Effect of high temperature on reduction-controlling reaction rate of agricultural waste chars and coke with steelmaking slag

  • Nur Farhana M. YunosEmail author
  • Nur Hazira Najmi
  • Sri Raj Rajeswari Munusamy
  • Muhammad Asri Idris
Article
  • 12 Downloads

Abstract

Agricultural wastes generated from palm and coconut shells could be renewable carbon sources in steelmaking by providing the solution to environmental problems and reducing the gas emission. By applying these wastes as carbon reductant at steelmaking’s temperature, the determination of the reduction-controlling reaction rate is necessary. Thus, the present study aims to provide an understanding of the effect of high temperature (1823 K) on the reduction-controlling reaction rate of palm and coconut chars that reacted with steelmaking slag. Palm and coconut shells were pyrolyzed at 723 K under nitrogen inert for char conversion. The char has a porous structure and contains high volatile matter that is more chemically active in the system reaction compared to coke. All carbonaceous materials including coke as a control carbon mixed with steelmaking slag using an infrared (IR) gas analyzer to measure the amounts of carbon dioxide (CO2) and carbon monoxide (CO) gases produced after reduction. The reaction rate of palm and coconut chars after reaction with steelmaking slag was lower (0.93721 × 10−5 and 0.30563 × 10−5 mol cm−2 s−1) than that of coke (2.16283 × 10−5 mol cm−2 s−1) due to lower fixed carbon content that retards the reaction rate. The reaction using palm and coconut chars approached faster the equilibrium of the carbon solution-loss reaction (C + CO2 → 2CO) and Boudouard equilibrium where the reaction reached the equilibrium value of 1.0 than coke due to higher CO generation. The results found that agricultural waste char is used as a carbon reductant in iron oxide reduction of steelmaking slag in a cleaner and sustainable production of iron due to their better properties such as volatile matter and porous structure.

Keywords

Reduction Reaction rate Agricultural wastes char Coke Steelmaking slag Boudouard equilibrium 

Notes

Acknowledgements

Part of this work was done at the School of Materials Science and Engineering, University of New South Wales (UNSW), Sydney, Australia. We are grateful to Prof Veena Sahajwalla at (SMaRT@UNSW) for opinions and guidance. We acknowledge the financial support from a Fundamental Research Grant Scheme (FRGS, 2013-Grants No: 9003-00366) from the Ministry of Higher Education Malaysia (MOHE), and Research Management and Innovation Center (RMIC) and School of Materials Engineering, Universiti Malaysia Perlis, (UniMAP) for this research.

