Fabrication of TMPTMA foams with SiO2 sub-microspheres gradient doped via slope-rotation method

  • Xiao Pang
  • Xuan Luo
  • Chun Yang
  • Ting Shao
  • Lin ZhangEmail author
Original Paper: Sol-gel, hybrids and solution chemistries
  • 6 Downloads

Abstract

In this paper, we report a novel approach to fabricate gradient doped porous material via the slope-rotation method. By using dibutyl phthalate as the solvent, benzoin methyl ether as the photoinitiator, and silica sub-microsphere as filler, gradient doped trimethylolpropane trimethacrylate (TMPTMA) foams were fabricated after rotating and mixing, ultraviolet curing, and CO2 supercritical drying. The microstructure and gradient distribution of silica fillers were characterized by nitrogen adsorption, scanning electron microscopy, UV–visible absorption spectrum, and thermogravimetric analysis. The mechanical property was obtained by dynamic mechanical analysis. The results indicated that the approach was an effective method to fabricate gradient doped TMPTMA foams and had the potential to prepare any kind of gradient doped porous material derived from a sol–gel process. The mechanical property was further reinforced by gradient doping of silica sub-microspheres.

Highlights

  • SiO2 sub-microspheres gradient doped TMPTMA foams had been fabricated for the first time via slope rotation method.

  • The mechanical properties of TMPTMA foams could be further improved with the SiO2 sub-microspheres gradient doped.

Keywords

Gradient doped Sol–gel process Slope-rotation Mechanical property 

Notes

Acknowledgements

This work was financially supported by the Science and Technology Development Foundation of China Academy of Engineering Physics (2015B0302071).

Compliance with ethical standards

Conflict of interest

The authors declare that they have no conflict of interest.

References

  1. 1.
    Lawrence WH (1998) Aerogel applications. J Non-Cryst Solids 225:335–342CrossRefGoogle Scholar
  2. 2.
    Wu D, Xu F, Sun B, Fu R, He H, Matyjaszewski K (2012) Design and preparation of porous polymers. Chem Rev 112:3959–4015CrossRefGoogle Scholar
  3. 3.
    Cui L, Kiernan S, Gilchrist MD (2009) Designing the energy absorption capacity of functionally graded foam materials. Mater Sci Eng A 507:215–225CrossRefGoogle Scholar
  4. 4.
    Sandford SA, Aleon J et al. (2006) Organics captured from comet 81P Wild 2 by the Stardust spacecraft. Science 314:1720–1724CrossRefGoogle Scholar
  5. 5.
    Dhakate SR, Subhedar KM, Singh BP (2015) Polymer nanocomposite foam filled with carbon nanomaterials as an efficient electromagnetic interference shielding material. RSC Adv 5:43036–43057CrossRefGoogle Scholar
  6. 6.
    Chen L, Liu C, Liu K, Meng C, Hu C, Wang J, Fan S (2011) High-performance, low-voltage, and easy-operable bending actuator based on aligned carbon nanotube/polymer composites. ACS Nano 5:1588–1593CrossRefGoogle Scholar
  7. 7.
    Shim SE, Isayev AI (2004) Rheology and structure of precipitated silica and poly(dimethyl siloxane) system. Rheol Acta 43:127–136CrossRefGoogle Scholar
  8. 8.
    Brothers AH, Dunand DC (2008) Mechanical properties of a density-graded replicated aluminum foam. Mater Sci Eng A 489:439–443CrossRefGoogle Scholar
  9. 9.
    Hangai Y, Takahashi K, Utsunomiya T, Kitahora S, Kuwazuru O, Yoshikawa N (2012) Fabrication of functionally graded aluminum foam using aluminum alloy die castings by friction stir processing Mater Sci Eng A 534:716–719CrossRefGoogle Scholar
  10. 10.
    He SY, Zhang Y, Dai G, Jiang JQ (2014) Preparation of density-graded aluminum foam. Mater Sci Eng A 618:496–499CrossRefGoogle Scholar
  11. 11.
    Gupta N et al. (2007) A functionally graded syntactic foam material for high energy absorption under compression. Mater Lett 61:979–982CrossRefGoogle Scholar
  12. 12.
    Kaune G, Müller-Buschbaum P (2010) Gradient-doping of a conductive polymer film with a layer-by-layer approach. Phys Status Solidi RRL 4:52–54CrossRefGoogle Scholar
  13. 13.
    Ishiguro Y, Inagi S, Fuchigami T (2011) Gradient doping of conducting polymer films by means of bipolar electrochemistry. Langmuir 27:7158–7162CrossRefGoogle Scholar
  14. 14.
    Xu EY et al. (2010) Doped carbon nanotube array with a gradient of nitrogen concentration. Carbon 48:3097–3102CrossRefGoogle Scholar
  15. 15.
    Yang Z et al. (2007) Comparison between gradient-doping GaAs photocathode and uniform-doping GaAs photocathode. Appl Opt 46:7035–7039CrossRefGoogle Scholar
  16. 16.
    Pang X et al. (2018) Facile fabrication of gradient density organic aerogel foams via density gradient centrifugation and UV curing in one-step. J Sol-Gel Sci Technol 85:243–250CrossRefGoogle Scholar
  17. 17.
    Camenzind A, Schweizer T, Sztucki M, Pratsinis SE (2010) Structure and strength of silica-PDMS nanocomposites. Polymer 51:1796–1804CrossRefGoogle Scholar
  18. 18.
    Suzuki N, Kamachi Y, Takai K, Kiba S, Sakka Y, Miyamoto N, Yamauchi Y (2014) Effective use of mesoporous silica filler: comparative study on thermal stability and transparency of silicone rubbers loaded with various kinds of silica particles. Eur J Inorg Chem 2014:2773–2778Google Scholar
  19. 19.
    Stober W, Fink A (1968) Controlled growth of monodisperse silica spheres in the micron size range. J Colloid Interface Sci 26:62–69CrossRefGoogle Scholar
  20. 20.
    Neville F, Dixon L, Hyde E (2016) A comparative study of hydrophobic silica particle synthesis. Adv Powder Technol 27:2317–2323CrossRefGoogle Scholar
  21. 21.
    Egbuchunam T, Balkose D (2012) Effect of supercritical ethanol drying on the properties of zinc oxide nanoparticles. Dry Technol 30:739–749CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  1. 1.Research Center of Laser FusionChina Academy of Engineering PhysicsMianyangPR China

Personalised recommendations