Investigation of structural, morphological and optical properties of Nickel-doped Zinc oxide thin films fabricated by co-sputtering

  • Ozkan Bayram
  • Emre Sener
  • Erdal İgman
  • Onder Simsek
Article
  • 26 Downloads

Abstract

In this study, it was aimed to grow Nickel doped (0.0 at.%, 0.16 at.%, 0.20 at. % and 0.24 at. %) Zinc Oxide (NZO) thin films on quartz substrates using Magnetron Sputtering technique. NZO thin films were obtained at a temperature of 450 °C, a pressure of 480 m Torr and a deposition time of 30 min. Co-sputtering process for both Ni and ZnO target was performed using two separate power sources. The DC power of the Ni target material was 20, 30 and 40 W, respectively while the radio frequency (RF) power of the Zinc oxide (ZnO) target material was set to 150 W. Using XRD analysis, thin films were found to have polycrystalline morphology, and the average crystallite size changed significantly depending on the increased Ni doping level. The optical Transmittance of the thin films was greater than 90% in the visible region (550 nm), and this value tends to decrease slightly by Ni doping. The optical band gap (Eg) firstly decreased and then slightly increased with the Nickel doping ratio and these values were found to be 3.23 eV, 3.11 eV and 3.15 eV, respectively, with increase of Ni doping.

