Effect of PAA-coated magnetic nanoparticles on the performance of PVA-based hydrogels developed to be used as environmental remediation devices

  • Laura M. SanchezEmail author
  • Daniel G. Actis
  • Jimena S. Gonzalez
  • Pedro Mendoza Zélis
  • Vera A. Alvarez
Research Paper
  • 65 Downloads

Abstract

In the present work, the effect of the incorporation of polyacrylic acid (PAA)–coated magnetic nanoparticles (MNPs) on the performance of polyvinyl alcohol (PVA)–based hydrogels for water remediation was studied. Ferrogels from PVA and PAA-coated MNPs were prepared through the ecocompatible freezing–thawing physical cross-linking method, and then they were completely characterized. Two different lab-made PAA-coated iron oxide MNPs, characterized in a previous work, were prepared by coprecipitation method from two different low PAA molecular weights, Mw 1800 g/mol and 5000 g/mol. The effect of MNP content and the PAA Mw on ferrogel final properties was determined. In addition, adsorption of methylene blue (MB) and cadmium (Cd+2) was carried out to analyze the possible application of the developed materials as environmental remediation devices. The capture of a ferrogel by an external field occurs due to the force that the field gradient exerts on single magnetic particles, which is then transferred onto the polymer matrix. This force was measured as a function of the distance to a permanent magnet, and the condition to magnetically recover the sample was established. The results obtained demonstrated that the ferrogels presented in this work are able to adsorb heavy metals and then be magnetically separated.

Keywords

Magnetic hydrogel Ferrogel Iron oxide nanoparticles Nanocomposite Polyvinyl alcohol Polyacrylic acid Environmental remediation 

Notes

Acknowledgements

The authors acknowledge the collaborations made by Dra. Romina P. Ollier and Dra. M. Fernanda Horst.

Funding information

This study received funding from CONICET (PIP00617), Universidad Nacional de Mar del Plata, Universidad Nacional de La Plata (X807), ANPCyT (PICT 2014-3228 and PICT 2016-1905) and Fundación Bunge & Born.

Compliance with ethical standards

Conflict of interest

The authors declare that they have no conflict of interest.

