Chain structure comparison of two low density polyethylene resins fractionated by temperature rising elution fractionation and thermal fractionation

  • Pei Li
  • Yanhu XueEmail author
  • Wei Liu
  • Guangping SunEmail author
  • Xiangling Ji
ORIGINAL PAPER
First Online:
  • 8 Downloads

Abstract

Two low-density polyethylene resins were fractionated into 11 fractions using the temperature rising elution fractionation technique. The resins were of injection molding grade with similar densities but different melt indexes and mechanical properties. High-temperature gel permeation chromatography (HT-GPC), 13C-nuclear magnetic resonance (13C-NMR) spectroscopy, differential scanning calorimetry (DSC), and successive self-nucleation/annealing (SSA) thermal fractionation were employed to characterize the original resins and their fractions. Resin A had a higher molecular weight and broader molecular weight distribution than resin B did. The highest contents were found for the 80 °C and 75 °C fractions of resins A and B, respectively. In addition, the highest molecular weights for resins A and B at 2.14 × 105 and 1.42 × 105 g/mol, respectively, were attained for the fractions eluted at 80 °C. According to the results of 13C-NMR, the total branching contents of resins A and B, including short- and long-chain branching, were 3.63 mol% and 4.89 mol%, respectively. DSC analysis revealed that the crystallinity of fractions 3–10 of resin A was lower than that of resin B. We noted the presence of approximately eight multiple melting peaks in the original sample and fractions from the results of SSA. These peaks indicated the inhomogeneity of the molecular chain. Lw and Ln of resin A were longer than those of resin B. Lastly, the relationship between chain structure and property was also discussed.

Keywords

Chain structure Low density polyethylene Temperature rising elution fractionation Thermal fractionation· 
This is a preview of subscription content, log in to check access.