References

  1. 1.
  2. 2.
    Bains P, Psarras P, Wilcox J. CO2 capture from the industry sector. Prog Energy Comb Sci. 2017;63:146–72.CrossRefGoogle Scholar
  3. 3.
    Zandi M, Martinez-Pacheco M, Fray TAT. Biomass for iron ore sintering. Minerals Eng. 2010;23(14):1139–45.CrossRefGoogle Scholar
  4. 4.
    Norgate T, et al. Biomass as a source of renewable carbon for iron and steelmaking. ISIJ Int. 2012;52(8):1472–81.CrossRefGoogle Scholar
  5. 5.
    Oliveira TL, et al. Study of biomass applied to a cogeneration system: a steelmaking industry case. App Thermal Eng. 2015;80:269–78.CrossRefGoogle Scholar
  6. 6.
    Adrados A, et al. Biomass pyrolysis solids as reducing agents: comparison with commercial reducing agents. Materials. 2015;9(1):3.CrossRefGoogle Scholar
  7. 7.
    Emmerich FG, Luengo A. Babassu charcoal: a sulfurless renewable thermo-reducing feedstock for steelmaking. Biomass Bioenergy. 1996;10(1):41–4.CrossRefGoogle Scholar
  8. 8.
    Babich A, Senk D, Fernandez M. Charcoal behaviour by its injection into the modern blast furnace. ISIJ Int. 2010;50(1):81–8.CrossRefGoogle Scholar
  9. 9.
    Lahijani P, et al. Conversion of the greenhouse gas CO2 to the fuel gas CO via the Boudouard reaction: a review. Renew Sustain Energy Rev. 2015;41:615–32.CrossRefGoogle Scholar
  10. 10.
    González JF, et al. Pyrolysis of various biomass residues and char utilization for the production of activated carbons. J Anal Appl Pyrol. 2009;85(1–2):134–41.CrossRefGoogle Scholar
  11. 11.
    Moghtaderi B, Meesri C, Wall TF. Pyrolytic characteristics of blended coal and woody biomass. Fuel. 2004;83(6):745–50.CrossRefGoogle Scholar
  12. 12.
    Vamvuka D, et al. Pyrolysis characteristics and kinetics of biomass residuals mixtures with lignite. Fuel. 2003;82(15–17):1949–60.CrossRefGoogle Scholar
  13. 13.
    Li P, et al. Kinetics of CO2/coal gasification in molten blast furnace slag. Ind Eng Chem Res. 2012;51(49):15872–83.CrossRefGoogle Scholar
  14. 14.
    Ahmed HM, Viswanathan N, Bjorkman B. Composite pellets—a potential raw material for iron-making. Steel Res Int. 2014;85(3):293–306.CrossRefGoogle Scholar
  15. 15.
    Kumar U, et al. Cleaner production of iron by using waste macadamia biomass as a carbon resource. J Cleaner Prod. 2017;158:218–24.CrossRefGoogle Scholar
  16. 16.
    Zaharia M. Carbon/slag interactions between coke/rubber blends and EAF slag at 1823 K. ISIJ Int. 2009;49(10):1513–21.CrossRefGoogle Scholar
  17. 17.
    Paramguru R. Some kinetic aspects of reduction of FeO in molten slags by solute carbon. ISIJ Int. 1997;37(8):756–61.CrossRefGoogle Scholar
  18. 18.
    Jouhari AK, et al. Foaming during reduction of iron oxide in molten slag. Iron Steelmaking. 2000;27:27–31.CrossRefGoogle Scholar
  19. 19.
    Richardson FD. Physical chemistry of melts in metallurgy. Academic Press (Elsevier); 1974.Google Scholar
  20. 20.
    Zaharia M. Reactions of waste rubber tyres and polypropylene plastics with gases and electric arc furnace steelmaking slags. Ph.D. thesis. Sydney, Australia: 2010. p. 1–282.Google Scholar
  21. 21.
    Yunos NFM, et al. Recycling agricultural waste from palm shells during electric arc furnace steelmaking. Energy Fuels. 2012;26(1):278–86.CrossRefGoogle Scholar
  22. 22.
    Sun H. Interfacial phenomena and reaction kinetics between the carbon and slag in the ironmaking process. Energy Fuels. 2007;21:413–8.CrossRefGoogle Scholar
  23. 23.
    Dhunna R, et al. Recycling waste bakelite as an alternative carbon resource for ironmaking applications. ISIJ Int. 2014;54(3):613–9.CrossRefGoogle Scholar
  24. 24.
    Hong L, Sahajwalla W. Carbothermic reduction of mullite at elevated temperature. Metall Mater Trans B. 2013;44(6):1541–5.CrossRefGoogle Scholar
  25. 25.
    Akhtar K, et al. An experimental study of direct reduction of hematite by lignite char. J Therm Anal Calorim. 2016;123(2):1111–8.CrossRefGoogle Scholar
