Growth behavior of IMCs layer of the Sn–35Bi–1Ag on Cu, Ni–P/Cu and Ni–Co–P/Cu substrates during aging

  • Yulong Li
  • Zhiliang Wang
  • Xuewen Li
  • Xiaowu Hu
  • Min LeiEmail author
Article
  • 30 Downloads

Abstract

In this work, the interfacial reactions and IMC growth of the Sn–35Bi–1Ag on Cu, Ni–P/Cu and Ni–Co–P/Cu were studied during reflowing at 220 °C for 10 min and solid–state treatment at 150 °C with various aging times. For the solder joints of Sn–35Bi–1Ag/Cu, Cu6Sn5 IMC was formed at the interfacial layer after soldering, while Cu3Sn appeared after aging treatment. In the case of the electroless Ni–P plating of Cu, the IMC formed at the interface during isothermal aging was mainly Ni3Sn4 and a small amount of P-rich Ni (Ni3P) layer between the Ni3Sn4 IMC and the electroless Ni–P plating layer. In the case of the electroless Ni–Co–P plating of Cu, the IMC formed at the interface during isothermal aging was mainly (Ni, Co)3Sn4 and a small amount of P-rich Ni ((Ni, Co)3P) layer between (Ni, Co)3Sn4 IMC and the electroless Ni–Co–P plating layer. The addition of Co atoms could effectively inhibit the IMC growth rate, which inducing a lower growth rate of (Ni, Co)3Sn4 than that of Ni3Sn4. The thickness of Ni3P and (Ni, Co)3P layer reached about 2.31 µm and 1.25 µm after aging for 360 h, respectively. Also, the growth kinetics of the Ni3P and (Ni, Co)3P layer was found to be a diffusion–controlled process, which followed a parabolic relationship in the thickness increase. During the aging, the consumption of the electroless Ni–Co–P plating layer was greatly reduced compared with that of the electroless Ni–P plating layer. Moreover, there were no voids observed in the electroless Ni–Co–P plating layer while some defects formed in that of the electroless Ni–P plating layer. The electroless Ni–Co–P plating layer will be a good diffusion barrier for the lead-free soldering.

Notes

Acknowledgements

This work was sponsored by the National Natural Science Foundation of China (No. 51665038), Key Project of the Natural Science Foundation of Jiangxi Province (20171ACB21011), the Academic and Technical Leaders Founding Project of Major Disciplines of Jiangxi Province (2018), the Postgraduate Innovative Special Foundation of Nanchang University (CX2017057).