Notes

References

  1. 1.
    Simanke AG, Galland GB, BaumhardtNeto R, Quijada R, Mauler RS (1999) Influence of the type and the comonomer contents on the mechanical behavior of ethylene/α-olefin copolymers. J Appl Polym Sci 74(5):1194–1200CrossRefGoogle Scholar
  2. 2.
    Zhang JS, Qiao JL (2011) Polyethylene resin and its application. BeijingGoogle Scholar
  3. 3.
    Knuuttila H, Lehtinen A, Nummila-Pakarinen A (2004) Advanced polyethylene technologies—controlled material properties. Adv Polym Sci 169:13–27CrossRefGoogle Scholar
  4. 4.
    Mattice WL, Stehling FC (1981) Branch formation in low-density polyethylene. Macromolecules 14:1479–1484CrossRefGoogle Scholar
  5. 5.
    Mattice WL (1983) Complex branch formation in low-density polyethylene. Macromolecules 16:487–490CrossRefGoogle Scholar
  6. 6.
    Otocka EP, Roe RJ, Hellmann MY, Muglia PM (1971) Distribution of long and short branches in low-density polyethylenes. Macromolecules 4(4):507–512CrossRefGoogle Scholar
  7. 7.
    Krallis A, Pladis P, Kiparissides C (2007) Prediction of the bivariate molecular weight-long chain branching distribution in high-pressure low-density polyethylene autoclaves. Macomol Theory Simul 16:593–609CrossRefGoogle Scholar
  8. 8.
    Hsieh ET, Tso CC, Byers JD, Johnson TW, Fu Q, Cheng SZD (1997) Intermolecular structural homogeneity of metallocene polyethylene copolymers. J Macromol Sci Phys 36(5):615–628CrossRefGoogle Scholar
  9. 9.
    Xue YH, Bo SQ, Ji XL (2015) Molecular chain heterogeneity of a branched polyethylene resin using cross-fractionation techniques. J Polym Res 22:160CrossRefGoogle Scholar
  10. 10.
    Kouda S (2008) Prediction of processability at extrusion coating for low-density polyethylene. Polym Eng Sci 48(6):1094–1102CrossRefGoogle Scholar
  11. 11.
    Wang C, Chu MC, Lin TL, Lai SM, Shih HH, Yang JC (2001) Microstructures of a highly short-chain branched polyethylene. Polymer 42(4):1733–1741CrossRefGoogle Scholar
  12. 12.
    Xu JT, Xu XR, Feng LX (2000) Short chain branching distributions of metallocene-based ethylene copolymers. Eur Polym J 36(4):685–693CrossRefGoogle Scholar
  13. 13.
    Zhang XZ, Wang SH, Qi YZ (1995) Ethylene derivative engineering. BeijingGoogle Scholar
  14. 14.
    Xue YH, Fan YD, Bo SQ, Ji XL (2015) Microstructure characterization of a complex branched low-density polyethylene. Chin J Polym Sci 33:508–522CrossRefGoogle Scholar
  15. 15.
    Gulmine JV, Janissek PR, Heise HM, Akcelrud L (2002) Polyethylene characterization by FTIR. Polym Test 21(5):557–563CrossRefGoogle Scholar
  16. 16.
    Randall JC (1973) 13C-NMR of ethylene-1-olefin copolymers: extension to the short-chain branch distribution in a low-density polyethylene. J Polym Sci, Part B:Polym Phys 11(2):275–287Google Scholar
  17. 17.
    Xue YH, Bo SQ, Ji XL (2015) Parameters optimization of successive self-nucleation/annealing thermal fractionation experiments for polyethylene resin and comparison with step crystallization. Acta Polym Sin 3:326–330Google Scholar
  18. 18.
    Xue YH, Bo SQ, Ji XL (2016) Solvent gradient fractionation and chain microstructure of complex branched polyethylene resin. J Polym Res 23:131CrossRefGoogle Scholar
  19. 19.
    De Pooter M, Smith PB, Dohrer KK, Bennett KF, Meadows MD, Smith CG (1991) Determination of the composition of common linear low density polyethylene copolymers by 13C-NMR spectroscopy. J Appl Polym Sci 42(2):399–408CrossRefGoogle Scholar
  20. 20.
    Tackx P, Tacx J (1998) Chain architecture of LDPE as a function of molar mass using size exclusion chromatography and multi-angle laser light scattering (SEC-MALLS). Polymer 39(14):3109–3113CrossRefGoogle Scholar
  21. 21.
    Shroff RN, Mavridis H (1999) Long-chain-branching index for essentially linear polyethylenes. Macromolecules 32(25):8454–8464CrossRefGoogle Scholar
  22. 22.
    Li P, Xue YH, Wu XX, Sun GP, Ji XL, Bo SQ (2018) Microstructure characterization of one high-speed extrusion coating polyethylene resin fractionated by solvent gradient fractionation. J Polym Res 25:113CrossRefGoogle Scholar
  23. 23.
    Wild L (1991) Temperature rising elution fractionation. Adv Polym Sci 98:1–47Google Scholar
  24. 24.
    Anantawaraskul S, Soares JBP, Wood-Adams PM (2005) Fractionation of semicrystalline polymers by crystallization analysis fractionation and temperature rising elution fractionation. Adv Polym Sci 82:1–54Google Scholar
  25. 25.
    Desreux V, Spiegels MC (1950) Fractionnement par extraction du polythène. Bull Soc Chim Belg 59(7–8):476–489CrossRefGoogle Scholar
  26. 26.
