Synthesis of BSCCO Films on MgO (100) Substrate by Ultrasonic Spray Pyrolysis Technique
- 135 Downloads
In this study, the HT c Bi-2212 films were fabricated using the ultrasonic spray pyrolysis technique (USP). Structural/microstructural, electrical, magnetic, and critical current density, J c , properties of the films fabricated were studied depending on heat treatment conditions in detail. XRD analysis revealed that a pure Bi-2212 phase formed in all the films, which is confirmed by SEM-EDX analysis. T c values of the films were found near 75 K. J c values of the films were calculated using Beans’ equation. Highest J c value was found to be 3.36×105 A cm−2 at 5 K and 0 T for film A. The results obviously showed that the USP method is a very effective technique for fabrication of the HT c films having high J c values as well as its simplicity, low cost, easily coating.
KeywordsUltrasonic spray pyrolysis technique (USP) HTc thin films Magnetization Critical current density, Jc
This work was supported by Research Fund of Inonu University, Turkey, grant contracts no. 2010/100.