References

  1. 1.
    T.L. Yang, J.Y. Wu, C.C. Li, S. Yang, C.R. Kao, Low temperature bonding for high temperature applications by using SnBi solders. J. Alloys Compd. 647, 681–685 (2015)Google Scholar
  2. 2.
    Y.W. Wang, Y.W. Lin, C.R. Kao, Kirkendall voids formation in the reaction between Ni-doped SnAg lead-free solders and different Cu substrates. Microelectron. Reliab. 49(3), 248–252 (2009)Google Scholar
  3. 3.
    C.K. Chung, Y.J. Chen, C.C. Li, C.R. Kao, The critical oxide thickness for Pb-free reflow soldering on Cu substrate. Thin Solid Films 520(16), 5346–5352 (2012)Google Scholar
  4. 4.
    M.Y. Tsai, S.C. Yang, Y.W. Wang, C.R. Kao, Grain growth sequence of Cu3Sn in the Cu/Sn and Cu/Sn–Zn systems. J. Alloys Compd. 494(1–2), 123–127 (2010)Google Scholar
  5. 5.
    M.F.M. Nazeri, A.A. Mohamad, Effect of corrosion in alkaline solution to the microstructure and mechanical properties of Cu/Sn–9Zn/Cu. Proc. Chem. 19, 247–252 (2016)Google Scholar
  6. 6.
    J.C. Liu, G. Zhang, Z.H. Wang, J.S. Ma, K. Suganuma, Thermal property, wettability and interfacial characterization of novel Sn–Zn–Bi–In alloys as low-temperature lead-free solders. Mater. Des. 84, 331–339 (2015)Google Scholar
  7. 7.
    J. Shen, C. Wu, S. Li, Effects of rare earth additions on the microstructural evolution and microhardness of Sn30Bi0. 5Cu and Sn35Bi1Ag solder alloys. J. Mater. Sci.: Mater. Electron. 23(1), 156–163 (2012)Google Scholar
  8. 8.
    L. Zhang, L. Sun, Y.H. Guo, Microstructures and properties of Sn58Bi, Sn35Bi0. 3Ag, Sn35Bi1. 0Ag solder and solder joints. J. Mater. Sci.: Mater. Electron. 26(10), 7629–7634 (2015)Google Scholar
  9. 9.
    S. Amore, E. Ricci, G. Borzone, R. Novakovic, Wetting behaviour of lead-free Sn-based alloys on Cu and Ni substrates. Mater. Sci. Eng. A 495(1–2), 108–112 (2008)Google Scholar
  10. 10.
    S.W. Kim, J.W. Yoon, S.B. Jung, Interfacial reactions and shear strengths between Sn–Ag-based Pb-free solder balls and Au/EN/Cu metallization. J. Electron. Mater. 33(10), 1182–1189 (2004)Google Scholar
  11. 11.
    C.F. Tseng, C.J. Lee, J.G. Duh, Roles of Cu in Pb-free solders jointed with electroless Ni (P) plating. Mater. Sci. Eng. A 574, 60–67 (2013)Google Scholar
  12. 12.
    J.W. Yoon, S.B. Jung, Growth kinetics of Ni3Sn4 and Ni3P layer between Sn-3.5 Ag solder and electroless Ni–P substrate. J. Alloys Compd. 376(1–2), 105–110 (2004)Google Scholar
  13. 13.
    C.Y. Ho, J.G. Duh, C.W. Lin, C.J. Lin, Y.H. Wu, H.C. Hong, T.H. Wang, Microstructural variation and high-speed impact responses of Sn–3.0 Ag–0.5 Cu/ENEPIG solder joints with ultra-thin Ni–P deposit. J. Mater. Sci. 48(6), 2724–2732 (2013)Google Scholar
  14. 14.
    C.E. Ho, C.W. Fan, W.H. Wu, T.T. Kuo, Reliability evaluation on a submicron Ni (P) thin film for lead-free soldering. Thin Solid Films 529, 364–368 (2013)Google Scholar
  15. 15.
    Y.J. Hu, Y.C. Hsu, C.T. Lu, T.S. Huang, C.Y. Chen, W.N. Chuang, C.Y. Liu, Interfacial reactions between columnar or layered Ni (P) layers and Sn–Ag–Cu solder. J. Electron. Mater. 43(1), 277–283 (2014)Google Scholar
  16. 16.
    M.O. Alam, Y.C. Chan, K.C. Hung, Reliability study of the electroless Ni–P layer against solder alloy. Microelectron. Reliab. 42(7), 1065–1073 (2002)Google Scholar
  17. 17.
    M.O. Alam, Y.C. Chan, K.C. Hung, Interfacial reaction of Pb–Sn solder and Sn–Ag solder with electroless Ni deposit during reflow. J. Electron. Mater. 31(10), 1117–1121 (2002)Google Scholar
  18. 18.
    K. Zeng, K.N. Tu, Six cases of reliability study of Pb–free solder joints in electronic packaging technology. Mater. Sci. Eng. R 38(2), 55–105 (2002)Google Scholar
  19. 19.
    J.W. Yoon, C.B. Lee, S.B. Jung, Growth of an intermetallic compound layer with Sn–3.5 Ag–5Bi on Cu and Ni–P/Cu during aging treatment. J. Electron. Mater. 32(11), 1195–1202 (2003)Google Scholar
  20. 20.
    J.W. Jang, D.R. Frear, T.Y. Lee, K.N. Tu, Morphology of interfacial reaction between lead-free solders and electroless Ni–P under bump metallization. J. Appl. Phys. 88(11), 6359–6363 (2000)Google Scholar
  21. 21.
    T.S. Narayanan, S. Selvakumar, A. Stephen, Electroless Ni–Co–P ternary alloy deposits: preparation and characteristics. Surf Coat Technol. 172(2–3), 298–307 (2003)Google Scholar
  22. 22.
    Y. Liu, Q. Zhao, Study of electroless Ni–Cu–P coatings and their anti-corrosion properties. Appl. Surf. Sci. 228(1–4), 57–62 (2004)Google Scholar
