Degradation of polymer-based composites in corrosive media: experimental attempts towards underlying mechanisms

  • M. AminiEmail author
  • A. Khavandi
Article
  • 6 Downloads

Abstract

In spite of previous studies on the corrosion behavior of glass-fiber-reinforced plastic composites, it is necessary to establish the relationship between the degradation occurring at the fiber/matrix interface of these composites and their mechanical performance. Here we report a series of experimental-based investigations to assess the issue. For this purpose, glass fiber/polyester samples were immersed in HCl (10% wt.) at three different temperatures, 25°C, 50°C, and 70°C. The effects on the bending, tensile and hardness properties, changes in the appearance, and microstructural analyses were evaluated over periods of 1 to 4 weeks of immersion. The results indicated that the bending strength, ultimate tensile strength, Young’s modulus and hardness of the samples decreased when exposed to longer exposure duration and/or higher temperature. The polyester degradation was demonstrated by increased surface roughness, cracks and changes in the solution color. In addition, visual inspection of tensile test fracture surfaces and SEM images of the broken sections revealed the drastic corrosion of the fibers and the interface. Finally, atomic absorption spectroscopy (AAS) was carried out, indicating the occurrence of ion exchange reactions. Our results revealed that the underlying mechanism affecting the corrosion happens in the interfacial zone of these composites.

Keywords

Polymer composites Microstructural characterization Corrosion mechanisms Interface Mechanical properties 

