Effect of Hot Rolling Production Parameters on 12% Chromium Steel Structure and Properties

  • A. S. KudryavtsevEmail author
  • K. A. Okhapkin
  • Yu. M. Markova

The effect of heating temperature and deformation during hot rolling on the microstructure and mechanical properties of steel grade 07Kh12NMFB (0.07C–12Cr–Ni–Mo–V–Nb) are studied. It is established that a change in the plastic deformation regime, without having a significant effect on strength properties, leads to significant changes in steel impact strength. No effect of hot rolling production parameters on steel microstructure after the final heat treatment is detected. Based on research results a heating temperature up to 1150 °C for rolling steel grade 07Kh12NMFB and deformation of not less than 25% are recommended.


12% chromium martensitic-ferritic steel impact strength hot rolling microstructure ferrite 


  1. 1.
    M. Ya. Dzugutov, Plastic Deformation of Highly Alloyed Steels and Alloys [in Russian], Metallurgiya, Moscow (1977).Google Scholar
  2. 2.
    K. A. Lanskaya, High-Chromium Heat-Resistant Steels [in Russian], Metallurgiya, Moscow (1976).Google Scholar
  3. 3.
    D. A. Artem’yeva, G. P. Karzov, A. S. Kudryavtsev, et al., “Choice of structural material a steal generator according to criteria providing corrosion resistance under different high=power sodium reactor operating conditions,” Vopr. Atom. Nauk Tekhn., Ser. Obes. Besopas. AÉS, No. 34, 53–59 (2014).Google Scholar
  4. 4.
    A. D. Zobnin, Technological Bases of Planning Rolling Complexes. Calculation of Sheet Rolling Parameters: Textbook [in Russian], MISiS, Moscow (2009).Google Scholar
  5. 5.
    A. S. Kudryavtsev, M. S. Mikhailov, and D. A. Artem’eva, “Martensitic-ferritic class 12% chromium steel alloyed with nitrogen,” Fiz. Metal. Metallovedenie, 118, No. 8, 829–835 (2017).Google Scholar
  6. 6.
    A. S. Kudryavtseva, D. A. Artem’eva, and P. Ya. Reiner, “Effect of phase composition of steel deformation capacity of grade 07Kh12NMFB at high temperature,” Vopr. Materialoved., No. 3(79), 34–40 (2014).Google Scholar
  7. 7.
    E. N. Mosaleva, Trudy TsKTI No. 53: Heat-Resistant Material for Power Engineering (A. V. Stanyukovich, editor) [in Russian], Mashinostroenie, Leningrad (1965).Google Scholar
  8. 8.
    R. L. Klueh and D. R. Harries, High-Chromium Ferritic and Martensitic Steels for Nuclear Applications. ASTM Stock Number: MONO3. ASTM (2001).Google Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  • A. S. Kudryavtsev
    • 1
    Email author
  • K. A. Okhapkin
    • 1
  • Yu. M. Markova
    • 1
  1. 1.NITs Kurchatov Institute, TsNII KM PrometeiSt. PetersburgRussia

Personalised recommendations