  23. 23.
    Z. Bangwei, H. Wangyu, Z. Qinglong, Q. Xuanyuan, Properties of electroless Ni–WP amorphous alloys. Mater. Charact. 37(2–3), 119–122 (1996)Google Scholar
  24. 24.
    R.L. Melo, P.N. Casciano, A.N. Correia, P.D. Lima-Neto, Characterisation of electrodeposited and heat-treated Ni–Mo–P coatings. J. Braz. Chem. Soc. 23(2), 328–334 (2012)Google Scholar
  25. 25.
    A. Kumar, A. Singh, M. Kumar, D. Kumar, S. Barthwal, Study on thermal stability of electroless deposited Ni–Co–P alloy thin film. J. Mater. Sci.: Mater. Electron. 22(9), 1495 (2011)Google Scholar
  26. 26.
    M.M. Younan, I.H.M. Aly, M.T. Nageeb, Effect of heat treatment on electroless ternary nickel–cobalt–phosphorus alloy. J. Appl. Electrochem. 32(4), 439–446 (2002)Google Scholar
  27. 27.
    Y. Yang, J.N. Balaraju, Y. Huang, H. Liu, Z. Chen, Interface reaction between an electroless Ni–Co–P metallization and Sn–3.5 Ag lead-free solder with improved joint reliability. Acta Mater. 71, 69–79 (2014)Google Scholar
  28. 28.
    A. Kumar, M. Kumar, D. Kumar, Effect of composition on electroless deposited Ni–Co–P alloy thin films as a diffusion barrier for copper metallization. Appl. Surf. Sci. 258(20), 7962–7967 (2012)Google Scholar
  29. 29.
    A. Kumar, M. Kumar, D. Kumar, Deposition and characterization of electroless Ni–Co–P alloy for diffusion barrier applications. Microelectron. Eng. 87(3), 387–390 (2010)Google Scholar
  30. 30.
    H.F. Zou, Q.K. Zhang, Z.F. Zhang, Interfacial microstructure and mechanical properties of SnBi/Cu joints by alloying Cu substrate. Mater. Sci. Eng. A 532, 167–177 (2012)Google Scholar
  31. 31.
    X. Hu, Y. Li, K. Li, Z. Min, Effect of Bi segregation on the asymmetrical growth of Cu–Sn intermetallic compounds in Cu/Sn–58Bi/Cu sandwich solder joints during isothermal aging. J. Electron. Mater. 42(12), 3567–3572 (2013)Google Scholar
  32. 32.
    P.J. Shang, Z.Q. Liu, D.X. Li, J.K. Shang, Bi–induced voids at the Cu3Sn/Cu interface in eutectic SnBi/Cu solder joints. Scr. Mater. 58(5), 409–412 (2008)Google Scholar
  33. 33.
    P.L. Liu, J.K. Shang, Segregant–induced cavitation of Sn/Cu reactive interface. Scr. Mater. 53(6), 631–634 (2005)Google Scholar
  34. 34.
    J.W. Jang, P.G. Kim, K.N. Tu, D.R. Frear, P. Thompson, Solder reaction-assisted crystallization of electroless Ni–P under bump metallization in low cost flip chip technology. J. Appl. Phys. 85(12), 8456–8463 (1999)Google Scholar
  35. 35.
    J.W. Yoon, B.I. Noh, J.H. Yoon, H.B. Kang, S.B. Jung, Sequential interfacial intermetallic compound formation of Cu6Sn5 and Ni3Sn4 between Sn–Ag–Cu solder and ENEPIG substrate during a reflow process. J. Alloys Compd. 509(9), L153–L156 (2011)Google Scholar
  36. 36.
    P.L. Liu, J.K. Shang, Fracture of SnBi/Ni (P) interfaces. J. Mater. Res. 20(4), 818–826 (2005)Google Scholar
  37. 37.
    J.W. Yoon, C.B. Lee, S.B. Jung, Interfacial reactions between Sn–58 mass% Bi eutectic solder and (Cu, electroless Ni–P/Cu) substrate. Mater. Trans. 43(8), 1821–1826 (2002)Google Scholar
  38. 38.
    L. Magagnin, V. Sirtori, S. Seregni et al., Electroless Co–P for diffusion barrier in Pb-free soldering. Electrochim. Acta 50(23), 4621–4625 (2005)Google Scholar
  39. 39.
    X. Hu, Y. Li, Z. Min, Interfacial reaction and IMC growth between Bi–containing Sn0. 7Cu solders and Cu substrate during soldering and aging. J. Alloys Compd. 582, 341–347 (2014)Google Scholar
  40. 40.
    D.G. Kim, S.B. Jung, Interfacial reactions and growth kinetics for intermetallic compound layer between In-48Sn solder and bare Cu substrate. J. Alloys Compd. 386(1–2), 151–156 (2005)Google Scholar
  41. 41.
    C.H. Wang, C.Y. Kuo, Growth kinetics of the solid–state interfacial reactions in the Sn–Cu/Co and Sn/Co–Cu couples. Mater. Chem. Phys. 130(1–2), 651–656 (2011)Google Scholar
  42. 42.
    A. Li, X. Hu, X. Jiang, Y. Li, Interfacial reaction and microstructure between the Sn3Ag0. 5Cu solder and Cu–Co dual–phase substrate. Appl. Phys. A 124(7), 484 (2018)Google Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2018

Authors and Affiliations

  • Yulong Li
    • 1
  • Zhiliang Wang
    • 1
  • Xuewen Li
    • 1
  • Xiaowu Hu
    • 1
  • Min Lei
    • 1
    Email author
  1. 1.Key Lab for Robot & Welding Automation of Jiangxi Province, Mechanical & Electrical Engineering SchoolNanchang UniversityNanchangChina

Personalised recommendations