Structural, Magnetic, and Catalytic Properties of Mn-Doped Titania Nanoparticles Synthesized by a Sol–Gel Process
- 50 Downloads
TiO2 nanoparticles (NPs) doped with different concentrations of manganese (1–8 at.%) were synthesized by sol–gel method and characterized to determine their structure, optical, and magnetic properties. X-ray diffraction analysis confirmed the formation of Mn-doped TiO2 NPs with anatase structure and that no impurity phases were present. X-ray photoelectron spectroscopic data indicated that the amount of Mn in the doped TiO2 samples was slightly lower than the theoretical value, and scanning electron microscope images illustrated a morphology consisting of un-aggregated, well-arranged NPs with a homogeneous size distribution. Particle sizes determined from transmission electron microscope images were found to be 17 and 11 nm for pure and Mn-doped TiO2, respectively. The band gap for pure TiO2 was calculated to be 3.26 eV from ultraviolet–visible reflectance spectra, which decreased to 2.70 eV following 8% Mn-doping. The as-prepared pure TiO2 NPs were found to be weakly paramagnetic at room temperature from vibrating sample magnetometer; however, a transformation from paramagnetic to weak ferromagnetism at room temperature was observed for Mn-doped TiO2 (5 at.%) NPs. Mn doped TiO2 (5 at.%) NPs exhibited the higher antibacterial activity against Bacillus subtilis, Escherichia coli and Pseudomonas aeruginosa than the pure TiO2 NPs.
KeywordsStructure, optical, magnetic properties Photocatalysis Antibacterial properties
This work was supported by the 2018 Yeungnam University Research Grant.
- 3.S. Prabhu, M. Pudukudy, S. Sohila, S. Harish, M. Navaneethan, D. Navaneethan, R. Ramesh, and Y. Hayakawa (2018). Synthesis, structural and optical properties of ZnO spindle/reduced graphene oxide composites with enhanced photocatalytic activity under visible light irradiation. Opt. Mater. 79, 186–195.CrossRefGoogle Scholar
- 23.S. Zaman, S. Yeasmin, Y. Inatsu, C. Ananchaipattana, and M. L. Bari (2014). Low-cost sustainable technologies for the production of clean drinking water—a review. Int. J. Photoenergy 5, 42–53.Google Scholar
- 30.H. M. Yadav, S. V. Otari, V. B. Koli, S. S. Mali, C. K. Hong, S. H. Pawar, and S. D. Delekar (2014). Preparation and characterization of copper-doped anatase TiO2 nanoparticles with visible light photocatalytic antibacterial activity. J. Photochem. Photobiol. A Chem. 280, 32–38.CrossRefGoogle Scholar
- 33.J. A. Rengifo-Herrera, K. Pierzchała, A. Sienkiewicz, L. Forró, J. Kiwi, and C. Pulgarin (2009). Abatement of organics and Escherichia coli by N, S co-doped TiO2 under UV and Visible light. Implications of the formation of singlet oxygen (1O2) under visible light. Appl. Catal. B Environ. 88, 398–406.CrossRefGoogle Scholar
- 34.J. A. Rengifo-Herrera, J. Kiwi, and C. Pulgarin (2009). N, S co-doped and N-doped Degussa P-25 powders with visible light response prepared by mechanical mixing of thiourea and urea. Reactivity towards E. coli inactivation and phenol oxidation. J. Photochem. Photobiol. A Chem. 205, 109–115.CrossRefGoogle Scholar
- 45.B. D. Cullity and S. R. Stock Elements of X-Ray Diffraction, 3rd ed (Prentice-Hall, Upper Saddle River, 2001).Google Scholar
- 57.W. R. Li, X. B. Xie, Q. S. Shi, H. Y. Zeng, Y. S. Ou-Yang, and Y. B. Chen (2009). Antibacterial activity and mechanism of silver NPs on Escherichia coli. J. Appl. Microbiol. Biotechnol. 58, 1115–1122.Google Scholar