Mössbauer study of semiconducting and ferrimagnetic fly ash-recycled glass

Summary

Room temperature Mössbauer spectrum of fly ash-recycled glass (FARG), prepared with more than 86 mass% of fly ash and less than 14 mass% of Fe₂O₃, comprises two types of doublets due to Fe(II) and Fe(III) of magnetite nanoparticles. Isothermal annealing of fly ash-recycled glass at 1100 °C for 60 minutes results in a precipitation of ferrimagnetic magnetite phase having an internal magnetic field of 46.4-48.2 T. When the Fe₂O₃ content is equal to or more than 14%, room temperature Mössbauer spectrum of FARG shows a magnetic hyperfine structure due to a magnetite phase, in addition to two doublets due to Fe(II) and Fe(III). An increase in the electric conductivity is observed from the order of 10^-8 to 10^-6 S ^. cm^-1 after heat treatment at around the crystallization temperature. This can be ascribed to an improved step-by-step electron hopping from Fe(II) to Fe(III) of distorted FeO₄ tetrahedra in the three-dimensional glass network.