A facile method combined with catalyst solution printing and electroless plating to fabricate selective metal coating on inert polymer

  • Guangchao Qin
  • Yu Zhang
  • Manman Yuan
  • Rui Chen
  • Youhao Liu
  • Junjun HuangEmail author
Article
  • 10 Downloads

Abstract

It is highly desired to simplify the technology of electroless plating on inert polymer. Herein we developed a new kind of catalytic solution (mixture of H2O, AgNO3 and 3-aminopropyltriethoxysilane), which can write onto inert polymer directly with good stability, resolution and catalytic performance. Then, a facile method combined with catalyst solution printing and electroless plating to fabricate selective metal (copper and nickel) coating on polymer (polypropylene and polyethylene terephthalate) surface. The growth behavior, electrical, and structural properties of plated coating were investigated. The minimum width of copper coating is 250 μm, thickness is 2.2 μm, resistivity is 2.6 × 10−6 Ω cm, adhesion of 2.2 μm thick coating maintain 5B. In addition, the selective metal coating have excellent bending and fatigue resistance.

Notes

Acknowledgement

The authors thank the financial supports by the Research Foundation of Hefei University (No: 17ZR03ZDA), the State Key Laboratory of Rare Earth Permanent Magnetic Materials (No: SKLREPM17OF05) and the Opening project of Guangxi Key Laboratory of Calcium Carbonate Resources Comprehensive Utilization (HZXYKFKT201805).

References

  1. 1.
    X. Zhao, F. Muench, S. Schaefer et al., Electroless decoration of macroscale foam with nickel nano-spikes: a scalable route toward efficient catalyst electrodes. Electrochem. Commun. 65, 39–43 (2016)CrossRefGoogle Scholar
  2. 2.
    J.U. Yang, J.H. Cho, M.J. Yoo, Selective metallization on copper aluminate composite via laser direct structuring technology. Compos. Part B 110, 361–367 (2017)CrossRefGoogle Scholar
  3. 3.
    X. Li, G. Wang, X. Wang et al., Flexible supercapacitor based on MnO2 nanoparticlesvia electrospinning. Mater. Chem. A 1(35), 10103–10106 (2013)CrossRefGoogle Scholar
  4. 4.
    X. Sun, L. Zhang, S. Tao, S. Li, A general surface swelling-induced electroless deposition strategy for fast fabrication of copper circuits on various polymer substrates. Adv. Mater. Interfaces 4, 1700052 (2017)CrossRefGoogle Scholar
  5. 5.
    T. Zhang, X. Wang, T. Li, Q. Guo, T. Yang, Fabrication of flexible copper-based electronics with high-resolution and high-conductivity on paper via inkjet printing. J. Mater. Chem. C 2(2), 286–294 (2014)CrossRefGoogle Scholar
  6. 6.
    Y. Wang, Y. Wang, J.J. Chen et al., A facile process combined with inkjet printing, surface modification and electroless deposition to fabricate adhesion-enhanced copper patterns on flexible polymer substrates for functional flexible electronics. Electrochim. Acta 218, 24–31 (2016)CrossRefGoogle Scholar
  7. 7.
    Y. Chang, Y. Tao, Q. Zhang, Z.G. Yang, Selective adsorption of catalyst and copper plating for additive fabrication of conductive patterns and through-holes. Electrochim. Acta 158, 7–12 (2015)CrossRefGoogle Scholar
  8. 8.
    D. Chen, Y. Zhang, T. Bessho, Layer by layer electroless deposition: an efficient route for preparing adhesion-enhanced metallic coatings on plastic surfaces. Chem. Eng. J. 303, 100–108 (2016)CrossRefGoogle Scholar
  9. 9.
    J.J. Huang, C.A. Tian, J. Wang et al., Fabrication of selective electroless copper plating on PET sheet: effect of PET surface structure on resolution and adhesion of copper coating. Appl. Surf. Sci. 458, 734–742 (2018)CrossRefGoogle Scholar
  10. 10.
    Z.P. Sun, J.J. Huang, L.B. Wang et al., Method for electroless nickel plating on poly(ethylene terephthalate) substrate modified with primer and self-assembled monolayer. J. Mater. Sci. 26, 10132–10137 (2015)Google Scholar
  11. 11.
    J.J. Huang, Z.M. Chen, F. Zhou et al., High-adhesive electroless copper plating on polyethylene surface modified with primer. J. Solid State Electrochem. 21, 1559–1566 (2017)CrossRefGoogle Scholar
  12. 12.
    A. Hashemi, A. Bahari, S. Ghasemi, Reduction the leakage current through povidone-SiO2 nano-composite as a promising gate dielectric of FETs. J. Mater. Sci. 28(18), 13313–13319 (2017)Google Scholar
  13. 13.
    L.X. Yi, J. Heitmann, R. Scholz, M. Zacharias, Si rings, Si clusters, and Si nanocrystals-different states of ultrathin SiOx, layers. Appl. Phys. Lett. 81(22), 4248–4250 (2002)CrossRefGoogle Scholar
  14. 14.
    X. Wang, H. Hu, Y. Shen et al., Stretchable conductors with ultrahigh tensile strain and stable metallic conductance enabled by prestrained polyelectrolyte nanoplatforms. Adv. Mater. 23(27), 3090 (2011)CrossRefGoogle Scholar
  15. 15.
    Z. Chen, X. Xu, C.C. Wong, S. Mhaisalkar, Effect of plating parameters on the intrinsic stress in electroless nickel plating. Surf. Coat Technol. 167(2–3), 170–176 (2003)CrossRefGoogle Scholar
  16. 16.
    Y. Lu, S. Sathasivam, J. Song et al., Robust self-cleaning surfaces that function when exposed to either air or oil. Science 347(6226), 1132–1135 (2015)CrossRefGoogle Scholar
  17. 17.
    M. Baloch, C.M. López, Effect of additives on the pulsed-galvanostatic electrodeposition of iron nanoparticles from formamide media. ChemElectroChem 3(6), 883–886 (2016)CrossRefGoogle Scholar
  18. 18.
    Y.J. Yim, K.Y. Rhee, S.J. Park, Influence of electroless nickel-plating on fracture toughness of pitch-based carbon fibre reinforced composites. Compos. Part B 76, 286–291 (2015)CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  1. 1.Department of Chemical and Materials EngineeringHefei UniversityHefeiChina
  2. 2.State Key Laboratory of the Rare Earth Permanent Magnetic MaterialsEarth-Panda Advance Magnetic Material Co., LtdHefeiChina
  3. 3.Guangxi Key Laboratory of Calcium Carbonate Resources Comprehensive Utilization, College of Materials & Environmental EngineeringHezhou UniversityHezhouChina

Personalised recommendations