Characterization of Oxide Scales Formed on Ferritic Stainless Steel 441 at 1,100 °C under water vapor
- 308 Downloads
This study focuses on the characterization of the oxide scales formed after different exposure times in the range of 2.5–20 min. A commercially available ferritic steel grade AISI 441 was exposed to wet argon at 1100 °C with 5, 9 and 13% H2O. Raman microspectroscopy, XRD, EDS and XPS were used to fully characterize the oxide scale. For all samples exposed for over 4 min, the scale was constituted of three layers in this order: a thin top layer of spinel phases (Fe,Cr,Mn)3O4 with local outgrowths; a second and main layer of Cr2O3 + (Mn,Cr)3O4; and finally a bottom layer of SiO2. The uncommon presence of Fe in the top layer was also observed.
KeywordsFerritic stainless steel Oxidation High temperature Short-term exposures Water vapor
The authors wish to thank Linde AG for financing this research. The help of L. Bellot-Gurlet for Raman microspectroscopy experiments was also sincerely appreciated.
- 1.P. Lacombe, B. Baroux, G. Béranger, Stainless steels, Chap. 12 (Les éditions de physiques. Les Ulis, 1993).Google Scholar
- 8.J. Hammer, S. Laney, R. Jackson, K. Coyne, F. Pettit and G. Meier, Oxidation of metals 67, 1–38 (2007).Google Scholar
- 11.C. D. Wagner, W. M. Riggs, L. E. Davis, J. F. Moulder and G. E. Mullenberg, Handbook of X-ray Photoelectron Spectroscopy, (Physical Electronics Division, Perkin-Elmer Corporation, Eden Prairie, 1979).Google Scholar
- 17.G. R. Holcomb and D. E. Alman, ScriptaMaterialia 54, 1821–1825 (2006).Google Scholar
- 20.M. Da Cunha Belo, M. Walls, N. E. Hakiki, J. Corset, E. Picquenard, G. Sagon, and D. Noel, Corrosion Science 40, 1998 (447–463).Google Scholar