Chemicals from Biomass (2008) Wiley series in renewable resources. John Wiley & Sons, Ltd, ChichesterGoogle Scholar
- 3.Fengel D, Wegener G (1984) Wood chemistry, ultrastracture, reactions. Walter de Gruter, BerlinGoogle Scholar
- 9.de Long E, Hidson A, Walsh P (2013) Task 42. Biorefinery. In: Report IEA bioenergyGoogle Scholar
- 11.Van den Bosch S, Schutyser W, Vanholme R, Driessen T, Koelewijn SF, Renders T, De Meester B, Huijgen WJJ, Dehaen W, Courtin CM, Lagrain B, Boerjan W, Sels BF (2015) Reductive lignocellulose fractionation into soluble lignin-derived phenolic monomers and dimers and processable carbohydrate pulps. Energy Environ Sci 8(6):1748–1763CrossRefGoogle Scholar
- 20.Suchy M, Argyropoulos D (2002) Catalysis and activation of oxygen and peroxide delignification of chemical pulps: a review. Tappi 1(2):1–18Google Scholar
- 26.Fan M, Dai D, Huang B (2012) Fourier transform infrared spectroscopy for natural fibres. In: Salih S (ed) International conference on innovative technologies (IN-TECH 2012). Rejeka, Croatia, pp 45–68Google Scholar
- 30.Zuckerstatter G, Schild G, Wollboldt P, Roeder T, Weber HK, Sixta H (2009) The elucidation of cellulose supramolecular structure by 13C CP-MAS NMR. Lenzing Ber 87:38–46Google Scholar
- 33.Alonso DM, Hakim SH, Zhou S, Won W, Hosseinaei O, Tao J, Garcia-Negron V, Motagamwala AH, Mellmer MA, Huang K, Houtman CJ, Labbé N, Harper DP, Maravelias CT, Runge T, Dumesic JA (2017) Increasing the revenue from lignocellulosic biomass: maximizing feedstock utilization. Sci Adv 3(5):e1603301CrossRefPubMedPubMedCentralGoogle Scholar
- 34.Silvestre AJ, Gandini A (2008) Monomers, polymers and composites from renewable resources. Elsevier, AmsterdamGoogle Scholar