Steel Surface Modification with Carbon Nanomaterial Using Concentrated Energy Flows
- 16 Downloads
Surface strengthening of structural steels with carbon nanomaterials using laser and electron-beam heating is studied. It is shown that during laser treatment the maximum microhardness of a modified layer is achieved in a strengthened zone up to 70 μm thick with q = 9 × 104 W/cm2, and with electron beam treatment in a strengthened zone up to 300 μm thick with q = 4.6 × 104 W/cm2. It is established that in both cases with optimum treatment regimes strengthening is due to forming martensite, a cellular structure, and grain disintegration.
Key wordsmodification laser treatment electron-beam treatment carbon nanomaterials steel commercial iron microhardness microstructure
Work was carried out within the scope of project No. 16-19-10027 supported by the Russian Scientific Fund.
- 1.N. N. Rykalin, A. A. Uglov, I. V. Zuev, and A. N. Kokora, Laser and Electron-Beam Treatment of Materials: Handbook [in Russian], Mashinostroenie, Moscow (1985).Google Scholar
- 2.O. V. Chudina, “Modification of a steel surface using laser heating,” Svaroch. Prpoizvod., No. 3, 24 – 28 (2016).Google Scholar
- 3.V. K. Dragunov, A. L. Goncharov, E. V. Terent’ev, and A. E. Marchenkov, Creation of Welded Combined Structures in Power Engineering, Part 1. Physical Processes During Welding Different Metals: Textbook [in Russian], Veche, Moscow (2015).Google Scholar
- 5.G. S. Bocharov, A. V. Eletskii, A. V. Zakharenkov, et al., “Optimization of strengthening of a steel surface with carbon nanostructures and subsequent treatment with high-energy sources,” in: Proc. XIV Internat. Sci.-Tech. Conf. “Rapidly hardened materials and coatings” [in Russian], MAI, Moscow (2016), p. 31.Google Scholar
- 7.V. M. Matyunin, A. Yu. Marchenkov, and A. N. Demidov, “Study of the influence of a dimensional effect on results of determining hardness at different scale levels,” Tekhnol. Metallov, No. 6, 53 – 54 (2013).Google Scholar