Mechanical reinforced fiber needle felt/silica aerogel composite with its flammability
- 93 Downloads
Fiber needle felt–silica aerogel composite was successfully prepared by via sol–gel process based on water glass. The thermal conductivity show V-type variation tendency with the increase of water to Si. Thermogravimetric analysis-differential scanning calorimetry analysis revealed that the thermal stability was up to approximately 390.58 °C. It has been found that the fire hazard of the composites decreased with the increased ratio of water to Si according to the cone calorimeter test, which can be characterized by peak heat release rate, fire performance index, and fire growth rate index. The fiber needle felt/aerogels present greatly improved compressive and flexural strength (elastic modulus: 0.1–0.97 MPa; flexural modulus: 0.33–0.66 MPa) while keeping inherent properties of pure silica aerogel: low bulk density (0.166 g/cm3), low thermal conductivity of 0.0236 W/m·K, and high specific surface area (1091.62 m2/g). As a result, the as-prepared composite shows a great potential to be applied in the thermal insulation field.
Fiber needle felt reinforced silica aerogel were obtained under ambient pressure.
The water glass based aerogel show high flexibility & thermal insulation ability.
The composites' flammable ability were studied through cone calorimeter.
KeywordsAerogel composites Fiber needle felt Mechanical properties Thermal insulation Flammability
This research was financially supported by the National Key Research and Development Program of China (2017YFC0804900 and 2017YFC0804907), the Open Project Program of State Key Laboratory of Fire Science (HZ2017-KF12), and the Natural Science Foundation of China (No. 51706165).
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflict of interest.
- 14.Guanming DZLXY (2006) Study on preparation and performance of SiO_2 aerogels composites reinforced by mullite fiber [J]. N Chem Mater 7:021Google Scholar
- 38.Coffman BE, Fesmire JE, White S, Gould G, Augustynowicz S (2010) Aerogel blanket insulation materials for cryogenic applications. AIP Conference Proceeding 1218: 913–920.Google Scholar
- 39.H Wu, Y Chen, Q Chen, Y Ding, X Zhou, H Gao (2013) Synthesis of flexible aerogel composites reinforced with electrospun nanofibers and microparticles for thermal insulation. J Nanomater 2013: 1-8.Google Scholar