Solution-processed ZnO thin-film transistors codoped with Na and F
- 102 Downloads
Na and F codoping was utilized to realize high-performance ZnO thin-film transistors derived from sol–gel solution process. The effect of NaF doping concentration on the electrical properties of ZnO thin-film transistors annealed at 350 °C was investigated. Films with 10 at.% doping exhibited excellent performance with an average mobility of 70.98 cm2 V−1 s−1 and a high Ion/Ioff ratio on the order of 106. The X-ray photon spectroscopy exhibited oxygen bound with oxide lattice with and without vacancy related peak position shifted towards lower energy side when doped at 10 at.% and did not show the hydroxyl group on the NaF doped ZnO surface which indicates the improved performance of the thin-film transistors devices. The electrical performance of the devices also changed considerably as the thickness of the NaF-doped ZnO layer increased. Increasing the grain size and realizing a smooth surface morphology by varying the NaF concentration were found to enhance the thin-film transistors mobility.
This work was supported by International Collaborative Research and Development Program funded by the Ministry of Trade, Industry and Energy (MOTIE, Republic of Korea) (N0002626). This work was also supported by the Korea Institute of Energy Technology Evaluation and Planning (KETEP) and the Ministry of Trade, Industry & Energy (MOTIE) of the Republic of Korea (No. 20174010201490). This research was also supported by the 2018 KU Brain Pool of Konkuk University.
- 5.S. Wang, V. Mirkhani, K. Yapabandara, R. Cheng, G. Hernandez, M.P. Khana, M.S. Sultan, S. Uprety, L. Shen, S. Zou, P. Xu, C.D. Ellis, J.A. Sellers, M.C. Hamilton, G. Niu, M.H. Sk, M. Park, Electrical characteristics and density of states of thin-film transistors based on sol-gel derived ZnO channel layers with different annealing temperatures. J. Appl. Phys. 123, 161503 (2018)CrossRefGoogle Scholar
- 17.K. Kim, S.Y. Park, K.H. Lim, C.H. Shin, J.M. Myung, Y.S. Kim, Low temperature and solution-processed Na-doped zinc oxide transparent thin film transistors with reliable electrical performance using methanol developing and surface engineering. J. Mater. Chem. 22, 23120–23128 (2012)CrossRefGoogle Scholar
- 28.J. Chang, Z. Lin, M. Lin, C. Zhu, J. Zgang, J. Wu, Solution processed F doped ZnO (ZnO:F) for thin film transistors and improved stability through co-doping with alkali metals. J. Mater. Chem. C 3, 1787–1793Google Scholar