References

  1. Ahmed EM (2015) Hydrogel: preparation, characterization, and applications: a review. J Adv Res 6:105–121.  https://doi.org/10.1016/j.jare.2013.07.006 CrossRefGoogle Scholar
  2. Alghanmi S, Al Sulami A, El-Zayat T et al (2015) Acid leaching of heavy metals from contaminated soil collected from Jeddaj, Saudi Arabia: kinetic and thermodynamics studies. Int Soil Water Conserv Res 3:196–208CrossRefGoogle Scholar
  3. Bardajee GR, Hooshyar Z, Rastgo F (2013) Kappa carrageenan-g-poly (acrylic acid)/SPION nanocomposite as a novel stimuli-sensitive drug delivery system. Colloid Polym Sci 291:2791–2803.  https://doi.org/10.1007/s00396-013-3018-6 CrossRefGoogle Scholar
  4. Bonhome Espinosa AB (2017) Hidrogeles magnéticos para aplicaciones biomédicas. Estudio de su biocompatibilidad y propiedades viscoelásticas Universidad de Granada (España)Google Scholar
  5. Byun H, Hong B, Nam SY, Jung SY, Rhim JW, Lee SB, Moon GY (2008) Swelling behavior and drug release of poly ( vinyl alcohol ) hydrogel cross-linked with poly ( acrylic acid ). Macromol Res 16:189–193CrossRefGoogle Scholar
  6. Chen NX, Zhang JH (2010) The role of hydrogen-bonding interaction in poly(vinyl alcohol)/ poly(acrylic acid) blending solutions and their films. Chinese J Polym Sci (Eng Ed) 28:903–911.  https://doi.org/10.1007/s10118-010-9167-x CrossRefGoogle Scholar
  7. Goiti E, Salinas MM, Arias G, Puglia D, Kenny JM, Mijangos C (2007) Effect of magnetic nanoparticles on the thermal properties of some hydrogels. Polym Degrad Stab 92:2198–2205.  https://doi.org/10.1016/j.polymdegradstab.2007.02.025 CrossRefGoogle Scholar
  8. Gonzalez JS, Alvarez VA (2011) The effect of the annealing on the poly(vinyl alcohol) obtained by freezing-thawing. Thermochim Acta 521:184–190.  https://doi.org/10.1016/j.tca.2011.04.022 CrossRefGoogle Scholar
  9. Gonzalez JS, Nicolás P, Ferreira ML, Avena M, Lassalle VL, Alvarez VA (2014) Fabrication of ferrogels using different magnetic nanoparticles and their performance on protein adsorption. Polym Int 63:258–265.  https://doi.org/10.1002/pi.4498 CrossRefGoogle Scholar
  10. Gonzalez J, Ponce A, Alvarez V (2016) Preparation and characterization of poly (vinylalcohol) / bentonite hydrogels for potential wound dressings. Adv Mater Lett 7:979–985.  https://doi.org/10.5185/amlett.2016.6888 CrossRefGoogle Scholar
  11. Gudman L, Peppas NA (1995) Preparation and characterization of pH-sensitive , interpenetrating networks of poly ( vinyl alcohol ) and poly ( acrylic acid ). J Appl Polym Sci 55:919–928.  https://doi.org/10.1002/app.1995.070550610 CrossRefGoogle Scholar
  12. Gupta S, Pramanik AK, Kailath A, Mishra T, Guha A, Nayar S, Sinha A (2009) Composition dependent structural modulations in transparent poly(vinyl alcohol) hydrogels. Colloids Surf B Biointerfaces 74:186–190.  https://doi.org/10.1016/j.colsurfb.2009.07.015 CrossRefGoogle Scholar
  13. Hickey AS, Peppas NA (1997) Solute diffusion in poly(vinyl alcohol)/poly(acrylic acid) composite membranes prepared by freezing/thawing techniques. Polymer (Guildf) 38:5931–5936.  https://doi.org/10.1016/S0032-3861(97)00163-8 CrossRefGoogle Scholar
  14. Kim JI, Chun C, Kim B, Hong JM, Cho JK, Lee SH, Song SC (2012) Thermosensitive/magnetic poly(organophosphazene) hydrogel as a long-term magnetic resonance contrast platform. Biomaterials 33:218–224.  https://doi.org/10.1016/j.biomaterials.2011.09.033 CrossRefGoogle Scholar
  15. Kumar M, Tamilarasan R (2013) Modeling studies: adsorption of aniline blue by using Prosopis Juliflora carbon/Ca/alginate polymer composite beads. Carbohydr Polym 92:2171–2180.  https://doi.org/10.1016/j.carbpol.2012.11.076 CrossRefGoogle Scholar
