Improvement of structural and optical properties of ZnAl2O4:Cr3+ ceramics with surface modification by using various concentrations of zinc acetate

  • Dong Zhang
  • Chunyu Du
  • Jingxin Chen
  • Qiang Shi
  • Qingru Wang
  • Shuhong Li
  • Wenjun Wang
  • Xunling Yan
  • Quli Fan
Original Paper: Nano-structured materials (particles, fibers, colloids, composites, etc.)

Abstract

The influence of surface modification with various concentrations of zinc acetate solution on the structural and optical properties of ZnAl2O4:Cr3+ particles was studied. The X-ray diffraction peaks assigned to the spinel structure of ZnAl2O4:Cr3+ powders revealed a tiny shift towards the lower angle, and ZnO phase was detected when ZnAl2O4:Cr3+ crystals surface was modified. The results of X-ray photoelectron spectra confirmed that the antisite defects related to tetrahedral Al existed in the surface lattices of zinc aluminate crystals. The signal intensity of XPS assigned to tetrahedral Al decreased after surface modification, while that of XPS assigned to octahedral Zn increased. The results of transmission electron microscope showed that the surface lattices of ZnAl2O4:Cr3+ particles became more ordered after surface modification, and zinc oxide nanocrystals were observed as a coating layer or dispersed particles surrounding ZnAl2O4:Cr3+ particles when the concentration of Zn(AC)2 solution increased up to 1.5 mol/L. The red emission assigned to Cr3+ ions in spinel lattices was detected at room temperature, and the emission intensity was enhanced when ZnAl2O4:Cr3+ crystals was modified. While the emission intensity was reduced when the concentration of Zn(AC)2 solution increased up to 1.5 mol/L.

ZnAl2O4:Cr3+ crystals were modified by using with various concentrations of zinc acetate (0.5 M, 1.0 M and 1.5 M). These crystals surfaces showed different morphologies, and the crystallinity and photoluminescence performances were enhanced.

Highlights

  • The crystallinity of ZnAl2O4:Cr3+ crystals is improved by using surface modification.

  • The defects transform from AlZn to ZnAl after surface modification.

  • The PL intensity is 2.5 times than that of crystals without surface modification

Keywords

Ceramics Zinc aluminate Surface defects Photoluminescence 

Notes

Acknowledgements

This work was supported by Initial Foundation for Doctor Project of Liaocheng University (No. 318051410), the Project of Science and Technology Plan for University of Shandong Province (No. J16LJ05), the National Natural Science Foundation of China (No. 61574071, No.61775089, No. 11604132, No. 11604133), Industrial Alliance Fund of Shandong Provincial Key Laboratory (Grant No.SDKL2016038) and ‘Taishan scholars’ construction special fund of Shandong Province.

Compliance with ethical standards

Conflict of interest

The authors declare that they have no conflict of interest.

