Strengthening of very large crystalline and polycrystalline Nd:YAG rods for high-power laser applications

  • Revital FeldmanEmail author
  • Steven Jackel
  • Inon Moshe
  • Avi Meir
  • Eyal Lebiush
  • Zvi Horowitz
  • Yaakov Lumer
  • Yehoshua Shimony
Ceramics
  • 3 Downloads

Abstract

A multistep thermochemical etching procedure was applied to very large Nd3+:YAG rods to increase their fracture strength. The strengthening procedure combined selection of high-quality material, fine centerless grinding, thermochemical etching, and (after completion of the lapping, polishing and AR coating) an additional hot thermochemical etching, with rod ends protected with poly-tetra-fluoro-ethylene (Teflon) caps. The final cleaning step, not previously reported, is essential in removing fracture causing contaminations on the rod surface. A unique thermal load-to-fracture technique was applied on test rods to measure their fracture strength. The rods were thermally loaded up to fracture by means of optical pumping in a specially designed laser pump chamber. The results thus obtained were analyzed by Weibull distribution statistics appropriate to these tests. The strengthened laser rods of this study sustained a maximum pump power density of \( I_{{\ell_{\hbox{max} } }} \) = 500 W cm−1. This value is higher by a factor of four over untreated rods and also higher than any previously published data for such large rods. High-power diode-pumped laser heads were operated with the strengthened crystalline and polycrystalline Nd:YAG rods, yielded output power of ~ 3 kW, when pumped with 7 kW. Such performance was routinely achieved without any instance of rod fracture. Reliability of the strengthening procedure was further demonstrated by the failure-free operation of an azimuthally polarized high-power master-oscillator power-amplifier system (composed of oscillator, preamplifier, and six power amplifiers), emitting an output power in excess of 10 kW.

Notes

Compliance with ethical standards

Conflict of interest

The work presented in this publication has been carried out for few years in Soreq Nuclear Research Center, Yavne, Israel, as an Infrastructure Development Program for solid-state lasers without any external funding. All authors of the present publications declare that they have no conflict of interest with respect to this publication.

