Developments in injectable multiphasic biomaterials. The performance of microporous biphasic calcium phosphate granules and hydrogels

  • G. DaculsiEmail author
  • A. P. Uzel
  • P. Weiss
  • E. Goyenvalle
  • E. Aguado


Calcium phosphate bioceramic granules associated with hydrosoluble polymers were developed as bone substitutes for various maxillofacial and orthopaedic applications. These injectable bone substitutes, support and regenerate bone tissue and resorb after implantation. The efficiency of these multiphasic materials is due to the osteogenic and osteoconductive properties of the microporous biphasic calcium phosphate. The associated hydrosoluble polymers are considered as carriers in order to achieve the rheological properties of injectable bone substitutes (IBS). In this study, we used 2 semi synthetic hydrosoluble polymers of polysaccharidic origin. The hydroxy propyl methyl cellulose (HPMC), with and without silane, was combined with microporous BCP granules. The presence of silane induced considerable gelation of the suspension. The 2 IBS used (without gelation, IBS1, with gelation, IBS2) were implanted in critical size femoral epiphysis defects in rabbits. No foreign body reactions were observed in either sample. However, because of the higher density from gelation, cell colonisation followed by bone tissue ingrowth was delayed over time with IBS2 compared to the IBS1 without gelation. The results showed resorption of the BCP granule and bone ingrowth at the expense of both IBS with different kinetics. This study demonstrates that the hydrogel cannot be considered merely as a carrier. The gelation process delayed cell and tissue colonisation by slow degradation of the HPMC Si, compared to the faster release of HPMC with IBS1, in turn inducing faster permeability and spaces for tissue ingrowth between the BCP granules.


Calcium Phosphate Calcium Phosphate Cement Bone Ingrowth Biphasic Calcium Phosphate Regenerate Bone Tissue 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.



This study was supported by ANR (RNTS 2002 and BioRimp). The authors would like to thank Dr T. Lefrançois of CIRAD INRA Antilles for his help with the animal experiments. They would also like to thank Kirsty Snaith (Médicis Traduction) for reading and revising the English of the manuscript.


