Crystallization kinetics and morphology of poly(lactic acid) with polysaccharide as nucleating agent
- 37 Downloads
An ever-increasing concern about environmental pollution has spearheaded research into alternative biodegradable polymers. Currently, poly(lactic acid) (PLA) is one of the most notable biodegradable polymers due to its superior properties and low production cost. Nucleating agents have been used to overcome slow PLA crystallization. The present work aims at investigating cashew gum (CG) as nucleating agent in PLA produced by casting process. The effect of the CG (1–10 mass%) on the PLA crystallization process was evaluated by thermal analysis and hot-stage optical microscopy. The relative degree of crystallinity, crystallization kinetic parameters under isothermal conditions, and crystallite morphology of pure PLA and PLACG samples were also investigated. The PLA crystallization rate increased with the CG content at a temperature ranging from 130 °C to 140 °C. An increase in the degree of crystallinity and a reduction in the crystallite size of the PLA were observed in the samples which contained 5 and 10 mass% of CG. Cashew gum proved to be an effective nucleating agent for PLA. Results show that cashew gum can be used as a natural nucleating agent for PLA when faster crystallization rate, better crystallite size control or higher degree of crystallinity are required.
KeywordsPoly(lactic acid) Cashew gum Nucleating agent Crystallization rate DSC
The authors gratefully acknowledge the financial support from the Brazilian National Council for Scientific and Technological Development (CNPq) and the Brazilian Agricultural Research Corporation (EMBRAPA) for supplying the cashew gum.
- 3.Jiang X, Luo Y, Tian X, Huang D, Reddy N, Yang Y. Chemical structure of poly(lactic acid). In: Auras R, Lim L-T, Selke SEM, Tsuji H, editors. Poly (lactic acid): synthesis, structures, properties, processing, and applications. New Jersey: Wiley; 2010. p. 69–80.Google Scholar
- 6.Auras R, Singh SP, Singh J. Performance evaluation of PLA against existing PET and PS containers. J Test Eval. 2006;34:1–7.Google Scholar
- 17.Joseph S, Deenadayalan E, Mahanwar PA. Studies on melt processable biocomposites of polylactic acid. J Polym Environ. 2015; https://doi.org/10.1007/s10924-014-0668-5.
- 18.Vidovic´ E, Faraguna F, Jukic´ A. Influence of inorganic fillers on PLA crystallinity and thermal properties. J Therm Anal Calorim. 2017; https://doi.org/10.1007/s10973-016-5750-x.
- 20.Zhang K, Nagarajan V, Misra M, Mohanty AK. Supertoughened renewable PLA Reactive multiphase blends system: phase morphology and performance. ACS Appl Mater Interfaces 2014; https://pubs.acs.org/doi/10.1021/am502337u.
- 21.Ramesan MT, Surya K. Studies on electrical, thermal and corrosion behaviour of cashew tree gum grafted poly(acrylamide). Polym Renew Resour. 2016;7:81–100.Google Scholar
- 29.Cowie JMG. Polymers: chemistry and physics of modern materials. 2nd ed. Glasgow: Blackie Academic & Professional; 1991.Google Scholar