Facile fabrication of In:Ge/Cu nano-octahedra film for improving photoelectrochemical properties

  • Yuan-chun Yu
  • Yuling Liang
  • Fuqiao Liu
  • Pei-hui Yang
Article
  • 20 Downloads

Abstract

The novel In:Ge/Cu nano-octahedra photoelectric film, a kind of metal-semiconductor-metal (MSM) like structures, was prepared from by a facile two-step electrodeposition process, which In:Ge and Cu nano-octahedra were successively deposited on the indium tin oxide (ITO) substrates from aqueous solution. With the modification of Cu nano-octahedral, the photoresponse and photoactive current of the In:Ge films has significantly improved 88 flods under illuminations (wavelength range: 365, 532 and 805 nm). Notably, the In:Ge/Cu nano-octahedra films exhibit excellent photoelectrochemical properties in wide wavelength range from the UV to near-infrared. This novel photoelectric film shows great potential applications in optoelectronic devices and photodetectors, and the facilely synthesis route can provide an enlightening insight for the fabrication of photoelectric devices and high-performance energy conversion systems.

Notes

Acknowledgements

The authors gratefully acknowledge the Science Fund from the National Natural Science Foundation of China (No. 21375048).

Supplementary material

10854_2018_8881_MOESM1_ESM.doc (131.3 mb)
Supplementary material 1 (DOC 134433 KB)

References

  1. 1.
    P.T.A. Shah, R. Tscharner, N. Wyrsch, H. Keppner, Science 285, 692 (1999)CrossRefGoogle Scholar
  2. 2.
    D. Carolan, Prog. Mater Sci. 90, 128–158 (2017)CrossRefGoogle Scholar
  3. 3.
    Y.M. Niquet, G. Allan, C. Delerue, M. Lannoo, Appl. Phys. Lett. 77, 1182–1184 (2000)CrossRefGoogle Scholar
  4. 4.
    C. Bostedt, T. van Buuren, T.M. Willey, N. Franco, L.J. Terminello, C. Heske, T. Moller, Appl. Phys. Lett. 84, 4056–4058 (2004)CrossRefGoogle Scholar
  5. 5.
    M.S. Song, J.H. Jung, Y. Kim, Y. Wang, J. Zou, H.J. Joyce, Q. Gao, H.H. Tan, C. Jagadish, Nanotechnology 19, 125602 (2008)CrossRefGoogle Scholar
  6. 6.
    C.-Y. Chou, G.S. Hwang, J. Power Sources 263, 252–258 (2014)CrossRefGoogle Scholar
  7. 7.
    S. Averine, Y.C. Chan, Y.L. Lam, Appl. Phys. Lett. 77(2), 274–276 (2000)CrossRefGoogle Scholar
  8. 8.
    F.F. Ren, K.W. Ang, J. Ye, M. Yu, G.Q. Lo, D.L. Kwong, Nano Lett. 11, 1289–1293 (2011)CrossRefGoogle Scholar
  9. 9.
    M.E. Toimil-Molares, E.M. Hohberger, C. Schaeflein, R.H. Blick, R. Neumann, C. Trautmann, Appl. Phys. Lett. 82, 2139–2141 (2003)CrossRefGoogle Scholar
  10. 10.
    R. Rosenberg, D.C. Edelstein, C.K. Hu, K.P. Rodbell, Annu. Rev. Mater. Sci. 30, 229–262 (2000)CrossRefGoogle Scholar
  11. 11.
    T.M. Mattox, X. Ye, K. Manthiram et al., Adv. Mater. 27(38), 5830 (2015)CrossRefGoogle Scholar
  12. 12.
    S.G. Hickey, C. Waurisch, B. Rellinghaus, A. Eychmueller, JACS 130, 14978–14980 (2008)CrossRefGoogle Scholar
  13. 13.
    G.H. Shih, C.G. Allen, B.G. Potter Jr. Nanotechnology 23(7), 075203 (2012)CrossRefGoogle Scholar
  14. 14.
    D.-J. Xue, J.-J. Wang, Y.-Q. Wang, S. Xin, Y.-G. Guo, L.-J. Wan, Adv. Mater. 23, 3704–3707 (2011)CrossRefGoogle Scholar
  15. 15.
    L. Cao, J.S. Park, P. Fan, B. Clemens, M.L. Brongersma, Nano Lett. 10, 1229–1233 (2010)CrossRefGoogle Scholar
  16. 16.
    M.J. Jawad, M.R. Hashim, N.K. Ali, E.P. Corcoles, M.E. Sharifabad, J. Electrochem. Soc. 159, D124–D128 (2012)CrossRefGoogle Scholar
  17. 17.
    T. Burchhart, A. Lugstein, Y.J. Hyun, G. Hochleitner, E. Bertagnolli, Nano Lett. 9, 3739–3742 (2009)CrossRefGoogle Scholar
  18. 18.
    P. Lu, P. Yang. RSC Adv. 6(1), 601–606 (2015)CrossRefGoogle Scholar
  19. 19.
    N.K. Mahenderkar, Y.-C. Liu, J.A. Koza, J.A. Switzer, Acs Nano 8, 9524–9530 (2014)CrossRefGoogle Scholar
  20. 20.
    S.C. Tang, X.K. Meng, S. Vongehr, Electrochem. Commun. 11(4), 867–870 (2009)CrossRefGoogle Scholar
  21. 21.
    S. Devillers, Q. Lemineur, J. Delhalle, Z. Mekhalif, Electrochim. Acta 56, 4953–4959 (2011)CrossRefGoogle Scholar
  22. 22.
    J. Tu, Y. Yuan, H. Jiao, S. Jiao, RSC Adv. 4, 16380 (2014)CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2018

Authors and Affiliations

  1. 1.Department of ChemistryJinan UniversityGuangzhouChina

Personalised recommendations