References

  1. 1.
    Geusic JE, Marcos HM, Van Uitert LG (1964) Laser oscillations in Nd-doped yttrium-aluminum, yttrium-galium and gadolinium garnets. Appl Phys Lett 4(10):182–184Google Scholar
  2. 2.
    Takada A, Akiyama Y, Takase T, Yuasa H, Ono A (1999) Diode laser-pumped cw Nd:YAG lasers with more than 1 kW output power. In: Fejer MF, Injeyan H, Keller U (eds) Advanced solid-state lasers, OSA technical digest. Optical Society of America, Washington DC, pp 21–23Google Scholar
  3. 3.
    Golla D, Bode M, Knoke S, Schöne W, Tünnermann A (1996) 62-W cw TEM00 Nd:YAG laser side-pumped by fiber-coupled diode lasers. Opt Lett 21(3):210–212Google Scholar
  4. 4.
    Paschotta R, Aus der Au J, Keller U (1991) Thermal effects in high-power end pumped laers with elliptical-mode geometry. IEEE J Selected Top Quantum Electron 6(4):636–642Google Scholar
  5. 5.
    Schöne W, Knoke S, Schirmer S, Tünnermann A (1997) Diode-pumped cw Nd:YAG lasers with output powers up to 750 W. In: Pollock CR, Bosenberg WR (eds) Advanced solid-state lasers, technical digest. Optical Society of America, Washington DC, pp 241–243Google Scholar
  6. 6.
    Koechner W (2006) Solid state laser engineering, 6th edn. Springer Series in Optical Sciences, Berlin, pp 423–487, 102–155 (a Chapter 7, b Chapter 3) Google Scholar
  7. 7.
    Feldman R, Golan Y, Burshtein Z, Jackel S, Moshe I, Meir A, Lumer Y, Shimony Y (2011) Strengthening of polycrystalline (ceramic) Nd:YAG elements for high power laser applications. Opt Mater 33:95–701Google Scholar
  8. 8.
    Marion JE (1986) Fracture of solid-state laser slabs. J Appl Phys 60(1):69–77Google Scholar
  9. 9.
    Harris DC (1999) Materials for infrared windows and domes: properties and performances, SPIE. Optical Engineering Press, Bellingham, WA, pp 84–122 (Chapter 3) Google Scholar
  10. 10.
    Feldman R, Shimony Y, Lebiush E, Golan Y (2008) Effect of hot acid etching on thermomechanical strength of ground YAG laser elements. J Phys Chem Solids 69(4):839–846Google Scholar
  11. 11.
    Wood RM (2003) Laser-induced damage of optical materials. In: Brown RGW, Pike ER (eds) Series in optics and optoelectronics. Institute of Physics Publishing, Bristol, pp 54–131Google Scholar
  12. 12.
    Bloembergen N (1974) Laser-induced electric breakdown in solids. IEEE J Quantum Electron QE 10:375–386Google Scholar
  13. 13.
    Bloembergen N (1973) Role of cracks, pores, and absorbing inclusions on laser induced damage threshold at surfaces of transparent dielectrics. Appl Optics 12(4):661–664Google Scholar
  14. 14.
    Génin FY, Salleo A, Pistor TV, Chase LL (2001) Role of light intensification by cracks in optical breakdown on surfaces. J Opt Soc Am A 18(10):2607–2616Google Scholar
  15. 15.
    Mann G, Phillipps G (1995) Rough surface absorption of Nd:YAG laser rods. Opt Mater 4:811–814Google Scholar
  16. 16.
    Marion J (1985) Strengthened solid-state laser materials. Appl Phys Lett 47(7):694–696Google Scholar
  17. 17.
    Foster JD, Osterink LM (1970) Thermal effects in a Nd:YAG laser. J Appl Phys 41(9):3656–3663Google Scholar
  18. 18.
    Weber R, Neuenschwander B, Weber HP (1999) Thermal effects in solid-state laser materials. Opt Mater 11:245–254Google Scholar
  19. 19.
    Koechner W (1970) Absorbed pump power, thermal profile and stresses in a cw pumped Nd:YAG crystals. Appl Opt 9(6):1429–1434Google Scholar
  20. 20.
    Popov EP (1968) Introduction to mechanics of solids. Prentice-Hall Inc, New Jersey, pp 177–218 (Chapter 6) Google Scholar
  21. 21.
    Byer RL (1985) United State Patent No. 4,555,786, Stanford UniversityGoogle Scholar
  22. 22.
    Shafer KE, Eakins DE, Bahr DF, Norton MG, Lynn KG (2003) Strength enhancement of single crystal laser components. J Mater Res 18(11):2537–2539Google Scholar
  23. 23.
    Gerber M, Graf Th (2001) Optimum parameters to etch Nd:YAG crystals with orthophosphoric acid H3PO4. Optics Lasers Technol 33:449–453Google Scholar
  24. 24.
    Koechner W (1973) Rupture, stress, and modulus of elasticity for Nd:YAG crystals. Appl Phys 2(5):279–280Google Scholar
  25. 25.
    Lebiush E, Jackel S, Goldring S, Moshe I, Tzuk Y, Meir A (2005) Elimination of spherical aberration in multi-kW Nd:YAG rod pump-chambers by pump-distribution control. In: Quarles GJ, Denman C, Sorokina I (eds) Advanced solid-state photonics. Optical Society of America, Washington DC, p 7 (Paper MB45) Google Scholar
  26. 26.
    Moshe I, Jackel S, Lumer Y, Meir A, Feldman R, Shimony Y (2010) Use of polycrystalline Nd:YAG rods to achieve pure radially or azimuthally polarized beams from high-average-power lasers. Opt Lett 35(15):2511–2513Google Scholar
  27. 27.
    Weibull W (1951) A statistical distribution function of wide applicability. J Appl Mech 18:293–297Google Scholar
  28. 28.
    Brown DC (1997) Ultrahigh-average-power diode-pumped Nd:YAG and Yb:YAG laser. IEEE J Quant Elec 33(5):861–873Google Scholar
  29. 29.
    Chang JJ, Dragon EP, Ebbers CA, Bass IL, Cochran CW (1998) An efficient diode-pumped Nd:YAG laser with 451 W of CW IR and 182 W of pulsed green output. In: Bossenberg WR, Fejer MM (eds) OSA trends in optics and photonics, vol 19. Advanced solid-state lasers. Optical Society of America, Washington DC, pp 300–303Google Scholar
  30. 30.
    Burnham RL, Witt G, DiBiase D, Le K, Koechner W (1994) Diode-pumped solid-state lasers with kilowatt average power. In: Bohrer M, Letardi M, Schuoecker T, Weber H (eds) High-power gas and solid state lasers., pp 489–498 (Proceedings, SPIE Vol. 2206) Google Scholar
  31. 31.
    Akiyama AY, Takada A, Takase T, Sasaki M, Yuasa H, Nishida N (2000) Efficient 2-kW diode-pumped cw Nd:YAG single rod laser. In: Injeyan H, Keller U, Marshall C (eds) OSA trends in optics and photonics, vol 34. Advanced solid-state lasers. Optical Society of America, Washington DC, pp 48–51Google Scholar
  32. 32.
    Moshe I, Jackel S, Lumer Y, Meir A, Feldman R, Shimony Y (2011) Maintaining radial-polarization and beam-quality in multi-kW rod-based lasers through the use of polycrystalline Nd:YAG rods. In: Proceedings of the lasers and electro-optics Europe and 12th European quantum electronics CLEO/Europe-EQEC Conference, Münich, Paper No. CA9.5Google Scholar
  33. 33.
    Lumer Y, Moshe I, Jackel S, Horowitz Z, Meir A, Feldman R, Shimony Y (2010) Depolarization induced by pump edge effects in high average power laser rods. J Opt Soc Am B 27(1):38–44Google Scholar
  34. 34.
    Neauport J, Lamaignere L, Bercegol H (2005) Polishing-induced contamination of fused silica and laser induced damage density at 351 nm. Opt Express 13(25):10163–10171Google Scholar
  35. 35.
    Sir George Beilby (1921) Aggregation and flow of solids. MacMillan, LondonGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  1. 1.Applied Physics DivisionSoreq NRCYavneIsrael

Personalised recommendations