References

  1. 1.
    J. Song et al., Bicolor light-emitting diode based on zinc oxide nanorod arrays and poly (2-methoxy, 5-octoxy)-1, 4-phenylenevinylene. J. Electron. Mater. 41(3), 431–436 (2012)CrossRefGoogle Scholar
  2. 2.
    J. Huang, Z. Yin, Q. Zheng, Applications of ZnO in organic and hybrid solar cells. Energy Environ. Sci. 4(10), 3861–3877 (2011)CrossRefGoogle Scholar
  3. 3.
    T. Xu et al., The compatibility of ZnO piezoelectric film with micromachining process. Sens. Actuators A 104(1), 61–67 (2003)CrossRefGoogle Scholar
  4. 4.
    G. Hirata et al., Synthesis and optelectronic characterization of gallium doped zinc oxide transparent electrodes. Thin solid films 288(1–2), 29–31 (1996)CrossRefGoogle Scholar
  5. 5.
    B. Nasr et al., Electrical resistivity of nanocrystalline Al-doped zinc oxide films as a function of Al content and the degree of its segregation at the grain boundaries. J. Appl. Phys. 108(10), 103721 (2010)CrossRefGoogle Scholar
  6. 6.
    Z. Wang et al., Growth of ZnO: Al films by RF sputtering at room temperature for solar cell applications. Solid-State Electron. 53(11), 1149–1153 (2009)CrossRefGoogle Scholar
  7. 7.
    W. Beyer, J. Hüpkes, H. Stiebig, Transparent conducting oxide films for thin film silicon photovoltaics. Thin Solid Films 516(2–4), 147–154 (2007)CrossRefGoogle Scholar
  8. 8.
    L.E. Greene et al., General route to vertical ZnO nanowire arrays using textured ZnO seeds. Nano Lett. 5(7), 1231–1236 (2005)CrossRefGoogle Scholar
  9. 9.
    C. Huang et al., Low content indium-doped zinc oxide films with tunable work function fabricated through magnetron sputtering. Semicond. Sci. Technol. 25(4), 045008 (2010)CrossRefGoogle Scholar
  10. 10.
    C. Klingshirn, The luminescence of ZnO under high one-and two-quantum excitation. Phys. Status Solidi B 71(2), 547–556 (1975)CrossRefGoogle Scholar
  11. 11.
    L. Peng et al., Growth and characterization of indium doped zinc oxide films sputtered from powder targets. J. Wuhan Univ. Technol.-Mater. Sci. Ed. 32(4), 866–870 (2017)CrossRefGoogle Scholar
  12. 12.
    H. Mahdhi et al., Effect of sputtering power on the electrical and optical properties of Ca-doped ZnO thin films sputtered from nanopowders compacted target. Opt. Mater. 45, 97–103 (2015)CrossRefGoogle Scholar
  13. 13.
    H. Mahdhi, K. Djessas, Z.B. Ayadi, Synthesis and characteristics of Ca-doped ZnO thin films by rf magnetron sputtering at low temperature. Mater. Lett. 214, 10–14 (2018)CrossRefGoogle Scholar
  14. 14.
    N.-E. Sung, K.-S. Lee, I.-J. Lee, Structural characterization of Zr-doped ZnO films deposited on quartz substrates by reactive radio frequency magnetron co-sputtering. Thin Solid Films 651, 42–47 (2018)CrossRefGoogle Scholar
  15. 15.
    X. Jiang et al., Aluminum-doped zinc oxide films as transparent conductive electrode for organic light-emitting devices. Appl. Phys. Lett. 83(9), 1875–1877 (2003)CrossRefGoogle Scholar
  16. 16.
    I. Volintiru et al., Evolution of the electrical and structural properties during the growth of Al doped ZnO films by remote plasma-enhanced metalorganic chemical vapor deposition. J. Appl. Phys. 102(4), 043709 (2007)CrossRefGoogle Scholar
  17. 17.
    Y. Liu, L. Zhao, J. Lian, Al-doped ZnO films by pulsed laser deposition at room temperature. Vacuum 81(1), 18–21 (2006)CrossRefGoogle Scholar
  18. 18.
    Y. Caglar et al., Morphological, optical and electrical properties of CdZnO films prepared by sol–gel method. J. Phys. D 42(6), 065421 (2009)CrossRefGoogle Scholar
  19. 19.
    B. Singh et al., Highly conducting zinc oxide thin films achieved without postgrowth annealing. Appl. Phys. Lett. 97(24), 241903 (2010)CrossRefGoogle Scholar
  20. 20.
    M.Y. Zhang, G.J. Cheng, Highly conductive and transparent alumina-doped ZnO films processed by direct pulsed laser recrystallization at room temperature. Appl. Phys. Lett. 99(5), 051904 (2011)CrossRefGoogle Scholar
  21. 21.
    S. Fernandez, F. Naranjo, Optimization of aluminum-doped zinc oxide films deposited at low temperature by radio-frequency sputtering on flexible substrates for solar cell applications. Sol. Energy Mater. Sol. Cells 94(2), 157–163 (2010)CrossRefGoogle Scholar
  22. 22.
    K.H. Kim, R.A. Wibowo, B. Munir, Properties of Al-doped ZnO thin film sputtered from powder compacted target. Mater. Lett. 60(15), 1931–1935 (2006)CrossRefGoogle Scholar
  23. 23.
    J.-H. Oh, K.-K. Kim, T.-Y. Seong, Effects of deposition temperatures and annealing conditions on the microstructural, electrical and optical properties of polycrystalline Al-doped ZnO thin films. Appl. Surf. Sci. 257(7), 2731–2736 (2011)CrossRefGoogle Scholar
  24. 24.
    H. Ahn et al., Substrate effects on the structural properties of Cd1-xMnxTe thin films grown via magnetron Co-sputtering. J. Korean Phys. Soc. 67(4), 668–671 (2015)CrossRefGoogle Scholar