    Albrecht A, Bruell R, Macko T, Sinha P, Pasch H (2008) Analysing the chemical composition distribution of ethylene-acrylate copolymers: comparison of HT-HPLC, CRYSTAF and TREF. Macromol Chem Phys 209(18):1909–1919CrossRefGoogle Scholar
  27. 27.
    Xu JT, Feng LX, Yang SL (1996) Analysis of polyolefin alloy with TREF. Chem J Chinese U 17(6):991–992Google Scholar
  28. 28.
    Xu JT, Feng LX (2000) Application of temperature rising elution fractionation in polyolefins. Eur Polym J 36(5):867–878CrossRefGoogle Scholar
  29. 29.
    Xue YH, Bo SQ, Ji XL (2015) Comparison of chain structures between high-speed extrusion coating polyethylene resins by preparative temperature rising elution fractionation and cross-fractionation. Chin J Polym Sci 33(11):1586–1597CrossRefGoogle Scholar
  30. 30.
    Xue YH, Fan YD, Bo SQ, Ji XL (2011) Characterization of the microstructure of impact polypropylene alloys by preparative temperature rising elution fractionation. Eur Polym J 47(8):1646–1653CrossRefGoogle Scholar
  31. 31.
    Liu YG, Bo SQ, Zhu YJ, Zhang WH (2005) Studies on the intermolecular structural heterogeneity of a propylene-ethylene random copolymer using preparative temperature rising elution fractionation. J Appl Polym Sci 97(1):232–239CrossRefGoogle Scholar
  32. 32.
    Monrabal B (1994) Crystallization analysis fractionation: a new technique for the analysis of branching distribution in polyolefins. J Appl Polym Sci 52(4):491–499CrossRefGoogle Scholar
  33. 33.
    Mirabella FM, Ford EA (1987) Characterization of linear low-density polyethylene: cross-fractionation according to copolymer composition and molecular weight. J Polym Sci B Polym Phys 25(4):777–790CrossRefGoogle Scholar
  34. 34.
    Monrabal B, Sancho-Tello J, Mayo N, Romero L (2007) Crystallization elution fractionation. A new separation process for polyolefin resins. Macromol Symp 257(1):71–79CrossRefGoogle Scholar
  35. 35.
    Müller AJ, Hernández ZH, Arnal ML, Sánchez JJ (1994) Successive self-nucleation/annealing (SSA): a novel technique to study molecular segregation during crystallization. Polym Bull 39(4):465–472CrossRefGoogle Scholar
  36. 36.
    Müller AJ, Arnal ML (2005) Thermal fractionation of polymers. Prog Polym Sci 30(5):559–603CrossRefGoogle Scholar
  37. 37.
    Pasch H, Malik MI, Macko T (2013) Recent advances in high-temperature fractionation of polyolefins. Adv Polym Sci 251:77–140CrossRefGoogle Scholar
  38. 38.
    Xue YH, Yang HR, Bo SQ, Ji XL (2014) Microstructure characterization of low density polyethylene by temperature rising elution fractionation. Acta Polym Sin 12:1576–1584Google Scholar
  39. 39.
    Eselem Bungu PS, Pflug K, Pasch H (2018) Combination of preparative and two-dimensional chromatographic fractionation with thermal analysis for the branching analysis of polyethylene. Polym Chem 9:3142–3157CrossRefGoogle Scholar
  40. 40.
    Eselem Bungu PS, Pasch H (2018) Branching and molar mass analysis of low density polyethylene using the multiple preparative fractionation concept. Polym Chem 9:1116–1131CrossRefGoogle Scholar
  41. 41.
    Galland GB, Quijada R, Rojas R, Bazan G, Komon ZJA (2002) NMR study of branched polyethylenes obtained with combined Fe and Zr catalysts. Macromolecules 35(2):339–345CrossRefGoogle Scholar
  42. 42.
    Randall JC, Zoepfl FJ, Silverman J (1983) A 13C-NMR study of radiation-induced long-chain branching in polyethylene. Macromol Chem Rapid Commun 4(3):149–157CrossRefGoogle Scholar
  43. 43.
    Zhang MQ, Wanke SE (2003) Quantitative determination of short-chain branching content and distribution in commercial polyethylenes by thermally fractionated differential scanning calorimetry. Polym Eng Sci 43(12):1878–1888CrossRefGoogle Scholar
  44. 44.
    Xue YH, Bo SQ, Ji XL (2015) Calibration curve establishment and fractionation temperature selection of polyethylene for preparative temperature rising elution fractionation. Chin J Polym Sci 33:1000–1008CrossRefGoogle Scholar
  45. 45.
    Wild L (1991) Temperature rising elution fractionation. Adv Polym Sci 98:1–47 Google Scholar
  46. 46.
    Müller AJ, Arnal ML (2005) Thermal fractionation of polymers. Prog Polym Sci 30(5):559–603Google Scholar

Copyright information

© The Polymer Society, Taipei 2019

Authors and Affiliations

  1. 1.College of Materials Science and EngineeringJilin UniversityChangchunChina
  2. 2.State Key Laboratory of Polymer Physics and Chemistry, Changchun Institute of Applied ChemistryChinese Academy of SciencesChangchunChina

Personalised recommendations

Cite article

Buy options