References

  1. 1.
    Motloung SV, Dejene FB, Swart HC, Ntwaeaborwa OM (2015) Effects of Cr3+ mol% on the structure and optical properties of the ZnAl2O4:Cr3+ nanocrystals synthesized using sol-gel process. Ceram Int 41:6776–6783CrossRefGoogle Scholar
  2. 2.
    Cheng BC, Qu SC, Zhou HY, Wang ZG (2006) Porous ZnAl2O4 spinel nanorods doped with Eu3+: synthesis and photoluminescence. Nanotechnology 17:2982–2987CrossRefGoogle Scholar
  3. 3.
    Battistona S, Rigoa C, Severoa EC, Mazuttia MA, Kuhna RC, Gündelb A, Foletto EL (2014) Synthesis of Zinc Aluminate (ZnAl2O4) spinel and its application as photocatalyst. Mater Res 17:734–738CrossRefGoogle Scholar
  4. 4.
    Singh RK, Yadav A, Narayan A, Chandra M, Verma RK (2012) Thermal, XRD, and magnetization studies on ZnAl2O4 and NiAl2O4 spinels, synthesized by citrate precursor method and annealed at 450 and 650 oC. J Therm Anal Calorim 107:205–210CrossRefGoogle Scholar
  5. 5.
    Joo OS, Jung KD (2003) Stability of ZnAl2O4 Catalyst for Reverse-Water-Gas-Shift Reaction (RWGSR). Bull Korean Chem Soc 24:86–90CrossRefGoogle Scholar
  6. 6.
    Peng C, Li GG, Geng DL, Shang MM, Hou ZY, Lin J (2012) Fabrication and luminescence properties of one-dimensional ZnAl2O4 and ZnAl2O4:A3+ (A=Cr, Eu, Tb) microfibers by electrospinning method. Mater Res Bull 47:3592–3599CrossRefGoogle Scholar
  7. 7.
    Fernández-Osorio A, Rivera CE, Vázquez-Olmos A, Chávez J (2015) Luminescence ceramic nano-pigments based on terbium-doped zinc aluminate: synthesis, properties and performance. Dyes Pigm 119:22–29CrossRefGoogle Scholar
  8. 8.
    Kumar M, Mohapatra M, Natarajan V (2014) Luminescence characteristics of blue emitting ZnAl2O4:Ce nanophosphors. J Lumin 149:118–124CrossRefGoogle Scholar
  9. 9.
    Zhang D, Wang CZ, Liu YL, Shi Q, Wang WJ, Zhai Y (2012) Green and red photoluminescence from ZnAl2O4:Mn phosphors prepared by sol-gel method. J Lumin 132:1529–1531CrossRefGoogle Scholar
  10. 10.
    Zhang D, Yin YL, Liu YL, Chao WB, Zhai Y (2013) The photoluminescence and magnetic properties of ZnAl2O4:Mn nanocrystals. J Phys Chem Solids 74:1131–1135CrossRefGoogle Scholar
  11. 11.
    Matsui H, Xu CN, Liu Y, Tateyama H (2004) Origin of mechanoluminescence from Mn-activated ZnAl2O4: triboelectricity-induced electroluminescence. Phys Rev B 69:235109CrossRefGoogle Scholar
  12. 12.
    Wang SF, Sun GZ, Fang LM, Lei L, Xiang X, Zu XT (2015) A comparative study of ZnAl2O4 nanoparticles synhesized from different aluminum salts for use as fluorescence materials. Sci Report 5:12849CrossRefGoogle Scholar
  13. 13.
    Anand GT, Kennedy LJ, Vijaya JJ (2013) Microwave combustion synthesis, structural, optical and magnetic properties of Zn1-xCoxAl2O4 (0≤×≤0.5) spinel nanostructures. J Alloy Compd 581:558–566CrossRefGoogle Scholar
  14. 14.
    Kim YJ, Reddy DA, Park H, Kim TK (2016) Anionic precursor-mediated morphology-controlled synthesis of ZnS nanostructures: Morphology-dependent tunable photoluminescence in the visible region and pulsed laser-induced efficient reduction of Cr(VI). Ceram Int 42:12046–54CrossRefGoogle Scholar
  15. 15.
    Yi X, Zhou SM, Chen C, Lin H, Feng Y, Wang K, Ni Y (2014) Fabrication of Ce:YAG, Ce,Cr:YAG and Ce:YAG/Ce, Cr:YAG dual-layered composite phosphor ceramics for the application of white LEDs. Ceram Int 42:7043–7047CrossRefGoogle Scholar
  16. 16.
    Zhang D, Ma XX, Zhang Q, Xie YR, Shi Q, Wang QR, Wang WJ (2016) Influence of Zn/Al molar ratio on the structural and photoluminescence performances of ZnxAl2O4:Cr3+ phosphors. J Alloy Comp 688:581–587CrossRefGoogle Scholar
  17. 17.
    Singh V, Chakradhar RPS, Rao JL, Kwak HY (2011) EPR and photoluminescence properties of combustion-synthesized ZnxAl2O4:Cr3+ phosphors. J Mater Sci 46:2331–2337CrossRefGoogle Scholar
  18. 18.
    Zhang D, Qiu YH, Xie YR, Zhou XC, Wang QR, Shi Q, Li SH, Wang WJ (2017) The improvement of structure and photoluminescence properties of ZnxAl2O4:Cr3+ ceramics synthesized by using solvothermal method. Mater Des 115:37–45CrossRefGoogle Scholar
  19. 19.
    Sreeja V, Smitha TS, Nand D, Ajithkumar TG, Joy PA (2008) Size dependent coordination behavior and cation distribution in MgAl2O4 nanoparticles from 27Al solid state NMR studies. J Phys Chem C 112:14737–14744CrossRefGoogle Scholar
  20. 20.
    Zhang D, Guo QJ, Ren YF, Wang CZ, Shi Q, Wang QL, Xiao X, Wang WJ, Fan QL (2018) Influence of inversion defects and Cr-Cr pairs on the photoluminescent performance of ZnAl2O4 crystals. J Sol-Gel Sci Technol 85:121–131CrossRefGoogle Scholar
  21. 21.
    Cullity BD (1978) Elements of X-ray Diffraction. Addison Wesley, Boston, pp 285Google Scholar
  22. 22.
    Tshabalala KG, Cho SH, Park JK, Pitale SS, Nagpure IM, Kroon RE, Swart HC, Ntwaeaborwa OM (2011) Luminescent prperties and X-ray photoelectron spectroscopy study of ZnAl2O4:Ce3+,Tb3+ phosphor. J Alloy Comp 509:10115–10120CrossRefGoogle Scholar
  23. 23.
    Iaiche S, Djelloul A (2015) ZnO/ZnAl2O4 nanocomposite films studied by X-ray diffraction, FTIR, and X-ray photoelectron spectroscopy. J Spectrosc 19:9Google Scholar
  24. 24.
    Benito N, Díaz D, Vergara L, Galindo RE, Sánchez O, Palacio C (2014) An XPS and ellipsometry study of Cr-O-Al mixed oxides grown by reactive magnetron sputtering. Surf Coat Technol 206:1484–1489CrossRefGoogle Scholar
  25. 25.
    Bessière A, Jacquart S, Priolkar K, Lecointre A, Viana B, Gourier D (2011) ZnGa2O4:Cr3+: a new red long-lasting phosphor with high brightness. Opt Exp 19:10131–10137CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2018

Authors and Affiliations

  • Dong Zhang
    • 1
    • 2
  • Chunyu Du
    • 1
  • Jingxin Chen
    • 1
  • Qiang Shi
    • 1
    • 2
  • Qingru Wang
    • 1
    • 2
  • Shuhong Li
    • 1
    • 2
  • Wenjun Wang
    • 1
    • 2
  • Xunling Yan
    • 1
    • 2
  • Quli Fan
    • 1
    • 2
    • 3
  1. 1.School of Physical Science and Information TechnologyLiaocheng UniversityLiaochengChina
  2. 2.Key Laboratory of Optical Communication Science and Technology of Shandong ProvinceLiaocheng UniversityLiaochengChina
  3. 3.Institute of Advanced MaterialsNanjing University of Posts and TelecommunicationsNanjingChina

Personalised recommendations