Mechanical Synthesis of Tantalum Borides and Modeling of Solid Solutions of Boron in Tantalum

  • M.P. Savyak
  • O.B. Melnick
  • M.A. Vasil’kivska
  • I.I. Timofeeva
  • V.I. Ivchenko
  • I.V. Uvarova
THEORY, MANUFACTURING TECHNOLOGY, AND PROPERTIES OF POWDERS AND FIBERS
  • 10 Downloads

Two mechanisms of mechanochemical solid-phase reactions are observed when tantalum and boron powder mixtures are ground in the same conditions but at different contents of the starting components. The substitutional solid solution decomposes at 50 at.% B in the starting mixture and stimulates the self-propagating mechanochemical synthesis reaction to form the TaB phase. The supersaturated interstitial solid solution, whose formation is controlled by the diffusion of boron atoms into tantalum, shows up at a boron content of 66 at.% and gradually decomposes to form the TaB2 phase. Formalism is proposed for estimating the free Gibbs energy of the interstitial and substitutional solid solutions with the regular solution model. The use of this formalism shows that grinding of the tantalum and boron powders in a planetary-ball mill produces a combined interstitial and substitutional solid solution (two boron atoms substitute one tantalum atom) at the initial stage. Both the substitutional and interstitial mechanisms lead to decrease in the solution’s Gibbs energy. When the substitutional solid solution prevails over the interstitial solution, the Gibbs energy of the substitutional solution becomes minimal at 50 at.% B in tantalum and causes its disintegration.

Keywords

mechanical alloying tantalum borides crystalline lattice solid solutions 

References

  1. 1.
    G.K. Moiseev and A.L. Ivanovsky, “Standard enthalpies of forming related compounds in the metal–boron systems,” Izv. Chelyab. Nauch. Ts., 29, No. 3, 5–9 (2005).Google Scholar
  2. 2.
    C.L. Yeh and H.J. Wang, “A comparative study on combustion synthesis of Ta–B compounds,” Ceram. Int., 37, No. 5, 1569–1573 (2011).CrossRefGoogle Scholar
  3. 3.
    L. Takacs, “Self-sustaining reactions induced by ball milling,” Prog. Mater. Sci., 47, 355–414 (2002).Google Scholar
  4. 4.
    G.B. Schafer and P.G. McCormick, “Process modeling of the mechanics of mechanical alloying in SHS research,” Metall. Trans. A, 22A, 3019–3024 (1991).Google Scholar
  5. 5.
    A. Calca and A.P. Radlinski, “Formation of TiB2 by mechanical alloying,” J. Less-Common Met., 161, L23–L26 (1990).Google Scholar
  6. 6.
    M.P. Savyak, A.B. Melnik, Yu.M. Solonin, A.V. Kotko, I.I. Timofeeva, and I.V. Uvarova, “Mechanosynthesis of nanodispersed titanium diboride,” Powder Metall. Met. Ceram., 53, No. 9–10, 497–504 (2014).Google Scholar
  7. 7.
    G.M. Makarenko, L.A. Krushinskaya, I.I. Timofeeva, V.Yu. Matsera, M.A. Vasil’kovskaya, and I.V. Uvarova, “Formation of diborides of groups IV–VI transition metals during mechanochemical synthesis,” Powder Metall. Met. Ceram., 53, No. 9–10, 514–521 (2015).Google Scholar
  8. 8.
    K. Iizumi, C. Sekiya, S. Okad, K. Kudou, and T. Shishidо, “Mechanochemically assisted preparation of NbB2 powder,” J. Eur. Ceram. Soc., 26, 635–638 (2006).Google Scholar
  9. 9.
    M.A. Morris and D.G. Morris, “Competition between amorphous or intermetallic phase formation during ball-milling,” Colloq. Phys., Colloq. C4, 51, No. 14, 151–155 (1990).Google Scholar
  10. 10.
    R.A. Andrievskii and Ya.S. Umanskii, Interstitial Phases [in Russian], Moscow (1977), p. 239.Google Scholar
  11. 11.
    R. Kiessling, “The borides of tantalum,” Acta Chem., 3, 603–615 (1949).Google Scholar
  12. 12.
    B. Zhang, S. Liao, H. Xie, X. Yuan, and X. Shu, “A subregular model for calculating the mixing enthalpies in 10 binary IIB–IIIB alloy systems,” Europhys. Lett., 89, No. 5, 56002–56016 (2010).CrossRefGoogle Scholar
  13. 13.
    A. Takeuchi and A. Inoue, “Calculations of mixing enthalpy and mismatch entropy for ternary amorphous alloys,” Mater. Trans., 41, 1372–1378 (2000).Google Scholar
  14. 14.
    WebElements Periodic Table: the periodic table on the web. URL: http://www.webelements.com/.
  15. 15.
    A. Takeuchi and A. Inoue, “Classification of bulk metallic glasses by atomic size difference, heat of mixing and period of constituent elements,” Mater. Trans., 46, 2817–2829 (2005).Google Scholar
  16. 16.
    H.J. Goldschmidt, Interstitial Alloys, Plenum Press, New York (1967).CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2018

Authors and Affiliations

  • M.P. Savyak
    • 1
  • O.B. Melnick
    • 2
  • M.A. Vasil’kivska
    • 1
  • I.I. Timofeeva
    • 1
  • V.I. Ivchenko
    • 1
  • I.V. Uvarova
    • 1
  1. 1.Frantsevich Institute for Problems of Materials ScienceNational Academy of Sciences of UkraineKyivUkraine
  2. 2.Kurdyumov Institute for Metal PhysicsNational Academy of Sciences of UkraineKyivUkraine

Personalised recommendations