  16. Lin CL, Lee CF, Chiu WY (2005) Preparation and properties of poly(acrylic acid) oligomer stabilized superparamagnetic ferrofluid. J Colloid Interface Sci 291:411–420.  https://doi.org/10.1016/j.jcis.2005.05.023 CrossRefGoogle Scholar
  17. Liu Y, Zheng Y, Wang A (2010) Enhanced adsorption of methylene blue from aqueous solution by chitosan-g-poly (acrylic acid)/vermiculite hydrogel composites. J Environ Sci 22:486–493.  https://doi.org/10.1016/S1001-0742(10)60438-X CrossRefGoogle Scholar
  18. Majid S, Bukhari H, Khan S et al (2015) Synthesis and characterization of chemically cross-linked acrylic acid / gelatin hydrogels : effect of pH and composition on swelling and drug release. Int J Polym Sci 15Google Scholar
  19. Manavi-Tehrani I, Rabiee M, Parviz M, Tahriri MR, Fahimi Z (2010) Preparation, characterization and controlled release investigation of biocompatible pH-sensitive PVA/PAA hydrogels. Macromol Symp 296:457–465.  https://doi.org/10.1002/masy.201051062 CrossRefGoogle Scholar
  20. Mansur HS, Oréfice RL, Mansur AAP (2004) Characterization of poly(vinyl alcohol)/poly(ethylene glycol) hydrogels and PVA-derived hybrids by small-angle X-ray scattering and FTIR spectroscopy. Polymer (Guildf) 45:7193–7202.  https://doi.org/10.1016/j.polymer.2004.08.036 CrossRefGoogle Scholar
  21. Mansur HS, Sadahira CM, Souza AN, Mansur AAP (2008) FTIR spectroscopy characterization of poly (vinyl alcohol) hydrogel with different hydrolysis degree and chemically crosslinked with glutaraldehyde. Mater Sci Eng C 28:539–548.  https://doi.org/10.1016/j.msec.2007.10.088 CrossRefGoogle Scholar
  22. Mendoza Zelis P, Muraca D, Gonzalez JS et al (2013) Magnetic properties study of iron-oxide nanoparticles/PVA ferrogels with potential biomedical applications. J Nanopart Res 15:1613.  https://doi.org/10.1007/s11051-013-1613-6 CrossRefGoogle Scholar
  23. Moscoso-Londono O, Muraca D, de Oliveira L et al (2013) The effect of coated-Fe3O4 nanoparticles on magnetic properties of ferrogels produced by diffusion route. IEEE Trans Magn 49:4551–4554.  https://doi.org/10.1109/TMAG.2013.2259804 CrossRefGoogle Scholar
  24. Nigam P, Armour G, Banat IM, Singh D, Marchant R (2000) Physical removal of textile dyes from effluents and solid-state fermentation of dye-adsorbed agricultural residues. Bioresour Technol 72:219–226.  https://doi.org/10.1016/S0960-8524(99)00123-6 CrossRefGoogle Scholar
  25. Peppas NA, Tennenhouse D (2004) Semicrystalline poly (vinyl alcohol) films and their blends with poly (acrylic acid) and poly (ethylene glycol) for drug delivery applications. J Drug Del Sci Technol 14:291–297CrossRefGoogle Scholar
  26. Peppas NA, Wright SL (1998) Drug diffusion and binding in ionizable interpenetrating networks from poly(vinyl alcohol) and poly(acrylic acid). Eur J Pharm Biopharm 46:15–29.  https://doi.org/10.1016/S0939-6411(97)00113-6 CrossRefGoogle Scholar
  27. Quintero SMM, Ponce FRV, Cremona M et al (2010) Swelling and morphological properties of poly(vinyl alcohol) (PVA) and poly(acrylic acid) (PAA) hydrogels in solution with high salt concentration. Polymer (Guildf) 51:953–958.  https://doi.org/10.1016/j.polymer.2009.12.016 CrossRefGoogle Scholar
  28. Ray D, Mohanta GP, Gils PS et al (2009) Delivery of antihypertensive drug through synthesized hydrogel network, a comparative study. Lat Am J Pharm 28:747–755Google Scholar
  29. Reddy DHK, Lee SM (2013) Application of magnetic chitosan composites for the removal of toxic metal and dyes from aqueous solutions. Adv Colloid Interf Sci 201–202:68–93.  https://doi.org/10.1016/j.cis.2013.10.002 CrossRefGoogle Scholar
