Article
  • 11 Downloads

Abstract

The endothermic reaction of the fuel is used as a cooling system for hypersonic aircraft. At this time, the zeolite catalyst is used for an effective endothermic reaction. In this work, the effect of metal foam catalyst on the composition of the product was investigated by using zeolite with a metal foam support as a catalyst for the endothermic reaction. The metal foam support was made with NiCrAl alloy. The characteristics of the zeolite catalyst were confirmed by X-ray diffraction (XRD) analysis, Fourier transform infrared spectroscopy (FT-IR) analysis and NH3-Temperature programmed desorption (NH3-TPD) analysis. The composition of the product of the endothermic reaction was analyzed by GC–MS. In experiments of H-ZSM-5 catalyst pellet, the conversion of methylcyclohexane (MCH) was about 82%. While, in the case of the H-ZSM-5 catalyst supported with the metal foam, the conversion of MCH was about 93% and the conversion was 11% higher than that of the zeolite catalyst itself. In addition, experimental results with different temperatures showed that MCH conversion and aromatic hydrocarbon increased with increasing temperature. On the other hand, low hydrocarbons increased when increasing from 598 to 633 K, but decreased when increasing to 673 K.

Keywords

Decomposition reaction Methylcyclohexane H-ZSM-5 Zeolite NiCrAl Metal foam Batch reactor 

Notes

Acknowledgements

This study was conducted as part of the Basic Research Project (Pure-17-20) of Defense Acquisition Program Administration.

References

  1. 1.
    Sicard M, Grill M, Raepsaet B, Ser F (2008) Comparison between thermal and catalytic cracking of a model endothermic fuel. AIAA-2008-2622Google Scholar
  2. 2.
    Petley DH, Jones SC (1992) Thermal management for a Mach 5 cruise aircraft using endothermic fuel. J Aircraft 29(3):384–389CrossRefGoogle Scholar
  3. 3.
    Huang H, Sobel DR, Spadaccini LJ (2002) Endothermic heat-sink of hydrocarbon fuels for SCRAMJET cooling. AIAA-2002-3871Google Scholar
  4. 4.
    Sicard M, Raepsaet B, Ser F, Masson C (2005) Determination of the decomposition products of a n-alkane endothermic fuel under supercritical conditions. AIAA-2005-3402Google Scholar
  5. 5.
    Fan XJ, Zhong FQ, Yu G, Li JG, Sung CJ (2009) Catalytic cracking and heat sink capacity of aviation kerosene under supercritical conditions. J Propuls Power 25(6):1226–1232CrossRefGoogle Scholar
  6. 6.
    Edwards T (2006) Cracking and deposition behavior of supercritical hydrocarbon aviation fuels. Combust Sci Techol 178:307–334CrossRefGoogle Scholar
  7. 7.
    Kim JY, Park SH, Chun BH, Jeong BH, Han JS, Kim SH (2012) Improvement of the heats of reaction in endothermic reactions of methylcyclohexane with zeolites. Catal Today 185:47–53CrossRefGoogle Scholar
  8. 8.
    Huang B, Bai P, Neurock M, Davis RJ (2017) Conversion of n-hexane and n-dodecane over H-ZSM-5, HY and Al-MCM-41 at supercritical conditions. Appl Catal A Gen 546:149–158CrossRefGoogle Scholar
  9. 9.
    Lander H, Nixon AC (1971) Endothermic fuels for hypersonic vehicles. J Aircraft 8(4):200–207CrossRefGoogle Scholar
  10. 10.
    Wan Z, Li GK, Wang CF, Yang H, Zhang DK (2018) Relating coke formation and characteristics to deactivation of ZSM-5 zeolite in methanol to gasoline conversion. Appl Catal A Gen 549:141–151CrossRefGoogle Scholar
  11. 11.
    Lee KH, Lee SH, Jun YS, Choi MK (2017) Cooperative effects of zeolite mesoporosity and defect sites on the amount and location of coke formation and its consequence in deactivation. J Catal 347:222–230CrossRefGoogle Scholar
  12. 12.
    Maurice LQ, Edwards T, Griffiths J (2001) Liquid hydrocarbon fuels for hypersonic propulsion. Scramjet Propuls 189:757–822Google Scholar
  13. 13.
    Usman MR, Cresswell DL, Garforth AA (2010) Kinetics of methylcyclohexane dehydrogenation and reactor simulation for “On-board” hydrogen storage. Thesis submitted to The University of Manchester for the degree of Doctor of Philosophy, p. 139Google Scholar
  14. 14.
    Moljord K, Magnoux P, Guisnet M (1995) Coking, aging and regeneration of zeolites XVI. Influence of the composition of HY zeolites on the removal of coke through oxidative treatment. Appl Catal A Gen 121(2):245–259CrossRefGoogle Scholar
  15. 15.
    Qu S, Liu G, Meng F, Wang L, Zhang X (2011) Catalytic cracking of supercritical n-dodecane over wall-coated HZSM-5 with different Si/Al ratio. Energy Fuels 25:2808–2814CrossRefGoogle Scholar
  16. 16.
    Qiu Y, Hou X, Liu G, Wang L, Zhang X (2017) Fast recovery of Brønsted acid sites lost during high-temperature calcination in HZSM-5. Microporous Mesoporous Mater 243:176–185CrossRefGoogle Scholar

Copyright information

© Akadémiai Kiadó, Budapest, Hungary 2019

Authors and Affiliations

  • Min Chang Shin
    • 1
  • Jung In Moon
    • 2
  • Ji Hoon Jung
    • 2
  • Byung Hun Jeong
    • 3
  • Jung Hoon Park
    • 1
  1. 1.Department of Biochemical and Chemical EngineeringDongguk UniversitySeoulSouth Korea
  2. 2.Department of Chemical EngineeringKyonggi UniversitySuwonSouth Korea
  3. 3.Agency for Defense DevelopmentDaejeonSouth Korea

Personalised recommendations