Lifetime estimation applying a kinetic model based on the generalized logistic function to biopolymers
- 179 Downloads
The aim of this work was to estimate the lifetime due thermal aging of polymers and even other materials using a new approach based on the application of a kinetic model based on the generalized logistic function. For this purpose, thermogravimetric analysis, including dynamic and isothermal tests, was performed for different formulations based on polylactic acid used in dental applications (scaffolds). In this work, lifetime is defined as the time passed for losing the 5 wt% of the mass corresponding to the first and main degradation process. The 5 mass% mass loss could be a critic parameter in manufacturing processes, in terms of economical profit and quality of the final product. The proposed model provides lifetime estimates of polymeric materials depending on the storage temperature. The present procedure permits to obtain lifetime estimates of materials characterized by more than one main degradation process, since they can be dis-overlapped using generalized logistic functions.
KeywordsLifetime Scaffolds Thermogravimetric analysis Logistic function Kinetics Biopolymers
This research has been partially supported by the Spanish Ministry of Science and Innovation. Grant MTM2011-22392 and MTM2013-41383P (ERDF included).
- 2.ASTM E1641-07 Standard test method for decomposition kinetics by thermogravimetry, Annual Book of ASTM Standards, vol. 14.02, ASTM International, West Conshohocken, PA, 2007.Google Scholar
- 3.ASTM E698-05 Standard Test Method for Arrhenius Kinetic Constants for Thermally Unstable Materials, Annual Book of ASTM Standards, vol. 14.02, ASTM International, West Conshohocken, PA, 2005, p. 226.Google Scholar
- 6.Tarrío-Saavedra J, Naya S, López-Beceiro J, Zaragoza S, Álvarez A, Quintela-Pita S, García-Sabán J. Degradation modelling of bio-polymers used as dental scaffolds. In: Natal Jorge RM, Reis Campos JC, Vaz MAP, Santos SM, Tavares JMRS, editors. Biodental engineering III, 51. London: CRC Press, Taylor & Francis Group; 2014. p. 281–6.Google Scholar
- 13.Hoque ME, Yong LC, Ian P. Mathematical modeling on degradation of 3d tissue engineering scaffold materials. Regen Res. 2012;1(1):58–61.Google Scholar
- 16.Thermal analysis application brief. Estimation of polymer lifetime by TGA decomposition kinetics. TA Instrument technical note no 125. http://www.tainstruments.com/main.aspx?id=46&n=2&siteid=11. Accessed 20 Oct 2014.
- 17.Kingsland SE. Modeling nature: episodes in the history of population ecology. 2nd ed. Chicago: University of Chicago Press; 1995.Google Scholar
- 29.GNOME Office/Gnumeric—Welcome to Gnumeric! https://projects.gnome.org/gnumeric/. Last Accessed 20 Oct 2014.