Notes

References

  1. Alsayed, S., Al-Salloum, Y., Almusallam, T., El-Gamal, S., Aqel, M.: Performance of glass fiber reinforced polymer bars under elevated temperatures. Composites, Part B, Eng. 43, 2265–2271 (2012) CrossRefGoogle Scholar
  2. Amaro, A.M., Reis, P.N.B., Moura, M.D.: Delamination effect on bending behaviour in carbon-epoxy composites. Strain 47, 203–208 (2011) CrossRefGoogle Scholar
  3. Amini, M., Khavandi, A.: Evaluation of the electrical properties and mechanical behavior of insulator’s composite core in harsh environments. Mater. Res. Express 5, 115306 (2018) CrossRefGoogle Scholar
  4. Arun, K.V., Basavarajappa, S., Sherigara, B.S.: Damage characterization of glass/textile fabric polymer hybrid composites in sea water environment. Mater. Des. 31, 930–939 (2010) CrossRefGoogle Scholar
  5. Bagherpour, S., Bagheri, R., Saatchi, A.: Effects of concentrated HCl on the mechanical properties of storage aged fiber glass polyester composite. Mater. Des. 30, 271–274 (2009) CrossRefGoogle Scholar
  6. Banna, M.H., Shirokoff, J., Molgaard, J.: Effects of two aqueous acidic solutions on polyester and bisphenol A epoxy vinyl ester resins. Mater. Sci. Eng. A 528, 2137–2142 (2011) CrossRefGoogle Scholar
  7. Callister, W.D.: Material Science and Engineering, 7th edn. Wiley, New Jersey (2007) Google Scholar
  8. Cho, E.H., Mounts, J.L.: Durability of glass-fiber-reinforced polymer composites in an alkaline environment. J. Vinyl Addit. Technol. 13, 221–228 (2007) CrossRefGoogle Scholar
  9. Ely, T., Kumosa, M.: The stress corrosion experiments on an E-glass/epoxy unidirectional composite. J. Compos. Mater. 34, 841–878 (2000) CrossRefGoogle Scholar
  10. Feng, P., Wang, J., Wang, Y., Loughery, D., Niu, D.: Effects of corrosive environments on properties of pultruded GFRP plates. Composites, Part B, Eng. 67, 427–433 (2014) CrossRefGoogle Scholar
  11. Fitriah, S.N., Abdul Majid, M.S., Ridzuan, M.J.M., Daud, R., Gibson, A.G., Assaleh, T.A.: Influence of hydrothermal ageing on the compressive behaviour of glass fibre/epoxy composite pipes. Compos. Struct. 159, 350–360 (2017) CrossRefGoogle Scholar
  12. Gellet, E.P., Turley, D.M.: Seawater immersion ageing of glass-fibre reinforced polymer laminates for marine applications. Composites, Part A, Appl. Sci. Manuf. 30, 1259–1265 (1999) CrossRefGoogle Scholar
  13. Groysman, A.: Corrosion Problems and Solutions in Oil Refining and Petrochemical Industry. Springer, Cham (2017) CrossRefGoogle Scholar
  14. Gu, H.: Dynamic mechanical analysis of the seawater treated glass/polyester composites. Mater. Des. 30, 2774–2777 (2009) CrossRefGoogle Scholar
  15. Gu, H., Honagxia, S.: Delamination behaviour of glass/polyester composites after water absorption. Mater. Des. 29, 262–264 (2007) CrossRefGoogle Scholar
  16. Hammami, A., Al-Ghuilani, N.: Durability and environmental degradation of glass–vinylester composites. Polym. Compos. 16, 609–616 (2004) CrossRefGoogle Scholar
  17. Harper, C.A.: Handbook of Plastics, Elastomers and Composites, 4th edn. McGraw-Hill, New York (2002) Google Scholar
  18. Hogg, P.J., Hull, D., Spencer, B.: Stress and strain corrosion of glass reinforced plastics. Composites 12, 166–172 (1981) CrossRefGoogle Scholar
  19. Imielińska, K., Guillaumat, L.: The effect of water immersion ageing on low-velocity impact behaviour of woven aramid–glass fibre/epoxy composites. Compos. Sci. Technol. 64, 2271–2278 (2004) CrossRefGoogle Scholar
  20. Huang, G., Sun, H.: Effect of water absorption on the mechanical properties of glass/polyester composites. Mater. Des. 28, 1647–1650 (2007) CrossRefGoogle Scholar
  21. Jones, F.R.: Durability of reinforced plastics in liquid environments. In: Pritchard, G. (ed.) Reinforced Plastics Durability. Woodhead, Abington Hall (1999) Google Scholar
  22. Jones, R.L.: Chemical corrosion of E-glass fibers in oxalic and other organic acids. J. Am. Ceram. Soc. 89, 20–23 (2006) CrossRefGoogle Scholar
  23. Kajorncheappungam, S., Gupta, R.K., GangaRao, H.V.S.: Effect of aging environment on degradation of glass reinforced epoxy. J. Compos. Constr. 6, 61–69 (2002) CrossRefGoogle Scholar
  24. Kootsookos, A., Mouritz, A.P.: Seawater durability of glass-and-carbon-polymer composites. Compos. Sci. Technol. 64, 1503–1511 (2004) CrossRefGoogle Scholar
