The influence of grain size on the magnetic properties of Fe3O4 nanocrystals synthesized by solvothermal method

  • Zhang Shaoqiang
  • Tian Dong
  • Zhang Geng
  • He Lin
  • Zheng Hua
  • Hu Jun
  • Li Yi
  • Liu Minxia
  • Hu Yaohua
  • Zhang Wei
Original Paper: Nano-structured materials (particles, fibers, colloids, composites, etc.)
  • 43 Downloads

Abstract

The peculiar magnetic properties of superparamagnetic iron oxide nanoparticles (SIONs) have spurred great interest in their potential application in enhancing medical images and drug delivery. Currently hindering the application of nanomagnetic particles in these fields is due to SIONs nonuniform size distribution, agglomeration, non-crystallinity, and low magnetic moment. In this paper, magnetic nanocrystals of different sizes and morphologies were prepared by the solvothermal method, which utilized an n-hexane-surfactant system with Fe(acac)3 and iron-powder precursors. The crystalline structure and particle size of grown SIONs are characterized by X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM). HRTEM showed that the SIONs were approximately 5.6–6.8 nm in size with no agglomeration and a uniform distribution. Within the reaction time, HRTEM also confirmed that the shape and nanocrystals of SIONs had changed from an irregular crystal shape to triangles and quadrilaterals, and finally to hexagonal nanoparticles. According to the test results of the magnetic properties test and the literature, the material that has been synthesized is a superparamagnetic material. And the maximum saturation magnetization was 62.65 emu/g, which is reported among the largest magnetic properties of SIONs at a size of 6.8 nm.

Superparamagnetic Fe3O4 nanoparticals with different size and morphology were prepared by solvothermal method in N-hexane-surfactant system with the precursors of Fe(acac)3 and iron powder. With the increasing reaction time and under the regulation of the surfactant molecules, the morphology and nanocrystals of SIONs have initially changed from the irregular crystal to triangles and quadrilaterals shape, and finally to the hexagonal nanoparticles.

Highlights

  • The SIONs are approximately 5.6–6.8 nm in size with no agglomeration and a uniform distribution.

  • The maximum saturation magnetization was 62.65 emu/g, which is reported among the largest magnetic properties of SIONs at a size of 6.8 nm.

Keywords

Fe3O4 nanocrystal Solvothermal method Morphology Magnetic property 

Notes

Acknowledgements

This work was supported by the National Natural Science Foundation of China (Grant No. 61501118), the Science and Technology Planning Project of Guangdong Province, China (Grant Nos. 2017A010101020 and 2017A010101038), the Natural Science Foundation of Guandong Province, China (Grant Nos. 2015A03031346 and 2018A030313388), and the Youth Innovative Talents Project of Guangdong Education Department, China (Grant No. 2015KQNCX160).

Compliance with ethical standards

Conflict of interest

The authors declare that they have no conflict of interest.

