Uranium recovery with zinc distillation from a liquid zinc cathode for pyroprocessing
- 11 Downloads
U recovery test was performed on a Zn-U alloy to confirm the feasibility of Zn as an alternative cathode material. An evaporation test of pure Zn first confirmed that Zn started to evaporate at above 450 °C. Next, a U recovery test was performed using liquid Zn in which U was electrochemically deposited. U was successfully recovered via distillation at 800 °C, leaving a disk-shaped product. The product was mostly U, indicating that the Zn was completely removed. These results confirm the feasibility of Zn as a cathode material, which offers the advantage of a lower operation temperature compared to Cd distillation.
KeywordsDistillation Liquid Zn cathode Pyroprocessing U recovery Zn
This work was supported by a National Research Foundation of Korea Grant funded by the Korean Ministry of Science, ICT and Future Planning [Grant Number 2017M2A8A5015079].
- 1.Yoo J, Lee B, Lee H, Kim E (2007) Investigation of pyroprocessing concept and its applicability as an alternative technology for conventional fuel cycle. J Korean Radioact Waste Soc 5:283–295Google Scholar
- 2.Yoo J, Hong K, Lee H (2008) A conceptual design study for a spent fuel pyroprocessing facility of a demonstration scale. J Korean Radioact Waste Soc 6:233–244Google Scholar
- 3.Brunsvold A, Roach P, Westphal B (2000) Design and development of a cathode processor for electrometallurgical treatment of spent nuclear fuel. In: Proceedings, 8th International Conference on Nuclear Engineering, ICONE8–8702 4393–402, Baltimore, MD, USA, 2–6 April, 2000Google Scholar
- 8.Nuclear Science (2012) Spent nuclear fuel reprocessing flowsheet, NEA/NSC/WPFC/DOC(2012)15, OECDGoogle Scholar
- 12.Johnson I, Chasanov MG, Yonco RM (1965) Pu-Cd system: thermodynamics and partial phase diagram. Trans Metall Soc AIME 233:1408–1414Google Scholar
- 21.Massalski TB, Okamoto H, Subramanian PR, Kacprzak L (1986) Binary alloy phase diagrams, 1st edn, American Society for Metals International, Materials Park, Ohio, USA, pp. 2149–2150Google Scholar