Optimization of process parameters and its effect on structure and morphology of CuO nanoparticle synthesized via the sol−gel technique
- 202 Downloads
This article describes systematic basic research on the optimization of the processing parameters of sol−gel technique for synthesis of the high purity CuO nanoparticles. Effect of the synthesis parameters such as copper salt concentration, solvent and gelating agent, optimized one at a time, was investigated by employing XRD, TEM, FESEM, micro-Raman, UV-visible-NIR and PL spectroscopies. XRD results clearly demonstrate the monoclinic structure of CuO nanoparticles with traceable impurities at a lower molar concentration of Cu2+, transition of nucleation system from homogeneous to heterogeneous state with the increase in concentration of Cu2+ from 0.05 to 0.15 M. It was also found that the isopropyl alcohol offers better results in comparison to ethanol and water. Moreover, the lattice parameters, space group, and crystal system were determined by powder X-ray diffraction method. Further we propose the optimization of synthesis process using ethylene glycol and citric acid (EG:CA). The Raman analysis confirmed the influence of ethylene glycol and citric acid ratio and TEM observations confirmed that EG:CA 1:2 ratio formulate homogenous flower-like nanostructures. The optical absorption of CuO nanostructures can be easily tuned by varying the concentration of citric acid without changing other conditions; it shows the role of synthesis parameters more significant. Our results suggest that the prepared CuO nanostructures have a potential to be used as absorbing material in solar cell applications.
CuO nanoparticles are successfully synthesized via simple non-aqueous sol-gel method.
The effect of various process parameters on the morphology and structure of CuO nanoparticles are investigated.
Vibrant modifications in the morphology of CuO nanoparticles are detected via TEM and SEM.
Isopropyl alcohol gives better crystallization of CuO nanostructures in comparison to ethanol.
1:2 ratio of ethylene glycol and citric acid yield superior assembly of CuO nanostructures.
KeywordsCuO nanostructures Sol–gel technique Solvent Gelating agent Citric acid
Ms. Hafsa Siddiqui and Mr. Mohammad Ramzan Parra deeply acknowledge the UGC, New Delhi, and HRDG-CSIR for the financial support given in the form of UGC-MANF reference no. F1-17.1/2011-12/MANF-MUS-MAD-4694 and CSIR-SRF ack. no. 163320/2K14/1. The authors would like to acknowledge the Director-UGC-DAE-Consortium for Scientific Research, Indore Centre (M.P.), India for performing XRD, Raman and UV−Vis-diffused reflectance measurements. The authors are very grateful to the USIF-AMU, Aligarh (U.P.) for the TEM facility, and Department of Physics and Astrophysics, University of Delhi, India for the FESEM facility.
Compliance with ethical standards
Conflict of interest
The authors declare that they have no conflict of interest.
- 9.Fernánde AI, Calleja A, Chimenos JM, Fernández MA, Capdevila XG, Segarra M, Xuriguera H, Espiell F (2005) Preparation of ultra-fine CuO: comparison of polymer gel methods and conventional precipitation processes. J Sol-Gel Sci Technol 36:11. https://doi.org/10.1007/s10971-005-4789-0 CrossRefGoogle Scholar
- 10.Etefagh R, Azhir E, Shahtahmasebi N (2013) Synthesis of CuO nanoparticles and fabrication of nanostructural layer biosensors for detecting Aspergillus niger fungi. Sci Iran 20(3):1055–1058Google Scholar
- 13.Niederberger M, Pinna N (2009) Metal oxide nanoparticles in organic solvents. Springer-Verlag, London. https://doi.org/10.1007/978-1-84882-671-7
- 18.Bhaumik A, Shearin AM, Patel R, Ghosh K (2014) Significant enhancement of optical absorption through nano-structuring of copper based oxide semiconductors: possible future materials for solar energy applications. Phys Chem Chem Phys 16:11054–11066. https://doi.org/10.1039/C4CP00827H CrossRefGoogle Scholar
- 31.Siddiqui H, Qureshi MS, Haque FZ (2014) Structural and optical properties of CuO nanocubes prepared through simple hydrothermal route. J Sci Eng Res 5(3):173–177Google Scholar
- 34.Siddiqui, H, Parra, MR, Qureshi MS, Haque FZ (2018) Studies of structural, optical, and electrical properties associated with defects in sodium-doped copper oxide (CuO/Na) nanostructures. J Mater Sci. https://doi.org/10.1007/s10853-018-2179-6
- 35.Sharma A, Dutta RK, Roychowdhury A, Das D (2016) Studies on structural defects in bare, PVP capped and TPPO capped copper oxide nanoparticles by positron annihilation lifetime spectroscopy and their impact on photocatalytic degradation of rhodamine B. RSC Adv 6:74812–74821. https://doi.org/10.1039/C6RA12795A CrossRefGoogle Scholar
- 39.Haque FZ, Nandanwar R, Singh P (2017) Evaluating photodegradation properties of anatase and rutile TiO2 nanoparticles for organic compounds. Optik 128:191. https://doi.org/10.1016/j.ijleo.2016.10.025Google Scholar
- 44.Sukhorukov YP, Loshkareva NN, Samokhvalov AA, Moskvin AS (1995) Absorption spectra of CuO single crystals near the absorption edge and the nature of the optical gap in copper oxides. J Exp Theor Phys 81(5):998. http://doi.org/1063-7761/95/110998-05$10.00Google Scholar
- 46.Balamurugan B, Mehta B, Avasthi D, Singh F, Arora A, Rajalakshmi M, Raghavan G, Tyagi A, Shivaprasad S (2002) Modifying the nanocrystalline characteristics—structure, size, and surface states of copper oxide thin films by high-energy heavy-ion irradiation. J Appl Phys 92:3304. https://doi.org/10.1063/1.1499752 CrossRefGoogle Scholar