References

  1. 1.
    Kopanja L, Milosevic I, Panjan M, Damnjanovic V, Tadic M (2016) Sol–gel combustion synthesis, particle shape analysis and magnetic properties of hematite (α-Fe2O3) nanoparticles embedded in an amorphous silica matrix. Appl Surf Sci 362:380–386CrossRefGoogle Scholar
  2. 2.
    Tadic M, Kralj S, Jagodic M, Hanzel D, Makovec D (2014) Magnetic properties of novel superparamagnetic iron oxidenanoclusters and their peculiarity under annealing treatment. Appl Surf Sci 322:255–264CrossRefGoogle Scholar
  3. 3.
    Pan Y, Du XW, Zhao F et al. (2012) Magnetic nanoparticles for the manipulation of proteins and cells. Chem Soc Rev 41:2912–2942CrossRefGoogle Scholar
  4. 4.
    Wang DS, He JB, Rosenzweig N et al. (2004) Superparamagnetic Fe2O3 beads-CdSe/ZnS quantum dots core-shell nanocomposite particles for cell separation. Nano Lett 4:409–413CrossRefGoogle Scholar
  5. 5.
    Bao J, Chen W, Liu TT et al. (2007) Bifunctional Au-Fe3O4 nanoparticles for protein separation. ACS Nano 1:293–298CrossRefGoogle Scholar
  6. 6.
    Tang SQ, Moon SJ, Park KH (2011) Feasibility of TEOS coated CoFe2O4 nanoparticles to a GMR biosensor agent for single molecular detection. J Nanosci Nanotechnol 11:82–89CrossRefGoogle Scholar
  7. 7.
    Frey NA, Peng S, Cheng K et al. (2009) Magnetic nanoparticles: synthesis, functionalization, and applications in bioimaging and magnetic energy storage. Chem Soc Rev 38(9):2532–2542CrossRefGoogle Scholar
  8. 8.
    Shao H, Min C, Issadore D et al. (2012) Magnetic nanoparticles and micro NMR for diagnostic applications. Theranostics 2(1):55–65CrossRefGoogle Scholar
  9. 9.
    Cheng L, Ruan WM, Zou BF, Liu YY, Wang YQ (2017) Chemical template-assisted synthesis of monodisperse rattle-type Fe3O4@C hollow microspheres as drug carrier. Acta Biomater 58:432–441CrossRefGoogle Scholar
  10. 10.
    Cao SW, Zhu YJ, Ma MY et al. (2008) Hierarchically nanostructured magnetic hollow spheres of Fe3O4 and γ-Fe2O3: preparation and potential application in drug delivery. J Phys Chem C 112:1851–1856CrossRefGoogle Scholar
  11. 11.
    Gao JH, Gu HW, Xu B (2009) Multifunctional magnetic nanoparticles: design, synthesis, and biomedical applications. Acc Chem Res 42:1097–1107CrossRefGoogle Scholar
  12. 12.
    Liu ZL, Wang HB, Lu QH et al. (2004) Synthesis and characterization of ultrafine well-dispersed magnetic nanoparticles. J Magn Magn Mater 283:258–262CrossRefGoogle Scholar
  13. 13.
    Wang X, Zhuang J, Peng Q et al. (2005) A general strategy for nanocrystal synthesis. Nature 437:121–124CrossRefGoogle Scholar
  14. 14.
    Alberto GB, Maximiliano BS, Victor S (2012) Structure of reverse microemulsion- templated metal hexacyanoferrate nanoparticles. Nanoscale Res Lett 7(1):83–87CrossRefGoogle Scholar
  15. 15.
    Park J, An KJ, Hwang Y et al. (2004) Ultra-large-scale syntheses of monodisperse nanocrystals. Nat Mater 3:891–895CrossRefGoogle Scholar
  16. 16.
    Gharibshahian M, Nourbakhsh MS, Mirzaee O (2018) Evaluation of the superparamagnetic and biological properties of microwave assisted synthesized Zn & Cd doped CoFe2O4 nanoparticles via Pechini sol–gel method. J Sol-Gel Sci Tech 85:684–692CrossRefGoogle Scholar
  17. 17.
    Tadić M, Kusigerski V, Marković D, Panjan M, Milošević I (2012) Highly crystalline superparamagnetic iron oxide nanoparticles (SPION) in a silica matrix. J Alloy Comp 525:28–33CrossRefGoogle Scholar
  18. 18.
    De Faria DLA, Silva SV, De Oliveira MT (1997) Microspectroscopy of some Raman iron oxides and oxyhydroxides. J Raman Spectrosc 28:873–878CrossRefGoogle Scholar
  19. 19.
    Gouadec G, Colomban P (2007) Raman spectroscopy of nanomaterials: how spectra relate to disorder, particle size and mechanical properties. Prog Cryst Growth Ch 53:1–56CrossRefGoogle Scholar
  20. 20.
    Burda C, Chen X, Narayanan R et al (2005) Chemistry and properties of nanocrystals of different shapes. Chem Rev 105:1025–1029CrossRefGoogle Scholar
  21. 21.
    Cornell RM, Schwertmann U (2003) The iron oxides: structure, properties, reactions, occurrence and uses. Wiley-VCH, Weinheim, 7–35Google Scholar
  22. 22.
    Lee K, Lee SY, Oh MC, Ahn BM (2018) Alkaline metal reagent-assisted synthesis of monodisperse iron oxide nanostructures Metals 8:107–116CrossRefGoogle Scholar
  23. 23.
    Li L, Yang Y, Ding J, Xue JM (2010) Synthesis of magnetite nanooctahedra and their magnetic field-Induced two-/three-dimensional superstructure. Chem Mater 22:3183–3191CrossRefGoogle Scholar
  24. 24.
    Bao NZ, Shen LM, Wang YH, Padhan P, Gupta A (2007) A facile thermolysis route to monodisperse ferrite nanocrystals. J Am Chem Soc 129:12374–12375CrossRefGoogle Scholar
  25. 25.
    Kovalenko MV, Bodnarchuk MI, Lechner RT, Hesser G, Schäffler F, Heiss W (2007) Fatty acid salts as stabilizers in size- and shape-controlled nanocrystal synthesis: the case of inverse spinel iron oxide. J Am Chem Soc 129:6352–6353CrossRefGoogle Scholar
  26. 26.
    Teja A, Koh PY (2009) Synthesis, properties, and applications of magnetic iron oxide nanoparticles. Prog Cryst Growth Ch 55:22–45CrossRefGoogle Scholar
  27. 27.
    Tan YW, Zhuang ZB, Peng Q et al. (2008) Room-temperature soft magnetic iron oxide nanocrystals: synthesis, characterization, and size-dependent magnetic properties. Chem Mater 20:5029–5034CrossRefGoogle Scholar
  28. 28.
    Si SF, Li CH, Wang X et al. (2005) Magnetic monodisperse Fe3O4 nanoparticles. Cryst Growth Des 5(2):391–393CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  1. 1.School of Electrical Engineering and IntelligentizationDongguan University of TechnologyDongguanPR China
  2. 2.College of Materials Science and EngineeringSouth China University of TechnologyGuangzhouPR China
  3. 3.National Key Laboratory for Material Oriented Chemical Engineering and School of Chemical EngineeringNanjing Tech UniversityNanjingPR China

Personalised recommendations