  26. 26.
    Dankwah JR, Koshy P, Sahajwalla V. Reduction of FeO in EAF steelmaking slag by blends of metallurgical coke and end-of-life polyethylene terephthalate. Ironmaking Steelmaking. 2014;41(6):401–9.CrossRefGoogle Scholar
  27. 27.
    Sahajwalla V, et al. The power of steelmaking-harnessing high-temperature reactions to transform waste into raw material resources. Iron Steel Technol. 2013;10(8):68–83.Google Scholar
  28. 28.
    Dankwah JR, et al. Reduction of FeO in EAF steelmaking slag by metallurgical coke and waste plastics blends. ISIJ Int. 2011;51(3):498–507.CrossRefGoogle Scholar
  29. 29.
    Chase Jr MW. NIST-JANAF thermochemical tables, 4th edn. J Phys Chem Ref Data. 1998;9:1758.Google Scholar
  30. 30.
    Walker PL Jr, Taylor RL, Ranish JM. An update on the carbon-oxygen reaction. Carbon. 1991;29(3):411–21.CrossRefGoogle Scholar
  31. 31.
    Park H, Sahajwalla V. Reduction behavior of carbon composite pellets including alumina and silica at 1273 and 1373 K. ISIJ Int. 2014;54(6):1256–65.CrossRefGoogle Scholar
  32. 32.
    Yunos NFM. High temperature phenomena occurring during reactions of agricultural wastes in electric arc furnace steelmaking: interactions with gas and slag phases. Ph.D. thesis; Sydney, Australia: 2012. p. 1–347.Google Scholar
  33. 33.
    Wang H, Sohn HY. Reduction of magnetite concentrate particles by H2 + CO at 1673 K. ISIJ Int. 2015;55(3):706–8.CrossRefGoogle Scholar
  34. 34.
    Wang Y, et al. The reduction mechanism and kinetics of Fe2O3 by hydrogen for chemical-looping hydrogen generation. J Therm Anal Calorim. 2017;129(3):1831–8.CrossRefGoogle Scholar
  35. 35.
    Mróz J. Evaluation of the reduction of iron oxide from liquid slags using a graphite rotating disk. Metall Mater Trans B. 2001;32(5):821–30.CrossRefGoogle Scholar
  36. 36.
    Ajersch F. Chemical and physical characteristics affecting the reduction kinetics of iron oxide pellets with solid carbon. Can Metall Q. 1987;26(2):137–44.CrossRefGoogle Scholar
  37. 37.
    Li K, et al. The evolution of structural order, microstructure and mineral matter of metallurgical coke in a blast furnace: a review. Fuel. 2014;133:194–215.CrossRefGoogle Scholar
  38. 38.
    Fruehan R. The rate of reduction of iron oxides by carbon. Metall Mater Trans B. 1977;8(1):279–86.CrossRefGoogle Scholar
  39. 39.
    Hong L, Sahajwalla V. Reaction between steel-making slag and carbonaceous materials while mixing with high density polyethylene. High Temp Mater Proc. 2016:65.Google Scholar
  40. 40.
    Fidalgo B, Berrueco V, Millan M. Chars from agricultural wastes as greener fuels for electric arc furnaces. J Anal Appl Pyrol. 2015;113:274–80.CrossRefGoogle Scholar
  41. 41.
    Dankwah JR. Recycling blends of waste plastics and biomass as reducing agent for the production of metallic iron from iron oxide. Int J Eng Sci Technol. 2013;5(12):1967–76.Google Scholar
  42. 42.
    Yuan P, et al. Study on the formation of direct reduced iron by using biomass as reductants of carbon containing pellets in RHF process. Energy. 2017;141:472–82.CrossRefGoogle Scholar
  43. 43.
    Vamvuka D, et al. Kinetic modelling of coal/agricultural by-product blends. Energy Fuels. 2003;17–3:549–58.CrossRefGoogle Scholar
  44. 44.
    Yunos NFM, et al. Structural transformation of agricultural waste/coke blends and their implications during high temperature processes. ISIJ Int. 2011;51–7:1185–93.CrossRefGoogle Scholar
  45. 45.
    Dankwah JR. Recycling used pure water sachets and their blends with waste coconut shells as carbon resources in iron making. Afr J Appl Res. 2015;1-1.Google Scholar

Copyright information

© Akadémiai Kiadó, Budapest, Hungary 2019

Authors and Affiliations

  1. 1.School of Materials EngineeringUniversiti Malaysia PerlisArau, PerlisMalaysia
  2. 2.CoE of Frontier Materials Research, Universiti Malaysia PerlisKangar, PerlisMalaysia

Personalised recommendations