Effects of graphene quantum dots coating on the luminescence properties of K2SiF6:Mn4+ red-emitting phosphors

  • Youmiao Liu
  • Yuelan Li
  • Yutong Feng
  • Jianming Meng
  • Sen LiaoEmail author
  • Yingheng Huang
  • Huaxin Zhang
Article
  • 5 Downloads

Abstract

A series of K2SiF6:0.06Mn4+@ GQDs y mg/mol (KSF: K2SiF6, GQDs: graphene quantum dots) red-emitting phosphors were prepared with a simple coating method. Experimental results show that the KSF:0.06Mn4+@ GQDs y mg/mol has broad excitation bands in blue region and strong emission line bands in red region with the strongest peak at ~ 630 nm. Enhanced luminescence intensity and thermal stability induced by GQD coating are observed: (i) the integrated intensity of KSF:0.06Mn4+@ GQDs 5mg/mol is 1.32 times of that of KSF:0.06Mn4+, (ii) the integrated intensities of KSF:0.06Mn4+@ GQDs 5mg/mol at 120 and 180 °C are 1.57 and 1.26 times of that at 25 °C. Through temperature-dependent behavior measurement and stability test, it can distinctly learn that KSF:0.06Mn4+@GQDs 5 mg/mol exhibits exceptional thermal stability as well as color stability under LED-operating temperature conditions, which implies that the sample has potential applications for blue light-based warm W-LEDs.

Notes

Acknowledgements

This research is supported by the National Natural Science Foundation of China (Grant No. 21561003, No. 21661006 and No. 21965004), the Scientific Research Foundation of Guangxi University (Grant No. XDZ140116), the open foundation of Guangxi Key Laboratory of Processing for Non-ferrous Metals and Featured Materials, Guangxi University (Grant No. 2019GXYSOF03), the innovation Project of Guangxi Graduate Education (Grant No. YCSW2019031), the Students Experimental Skills and Innovation Ability Training Fund Project of Guangxi University (No. 201710593183 and No. 201910593177).

Compliance with ethical standards

Conflict of interest

The authors declare that they have no conflict of interest.

