Study of the Possibility of Obtaining Non-Decomposing Slag During Low-Carbon Ferrochrome Production

  • O. V. ZayakinEmail author
  • R. N. Statnykh
  • V. I. Zhuchkov
Article
  • 1 Downloads

Methods are analyzed for stabilizing self-disintegrating slags in melting low-carbon ferrochrome, and the main reasons for breakdown are considered. Four methods are shown for stabilizing oxide melts of which a promising method for preventing breakdown under contemporary production conditions for chromium ferroalloys by mixing melts is a reduction in the content of dicalcium silicate with a reduction in the CaO/SiO2 ratio in oxide melt to a value of less than 1.4. However a reduction in CaO/SiO2 slag basicity to < 1.7 leads to a reduction in the degree of chromium reduction. With a the aim of maintaining a high degree of chromium extraction into molten metal it is proposed to conduct melting with excess siliceous reducing agent, which undoubtedly leads to an increase in silicon in the ferrochrome obtained. A study of the molten slag characteristics showed that with an increase in silicon content in metal up to 5% there is a reduction in the residua content of Cr2O3 in slag to 6%. The fundamental possibility of obtaining on an industrial scale non-disintegrating slag with a residual content up to 6.0% Cr2O3 with basicity > 1.33 is demonstrated by experiment (during melting low-carbon ferrochrome containing not less than 5% Si). However, according to the specifications of GOST 4757–91 and the international standard ISO 5448-81 the silicon content in low-carbon ferrochrome should not exceed 1.5%, in view of which the silicothermal process for process for preparing ferrochrome by a mixing method should be separated into two stages. The first stage is preparation of siliceous semiproduct (low-carbon ferrochrome containing Si ≈ 5%) and non-disintegrating slag with reduced basicity (CaO/SiO2 = 1.3–1.4). The second stage is refining the semiproduct with respect to silicon with preparation of highly basic slag (CaO/SiO2 = 1.8–1.9) and ferrochrome with the required silicon content (less than 1.5%). The possibility of obtaining a non-disintegrating slag during melting low-carbon ferrochrome with subsequent processing into building rubble will make it possible to improve the ecological situation in the vicinity of ferroalloy enterprises, to reduce slag dump and adjacent territory contamination and dust content, and also to reduce the amount of slag, loss of chromium, and to increase productivity of the process with a reduction in specific consumption of lime and electrical energy.

Keywords

metallurgy ferroalloy slag oxide melt ferrochrome silicothermal process 

References

  1. 1.
    A. A. Akberdin, V. I. Zhuchkov, A. S. Kim, et al., “Stabilization of decomposing metallurgical slag,” in: Proc. Cong. with International Participation and Conf. Of Young Scientists, “Fundamental Research and Applied Development of Treatment Processes and Technogenic Formation” [in Russian], UrO RAN, Ekaterinburg (2017), pp. 160–163.Google Scholar
  2. 2.
    Yu. A. Guloyan, V. F. Smirnov, K. S. Katkova, et al., “Improvement of the efficiency of producing colored bottles using ferrochrome slags,” in: Proc. “Improvement of the Efficiency of Production Processes in Manufacturing Glass Objects” [in Russian], Moscow (1973), pp. 184–187.Google Scholar
  3. 3.
    M. S. Dosekenov, V. I. Zhuchkov, D. D. Izbembetov, and O. V. Zayakin, “Formation and use of technogenic waste in ferroalloy production,” in: Proc. Internat. Conf. Devoted to the 80th Anniversary Ural Science “Fundamental Bases of Processing Technology and Utilization of Technogenic Waste, TEKHNOGEN 2012” [in Russian], OOO UIPTs, Ekaterinburg (2012), pp. 46–49.Google Scholar
  4. 4.
    I. D. Kashcheev, K. G. Zemlyanoi, M. S. Dosekenov, et al., “Main characteristics of slags and dust formed during ferrochrome production,” in: Proc. Internat. Conf. Devoted to the 80th anniversary Ural Science “Fundamental Bases of Processing Technology and Utilization of Technogenic Waste, TEKHNOGEN 2012” [in Russian], OOO UIPTs, Ekaterinburg (2012), pp. 101–104.Google Scholar
  5. 5.
    N. A. Vatolin, B. D. Khalezov, A. G. Krasheninin, et al., “Complex treatment technology for vanadium metallurgical slags,” in: Proc. Internat. Conf. Devoted to the 80th Anniversary Ural Science “Fundamental Bases of Processing Technology and Utilization of Technogenic Waste, TEKHNOGEN 2012” [in Russian], OOO UIPTs, Ekaterinburg (2012), pp. 438–441.Google Scholar
  6. 6.
    V. I. Zhuchkov and O. V. Zayakin, “Nature conservation methods in ferroalloy production,” Rasplavy, No. 4, 66–69 (2010).Google Scholar
  7. 7.
    A. A. Akberdin and A. S. Kim, Method for Stabilizing Slags of Medium and Low-Carbon Grades of Ferrochrome from Melts, Kazakhstan Republic Pre-Patent, No. 1532, Priority 11.11.2002.Google Scholar
  8. 8.
    V. I. Zhuchkov, A. A. Akberdin, N. A. Vatolin, et al., “Use of boron-containing materials in metallurgy,” Élekrometallurgiya, No. 3, 25–28 (2011).Google Scholar
  9. 9.
    G. V. Kukolev and M. T. Mel’nik, “Synthesis and properties of dicalcium silicate,” in: Proc. 5th Meeting for Experimental and Technical Mineralogy and Petrography [in Russian], Izd. Akad. Nauk SSSR, Moscow (1958), pp. 407–413.Google Scholar
  10. 10.
    N. P. Lyakishev and M. I. Gasik, Chromium Metallurgy [in Russian], ÉLIZ, Moscow (1999).Google Scholar
  11. 11.
    V. N. Kornoukhov, Yu. I. Voronov, V. P. Zaiko, and V. I. Zhuchkov, Low-Carbon Ferrochrome Technology [in Russian], URO RAN Eketerinburg (2001).Google Scholar
  12. 12.
    V. I. Fadeev, Ya. I. Ostrovskii, A. A. Tsernikel’, et al., “Resource saving technology for producing low-carbon ferrochrome with preparation of stabilized slags,” in: Proc. “Contemporary Resource Saving Technology” [in Ukrainian], ONU im. I. I. Menchikova, Odessa (2012), pp. 131–134.Google Scholar
  13. 13.
    O. S. Bobkova, Silicothermal Reduction of Metals [in Russian], Metallurgiya, Moscow (1981).Google Scholar
  14. 14.
    V. I. Fadeev, Ya. I. Ostrovskii, O. S. Bobkova, et al., RF Patent 2424342, MPK C22C 33/04. Method for Preparing Low-Carbon Ferrochrome, Publ. 07.22.11, Bull. No. 20.Google Scholar
  15. 15.
    GOST 4757-91, Ferrochrome. Technical Specifications and Supply Conditions [in Russian], IPK Izd. Standartov, Moscow (1997).Google Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  • O. V. Zayakin
    • 1
    Email author
  • R. N. Statnykh
    • 1
  • V. I. Zhuchkov
    • 1
  1. 1.Institute of metallurgy, Ural SectionRussian Academy of SciencesEkaterinburgRussia

Personalised recommendations