  25. Kumar, M.S., Sharma, N., Ray, B.C.: Acid degradation of FRP composites. In: National Conference on Development of Composite, India (2007) Google Scholar
  26. Kumosa, L., Armentrout, D., Kumosa, M.: An evaluation of the critical conditions for the initiation of stress corrosion cracking in unidirectional E-glass/polymer composites. Compos. Sci. Technol. 61, 615–623 (2001) CrossRefGoogle Scholar
  27. Li, H., Yan, M., Qi, D., Zhang, S., Ding, N., Cai, X., Li, Q., Zhang, X., Deng, J.: Corrosion of E-glass fiber in simulated oilfield environments. J. Pet. Sci. Eng. 78, 371–375 (2011) CrossRefGoogle Scholar
  28. Lila, M.K., Saini, G.K., Kannan, M., Singh, I.: Effect of fiber type on thermal and mechanical behavior of epoxy based composites. Fiber Polym. 18, 806–810 (2017) CrossRefGoogle Scholar
  29. Mahmoud, M.K., Tantawi, S.H.: Effect of strong acids on mechanical properties of glass/polyester GRP pipe at normal and high temperatures. Polym.-Plast. Technol. Eng. 42, 677–688 (2003) CrossRefGoogle Scholar
  30. Marru, P., Latane, V., Puja, C., Vikas, K., Kumar, P., Neogi, S.: Lifetime estimation of glass reinforced epoxy pipes in acidic and alkaline environment using accelerated test methodology. Fiber Polym. 15, 1935–1940 (2014) CrossRefGoogle Scholar
  31. Miyano, Y., Nakada, M., Sekine, N.: Accelerated testing for long-term durability of FRP laminates for marine use. J. Compos. Mater. 39, 5–20 (2005) CrossRefGoogle Scholar
  32. Mouritz, A.P., Gallagher, J., Goodwin, A.A.: Flexural strength and interlaminar shear of stitched GRP laminates following repeated impacts. Compos. Sci. Technol. 57, 509–522 (1997) CrossRefGoogle Scholar
  33. Pour-Ghaz, M., Miller, B.L.H., Alla, O.K., Rizkalla, S.: Do mechanical and environmental loading have a synergistic effect on the degradation of pultruded glass fiber reinforced polymers. Composites, Part B, Eng. 106, 344–355 (2016) CrossRefGoogle Scholar
  34. Qiu, Q., Kumosa, M.: Corrosion of E-glass fibres in acidic environments. Compos. Sci. Technol. 57, 497–507 (1997) CrossRefGoogle Scholar
  35. Sapalidis, S.N., Hogg, P.J., Youd, S.J.: High temperature acidic stress corrosion of glass fibre composites: Part 1: Effect of fibre type. J. Mater. Sci. 32, 309–316 (1997) CrossRefGoogle Scholar
  36. Schutte, C.L.: Environmental durability of glass-fiber composites. Mater. Sci. Eng. 13, 265–323 (1994) CrossRefGoogle Scholar
  37. Selvan, M.G.A., Athijayamani, A.: Mechanical properties of fragrant screwpine fiber reinforced unsaturated polyester composite: effect of fiber length, fiber treatment and water absorption. Fiber Polym. 17, 104–116 (2016) CrossRefGoogle Scholar
  38. Solis-Ramos, E., Kumosa, M.: Synergistic effects in stress corrosion cracking of glass reinforced polymer composites. Polym. Degrad. Stab. 136, 146–157 (2017) CrossRefGoogle Scholar
  39. Stamenovic, M., Putic, S., Rakin, M., Medjo, B., Cikara, D.: Effect of alkaline and acidic solutions on the tensile properties of glass-polyester pipes. Mater. Des. 32, 2456–2461 (2011) CrossRefGoogle Scholar
  40. Takafumi, T., Pearson, R.A.: The moisture effect on the fatigue crack of glass particle and fibre reinforced epoxies with strong and weak bending conditions: Part 2: A microscopic study on toughening mechanism. Compos. Sci. Technol. 64, 1991–2007 (2004) CrossRefGoogle Scholar
  41. Visakh, P.M., Nazarenko, O.B.: Thermal Degradation of Polymer Blends, Composites and Nanocomposites, pp. 1–16. Springer, Cham (2015) CrossRefGoogle Scholar
  42. Wei, B., Cao, H., Song, S.: Degradation of basalt fibre and glass fibre/epoxy resin composites in seawater. Corros. Sci. 53, 426–431 (2011) CrossRefGoogle Scholar
  43. Won, J.P., Lee, S.J., Kim, Y.J., Jang, C.I., Lee, S.W.: The effect of exposure to alkaline solution and water on the strength–porosity relationship of GFRP rebar. Composites, Part B, Eng. 39, 764–772 (2008) CrossRefGoogle Scholar

Copyright information

© Springer Nature B.V. 2019

Authors and Affiliations

  1. 1.Faculty of Materials Science and EngineeringK.N. Toosi University of TechnologyTehranIran
  2. 2.School of Metallurgy and Materials EngineeringIran University of Science and Technology (IUST)TehranIran

Personalised recommendations