References

  1. 1.
    D.C. Huang, H.M. Zhu, Z.H. Deng, Q.L. Zou, H.Y. Lu, X.D. Yi, W. Guo, C.Z. Lu, X.Y. Chen, Angew. Chem. Int. Ed. 58, 3843 (2019)CrossRefGoogle Scholar
  2. 2.
    U. Bin Humayoun, S. Bin Kwon, S.K. Sami, D.H. Yoon, J. Alloys Compd. 776, 594 (2019)CrossRefGoogle Scholar
  3. 3.
    Y.M. Liu, T.M. Wang, Z.R. Tan, J.M. Meng, W.J. Huang, Y.H. Huang, S. Liao, H.X. Zhang, Ceram. Int. 45, 6243 (2019)CrossRefGoogle Scholar
  4. 4.
    T. Senden, R.J.A. van Dijk-Moes, A. Meijerink, Light-Sci. Appl. 7, 8 (2018)CrossRefGoogle Scholar
  5. 5.
    L. Huang, Y. Liu, J.B. Yu, Y.W. Zhu, F.J. Pan, T.T. Xuan, M.G. Brik, C.X. Wang, J. Wang, A.C.S. Appl, Mater. Inter. 10, 18082 (2018)CrossRefGoogle Scholar
  6. 6.
    R. Verstraete, H.F. Sijbom, J.J. Joos, K. Korthout, D. Poelman, C. Detavernier, P.F. Smet, A.C.S. Appl, Mater. Inter. 10, 18845 (2018)CrossRefGoogle Scholar
  7. 7.
    L. Huang, Y. Liu, S.C. Si, M.G. Brik, C.X. Wang, J. Wang, Chem. Commun. 54, 11857 (2018)CrossRefGoogle Scholar
  8. 8.
    Y.M. Liu, T.M. Wang, Z.P. Chen, K.Y. Chen, M.M. Guan, Y.H. Huang, S. Liao, H.X. Zhang, J. Mater. Sci. Mater. Electron. 29, 12536 (2018)CrossRefGoogle Scholar
  9. 9.
    T.M. Wang, Y. Gao, Z.P. Chen, Q.Y. Huang, B.L. Song, Y.H. Huang, S. Liao, H.X. Zhang, J. Mater. Sci. Mater. Electron. 28, 11878 (2017)CrossRefGoogle Scholar
  10. 10.
    F. Tang, Z.C. Su, H.G. Ye, W.P. Gao, X.Q. Pan, S.J. Xu, ACS Omega 3, 13704 (2018)CrossRefGoogle Scholar
  11. 11.
    E.H. Song, J.Q. Wang, J.H. Shi, T.T. Deng, S. Ye, M.Y. Peng, J. Wang, L. Wondraczek, Q.Y. Zhang, ACS Appl. Mater. Interfaces. 9, 8805 (2017)CrossRefGoogle Scholar
  12. 12.
    E.H. Song, J.Q. Wang, S. Ye, X.F. Jiang, M.Y. Peng, Q.Y. Zhang, J. Mater. Chem. C 4, 2480 (2016)CrossRefGoogle Scholar
  13. 13.
    L. Huang, Y.W. Zhu, X.J. Zhang, R. Zou, F.J. Pan, J. Wang, M.M. Wu, Chem. Mater. 28, 1495 (2016)CrossRefGoogle Scholar
  14. 14.
    T.T. Deng, E.H. Song, Y.Y. Zhou, L.Y. Wang, Q.Y. Zhang, J. Mater. Chem. C 5, 12422 (2017)CrossRefGoogle Scholar
  15. 15.
    E.J. Llorent-Martinez, G.M. Duran, A. Rios, A. Ruiz-Medina, Anal. Bioanal. Chem. 410, 391 (2018)CrossRefGoogle Scholar
  16. 16.
    G. Anoop, J.R. Rani, J. Lim, M.S. Jang, D.W. Suh, S. Kang, S.C. Jun, J.S. Yoo, Sci. Rep. 6, 33993 (2016)CrossRefGoogle Scholar
  17. 17.
    X.X. Zhang, W.J. Zhang, Y.J. Li, C.L. Li, Dyes Pigments 140, 150 (2017)CrossRefGoogle Scholar
  18. 18.
    W.J. Zhang, X.F. Zou, J.F. Zhao, J. Mater. Chem. C 3, 1294 (2015)CrossRefGoogle Scholar
  19. 19.
    Z.Y. Hou, X.Y. Tang, X.F. Luo, T.L. Zhou, L. Zhang, R.J. Xie, J. Mater. Chem. C 6, 2741 (2018)CrossRefGoogle Scholar
  20. 20.
    M. Novita, T. Honma, B. Hong, A. Ohishi, K. Ogasawara, J. Lumin. 169, 594 (2016)CrossRefGoogle Scholar
  21. 21.
    C.Y. Jiang, M.G. Brik, L.H. Li, L.Y. Li, J. Peng, J.N. Wu, M.S. Molokeev, K.L. Wong, M.Y. Peng, J. Mater. Chem. C 6, 3016 (2018)CrossRefGoogle Scholar