  25. 25.
    G. Paul et al., Structural, optical and electrical studies on sol–gel deposited Zr doped ZnO films. Mater. Chem. Phys. 79(1), 71–75 (2003)CrossRefGoogle Scholar
  26. 26.
    G. Malik et al., Optical and other physical properties of hydrophobic ZnO thin films prepared by dc magnetron sputtering at room temperature. J. Appl. Phys. 122(14), 143105 (2017)CrossRefGoogle Scholar
  27. 27.
    R. Gupta et al., Band gap engineering of ZnO thin films by In2O3 incorporation. J. Cryst. Growth 310(12), 3019–3023 (2008)CrossRefGoogle Scholar
  28. 28.
    R.J. Tilley, Crystals and Crystal Structures (Wiley, New York, 2006)Google Scholar
  29. 29.
    G. Singla, K. Singh, O. Pandey, Williamson–Hall study on synthesized nanocrystalline tungsten carbide (WC). Appl. Phys. A 113(1), 237–242 (2013)CrossRefGoogle Scholar
  30. 30.
    E. Keskenler, G. Turgut, S. Doğan, Investigation of structural and optical properties of ZnO films co-doped with fluorine and indium. Superlattices Microstruct. 52(1), 107–115 (2012)CrossRefGoogle Scholar
  31. 31.
    H. Morkoç, Ü Özgür, Zinc Oxide: Fundamentals, Materials and Device Technology (Wiley, New York, 2008)Google Scholar
  32. 32.
    L. Juárez-Amador et al., Electrical, optical and magnetoresistive behavior of nanostructured ZnO: Cu thin films deposited by sputtering. J. Mater. Sci. 29(18), 15339–15343 (2018)Google Scholar
  33. 33.
    D. Chakraborti, J. Narayan, J. Prater, Room temperature ferromagnetism in Zn 1–x Cu x O thin films. Appl. Phys. Lett. 90(6), 062504 (2007)CrossRefGoogle Scholar
  34. 34.
    H. Liu et al., Structural and optical properties of Cu–N codoped ZnO thin films deposited by magnetron cosputtering. J. Mater. Sci. 29(12), 9901–9907 (2018)Google Scholar
  35. 35.
    T. Li et al., Characteristics of Ni-doped ZnO: Al films grown on glass by direct current magnetron co-sputtering. Thin Solid Films 515(7–8), 3905–3909 (2007)CrossRefGoogle Scholar
  36. 36.
    B. Pandey et al., Synthesis of nanodimensional ZnO and Ni-doped ZnO thin films by atom beam sputtering and study of their physical properties. Physica E 41(7), 1164–1168 (2009)CrossRefGoogle Scholar
  37. 37.
    C.E. Kim et al., Effect of carrier concentration on optical bandgap shift in ZnO: Ga thin films. Thin Solid Films 518(22), 6304–6307 (2010)CrossRefGoogle Scholar
  38. 38.
    Y. Ammaih et al., Structural, optical and electrical properties of ZnO: Al thin films for optoelectronic applications. Opt. Quant. Electron. 46(1), 229–234 (2014)CrossRefGoogle Scholar
  39. 39.
    S. Mondal, P. Mitra, Preparation of Ni doped ZnO thin films by SILAR and their characterization. Indian J. Phys. 87(2), 125–131 (2013)CrossRefGoogle Scholar
  40. 40.
    G. Vijayaprasath et al., Optical and magnetic studies on Gd doped ZnO nanoparticles synthesized by co-precipitation method. J. Lumin. 178, 375–383 (2016)CrossRefGoogle Scholar
  41. 41.
    V. Khomchenko et al., Fabrication and properties of ZnO: Cu and ZnO: Ag thin films. Superlattices Microstruct. 42(1–6), 94–98 (2007)CrossRefGoogle Scholar
  42. 42.
    A. Farag et al., Photoluminescence and optical properties of nanostructure Ni doped ZnO thin films prepared by sol–gel spin coating technique. J. Alloy. Compd. 509(30), 7900–7908 (2011)CrossRefGoogle Scholar
  43. 43.
    S. Brahma et al., Self-assembled ZnO nanoparticles on ZnO microsheet: ultrafast synthesis and tunable photoluminescence properties. J. Phys. D 48(22), 225305 (2015)CrossRefGoogle Scholar
  44. 44.
    S. Singh, N. Rama, M. Ramachandra Rao, Influence of d–d transition bands on electrical resistivity in Ni doped polycrystalline ZnO. Appl. Phys. Lett. 88(22), 222111 (2006)CrossRefGoogle Scholar
  45. 45.
    R. Siddheswaran et al., Reactive magnetron sputtering of Ni doped ZnO thin film: investigation of optical, structural, mechanical and magnetic properties. J. Alloy. Compd. 636, 85–92 (2015)CrossRefGoogle Scholar
  46. 46.
    X. Yan et al., Nanostructure and optical properties of M doped ZnO (M = Ni, Mn) thin films prepared by sol–gel process. Physica B 406(20), 3956–3962 (2011)CrossRefGoogle Scholar
  47. 47.
    A. Ismail, M. Abdullah, The structural and optical properties of ZnO thin films prepared at different RF sputtering power. J. King Saud Univ.-Sci. 25(3), 209–215 (2013)CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  • Ozkan Bayram
    • 1
    • 2
  • Emre Sener
    • 2
  • Erdal İgman
    • 2
  • Onder Simsek
    • 2
    • 3
  1. 1.Department of Electrical and Electronics Engineering, Engineering FacultyBayburt UniversityBayburtTurkey
  2. 2.Department of Nanoscience and Nanoengineering, Graduate School of Natural and Applied SciencesAtaturk UniversityErzurumTurkey
  3. 3.Central Application and Research Laboratory (MERLAB)Agri Ibrahim Cecen UniversityAgriTurkey

Personalised recommendations