  30. Ricciardi R, Auriemma F, Gaillet C, de Rosa C, Lauprêtre F (2004) Investigation of the crystallinity of freeze/thaw poly(vinyl alcohol) hydrogels by different techniques. Macromolecules 37:9510–9516.  https://doi.org/10.1021/ma048418v CrossRefGoogle Scholar
  31. Sanchez LM, Alvarez VA, Gonzalez JS (2016) Ferrogels: smart materials for biomedical and remediation applications. In: Handbook of composites from renewable materials, volume 8: nanocomposites: advanced applications. pp 400–430Google Scholar
  32. Sanchez LM, Alvarez VA, Gonzalez JS (2017) 21. Ferrogels : smart materials for biomedical and remediation applications. In: Handbook of composites from renewable materialsGoogle Scholar
  33. Sanchez LM, Martin DA, Alvarez VA, Gonzalez JS (2018a) Polyacrylic acid-coated iron oxide magnetic nanoparticles: the polymer molecular weight influence. Colloids Surf A Physicochem Eng Asp 543.  https://doi.org/10.1016/j.colsurfa.2018.01.050 CrossRefGoogle Scholar
  34. Sanchez LM, Ollier RP, Gonzalez JS, Alvarez VA (2018b) Chapter 51. Nanocomposite materials for dyes removal. In: Handbook of nanomaterials for industrial applications. p 1143CrossRefGoogle Scholar
  35. Sekhavat Pour Z, Ghaemy M (2015) Removal of dyes and heavy metal ions from water by magnetic hydrogel beads based on poly(vinyl alcohol)/carboxymethyl starch-g-poly(vinyl imidazole). RSC Adv 5:64106–64118.  https://doi.org/10.1039/C5RA08025H CrossRefGoogle Scholar
  36. Sinha Ray S, Okamoto M (2003) Polymer/layered silicate nanocomposites: a review from preparation to processing. Prog Polym Sci 28:1539–1641.  https://doi.org/10.1016/j.progpolymsci.2003.08.002 CrossRefGoogle Scholar
  37. Smith TJ, Kennedy JE, Higginbotham CL (2009) Development of a novel porous cryo-foam for potential wound healing applications. J Mater Sci Mater Med 20:1193–1199.  https://doi.org/10.1007/s10856-008-3670-4 CrossRefGoogle Scholar
  38. Sorber J, Steiner G, Schulz V, Guenther M, Gerlach G, Salzer R, Arndt KF (2008) Hydrogel-based piezoresistive pH sensors: investigations using FT-IR attenuated total reflection spectroscopic imaging. Anal Chem 80:2957–2962.  https://doi.org/10.1021/ac702598n CrossRefGoogle Scholar
  39. Sun Y, Zhang Z, Moon KS, Wong CP (2004) Glass transition and relaxation behavior of epoxy nanocomposites. J Polym Sci Part B Polym Phys 42:3849–3858.  https://doi.org/10.1002/polb.20251 CrossRefGoogle Scholar
  40. Sun X-F, Baichen L, Jing Z, Wang H (2015) Preparation and adsorption property of xylan/poly(acrylic acid) magnetic nanocomposite hydrogel adsorbent. Carbohydr Polym 118:16–23.  https://doi.org/10.1016/j.carbpol.2014.11.013 CrossRefGoogle Scholar
  41. Timko BP, Dvir T, Kohane DS (2010) Remotely triggerable drug delivery systems. Adv Mater 22:4925–4943.  https://doi.org/10.1002/adma.201002072 CrossRefGoogle Scholar
  42. Vazquez Torres H, Cauich Rosriguez J, Cruz Ramos C (1993) Poly ( vinyl alcohol )/ poly ( acrylic acid ) blends : miscibility studies by DSC and characterization of their thermally induced hydrogels. J Appl Polym Sci 50:777–792CrossRefGoogle Scholar

Copyright information

© Springer Nature B.V. 2019

Authors and Affiliations

  1. 1.Materiales Compuestos Termoplásticos (CoMP), Instituto de Investigaciones en Ciencia y Tecnología de Materiales (INTEMA)CONICET - Universidad Nacional de Mar del Plata (UNMdP)Mar del PlataArgentina
  2. 2.Instituto de Física de La Plata (IFLP), CONICET-Departamento de FísicaUniversidad Nacional de La Plata (UNLP)La PlataArgentina

Personalised recommendations