  22. 22.
    L.Y. Wang, E.H. Song, Y.Y. Zhou, T.T. Deng, S. Ye, Q.Y. Zhang, J. Mater. Chem. C 6, 8670 (2018)CrossRefGoogle Scholar
  23. 23.
    T.T. Deng, E.H. Song, J. Su, Y.Y. Zhou, L.Y. Wang, S. Ye, Q.Y. Zhang, J. Mater. Chem. C 6, 4418 (2018)CrossRefGoogle Scholar
  24. 24.
    Y.L. He, J.L. He, H.R. Zhang, Y.L. Liu, B.F. Lei, J. Colloid Interface Sci. 496, 8 (2017)CrossRefGoogle Scholar
  25. 25.
    W. Li, H.R. Zhang, S. Chen, Y.L. Liu, J.L. Zhuang, B.F. Lei, Adv. Opt. Mater. 4, 427 (2016)CrossRefGoogle Scholar
  26. 26.
    M.M. Zhu, Y.X. Pan, L.Q. Xi, H.Z. Lian, J. Lin, J. Mater. Chem. C 5, 10241 (2017)CrossRefGoogle Scholar
  27. 27.
    L.Y. Wang, E.H. Song, Y.Y. Zhou, T.T. Deng, S. Ye, Q.Y. Zhang, J. Mater. Chem. C 5, 7253 (2017)CrossRefGoogle Scholar
  28. 28.
    L.L. Wei, C.C. Lin, M.H. Fang, M.G. Brik, S.F. Hu, H. Jiao, R.S. Liu, J. Mater. Chem. C 3, 1655 (2015)CrossRefGoogle Scholar
  29. 29.
    M.G. Brik, S.J. Camardello, A.M. Srivastava, N.M. Avram, A. Suchocki, ECS J. Solid State Sci. 5, R3067 (2016)CrossRefGoogle Scholar
  30. 30.
    M.G. Brik, S.J. Camardello, A.M. Srivastava, ECS J. Solid State Sci. 4, R39 (2015)CrossRefGoogle Scholar
  31. 31.
    M.G. Brik, A.M. Srivastava, ECS J. Solid State Sci. 2, R148 (2013)CrossRefGoogle Scholar
  32. 32.
    Z.Z. Lu, A.J. Fu, F.F. Gao, X.S. Zhang, L.Y. Zhou, J. Lumin. 203, 420 (2018)CrossRefGoogle Scholar
  33. 33.
    M. Gu, Y. Tian, C.E. Cui, P. Huang, L. Wang, Q.F. Shi, Mater. Res. Bull. 107, 242 (2018)CrossRefGoogle Scholar
  34. 34.
    M.M. Zhu, Y.X. Pan, X. Chen, H.Z. Lian, J. Lin, J. Am. Ceram. Soc. 101, 4983 (2018)CrossRefGoogle Scholar
  35. 35.
    Q.Y. Shao, L. Wang, L. Song, Y. Dong, C. Liang, J.H. He, J.Q. Jiang, J. Alloys Compd. 695, 221 (2018)CrossRefGoogle Scholar
  36. 36.
    H.F. Sijbom, J.J. Joos, L.I.D.J. Martin, K. Van den Eeckhout, D. Poelman, P.F. Smet, ECS J. Solid State Sc. 5, R3040 (2016)Google Scholar
  37. 37.
    Y.W. Zhu, L.Y. Cao, M.G. Brik, X.J. Zhang, L. Huang, T.T. Xuan, J. Wang, J. Mater. Chem. C 5, 6420 (2017)CrossRefGoogle Scholar
  38. 38.
    H. Chen, H. Lin, Q.M. Huang, F. Huang, J. Xu, B. Wang, Z.B. Lin, J.C. Zhou, Y.S. Wang, J. Mater. Chem. C 4, 2374 (2016)CrossRefGoogle Scholar
  39. 39.
    L.Y. Wang, E.H. Song, T.T. Deng, Y.Y. Zhou, Z.F. Liao, W.R. Zhao, B. Zhou, Q.Y. Zhang, Dalton Trans. 5, 9925 (2017)CrossRefGoogle Scholar
  40. 40.
    Y.W. Zhu, L. Huang, R. Zou, J.H. Zhang, J.B. Yu, M.M. Wu, J. Wang, Q. Sua, J. Mater. Chem. C 4, 5690 (2016)CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  1. 1.School of Chemistry and Chemical EngineeringGuangxi UniversityNanningChina
  2. 2.Guangxi Key Laboratory of Processing for Non-ferrous Metals and Featured Materials, School of Resources, Environment and MaterialsGuangxi UniversityNanningChina

Personalised recommendations