  1. 1.
    Heary RF, Schlenk RP, Sacchieri TA, Barone D, Brotea C. Persistent iliac crest donor site pain: independent outcome assessment. Neurosurgery. 2002;50:510–6.CrossRefPubMedGoogle Scholar
  2. 2.
    Silber JS, Anderson DG, DaVner SD, Brislin BT, Leland JM, Hilibrand AS, et al. Donor site morbidity after anterior iliac crest bone harvest for single-level anterior cervical discectomy and fusion. Spine. 2003;28:134–9.CrossRefPubMedGoogle Scholar
  3. 3.
    Tomford WW. Bone allografts: past, present and future. Cell Tissue Bank. 2000;1:105–9.CrossRefPubMedGoogle Scholar
  4. 4.
    Daculsi G, LeGeros RZ, Nery E, Lynch K, Kerebel B. Transformation of biphasic calcium phosphate ceramics: ultrastructural and physico-chemical characterization. J Biomed Mater Res. 1989;23:883–94.CrossRefPubMedGoogle Scholar
  5. 5.
    Daculsi G, LeGeros RZ, Heugheaert M, Barbieux I. Formation of carbonate apatite apatite crystals after implantation of calcium phosphate ceramics. Calcif Tissue Int. 1990;46:20–7.CrossRefPubMedGoogle Scholar
  6. 6.
    Daculsi G, Baroth S, LeGeros R. 20 years of biphasic calcium phosphate bioceramics development and applications ICACC’09—January 18–23, 2009; Daytona Beach, FL, USA. J Am Ceram Soc (in press).Google Scholar
  7. 7.
    Daculsi G. Biphasic calcium phosphate granules concept for injectable and mouldable bone substitute. Adv Sci Technol. 2006;49:9–13.CrossRefGoogle Scholar
  8. 8.
    Daculsi G, Weiss P, Bouler JM, Gauthier O. Aguado E Bcp/hpmc composite: a new concept for bone and dental substitution biomaterials. Bone. 1999;25:59–61.CrossRefGoogle Scholar
  9. 9.
    Daculsi G, Khairoun I, LeGeros RZ, Moreau F, Pilet P, Bourges X, et al. Bone ingrowth at the expense of a novel macroporous calcium phophate cement. Key Eng Mater. 2007;330/332:811–4.CrossRefGoogle Scholar
  10. 10.
    Lapkowski M, Weiss P, Daculsi G, Dupraz A. International patent WO 97/05911. 1997.Google Scholar
  11. 11.
    Weiss P, Vinatier C, Guicheux J, Grimandi G, Daculsi G. A self setting hydrogel as an extracellular synthetic matrix for tissue engineering. Key Eng Mater. 2004;254–256:1107–10.CrossRefGoogle Scholar
  12. 12.
    Weiss P, Gauthier O, Bouler JM, Grimandi G, Daculsi G. Injectable bone substitute using a hydrophilic polymer. Bone. 1999;25(2 Suppl):67S–70S.CrossRefPubMedGoogle Scholar
  13. 13.
    Turczyn R, Weiss P, Lapkowski M, Daculsi G. In situ self hardening bioactive composite for bone and dental surgery. J Biomater Sci Polym Ed. 2000;11:217–23.CrossRefPubMedGoogle Scholar
  14. 14.
    Bourges X, Weiss P, Coudreuse A, Daculsi G, Legeay G. General properties of silated hydroxyethylcellulose for potential biomedical applications. Biopolymers. 2002;63:232–8.CrossRefPubMedGoogle Scholar
  15. 15.
    Bourges X, Weiss P, Daculsi G, Legeay G. Synthesis and general properties of silated-hydroxypropyl methylcellulose in prospect of biomedical use. Adv Colloid Interface Sci. 2002;99:215–28.CrossRefPubMedGoogle Scholar
  16. 16.
    Fatimi A, Tassin JF, Quillard S, Axelos MAV, Weiss P. The rheological properties of silated hydroxypropylmethylcellulose tissue engineering matrices. Biomaterials. 2008;29:533–43.CrossRefPubMedGoogle Scholar
  17. 17.
    Stankewich CJ, Swionthowski MF, Tencer AF. Augmentation of femoral neck fracture fixation with an injectable calcium phosphate bone mineral cement J. Ortho Res. 1996;4:786–93.CrossRefGoogle Scholar
  18. 18.
    Ishikawa K. Calcium phosphate bone cement. In: Kokubo T, editor. Bioceramics and their clinical applications. Boca Raton, FL: Woodhead Publishing in Materials; 2008. p. 438–63.Google Scholar
  19. 19.
    Mahaguna V, TalbergR L, Peters JL, Adams S, Reynolds TD, Lam FY, et al. Influence of hydroxypropyl methyl cellulose polymer on in vitro and in vivo performance of controlled release tablets containing alprazolam. Eur J Pharm Biopharm. 2003;56:461–8.CrossRefPubMedGoogle Scholar
  20. 20.
    Dick HB, Augustin AJ, Pfeiffer N. Osmolarity of various viscoelastic substances: comparative study. J Cataract Refract Surg. 2000;26:1242–6.CrossRefPubMedGoogle Scholar
  21. 21.
    Fatimi A, Axelos AV, Tassin JF, Weiss P. Rheological characterization of self hardening hydrogel for tissue engineering applications: gel point determination and viscoelastic properties. Macromol Symp. 2008;266:12–6.CrossRefGoogle Scholar
  22. 22.
    Takebayashi T. Acute inhalation toxicity of high concentrations of silane in male ICR mice. Arch Toxic. 1993;67:55–60.CrossRefGoogle Scholar
  23. 23.
    Fujita H, Ido K, Matsuda Y, Lida H, Oka M, Kitamura Y, et al. Evaluation of bioactive bone cement in canine total hip arthroplasty. J Biomed Mater Res A. 1999;49:273–88.CrossRefGoogle Scholar
  24. 24.
    Borhane HF, Weiss P, Gauthier O, Rouillon T, Pilet P, Daculsi G, et al. Bone repair using a new injectable self crosslinkable bone substitute. J Orthop Res. 2006;24:628–35.CrossRefGoogle Scholar
  25. 25.
    Daculsi G, Rohanizadeh R, Weiss P, Bouler JM. Crystal polymer interaction with new injectable bone substitute; SEM and Hr TEM study. J Biomed Mater Res. 2000;50(1):1–7.CrossRefPubMedGoogle Scholar
  26. 26.
    Le Guehennec L, Layrolle P, Daculsi G. A review of bioceramics and fibrin sealant. Eur Cell Mater. 2004;8:1–11.PubMedGoogle Scholar
  27. 27.
    Bourges X. Patent WO 2008/059 058, Hydrogel and biomedical applications there.Google Scholar
  28. 28.
    Daculsi G, Bourges X, Goyenvalle E, Aguado E, Borget P. In vivo setting time effect on resorption and tissue ingrowth at the expense of Calcium Phosphate Cement (MCPC®). Key Eng. 2009, in press.Google Scholar
  29. 29.
    Daculsi G, Uzel PA, Bourgeois N, Le François T, Rouvillain JL, Bourges X, Baroth S. New injectable bone substitute using reversible thermosensitive hydrogel and BCP granules: in vivo rabbit experiments. Key Eng Mater. 2009;396–398:457–60.CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2009

Authors and Affiliations

  • G. Daculsi
    • 1
    • 2
    Email author
  • A. P. Uzel
    • 3
    • 4
  • P. Weiss
    • 1
  • E. Goyenvalle
    • 5
    • 6
  • E. Aguado
    • 5
    • 6
  1. 1.INSERM, U791, University of Nantes, Osteoarticular and dental tissue engineeringNantesFrance
  2. 2.CIC-IT INSERM, Hôpitaux de Bordeaux, Hôpital Xavier ArnozanPessacFrance
  3. 3.ERT 2004, Université de Nantes, Dental facultyNantesFrance
  4. 4.Service d’orthopédie-traumatologiePointe-à-PitreFrance
  5. 5.INSERM, EMI 0335, University of Angers, Faculty of Medicine, Remodelage osseux et BiomatériauxAngersFrance
  6. 6.Ecole Nationale Vétérinaire de Nantes, Service de chirurgie LBBTO exNantesFrance

Personalised recommendations