In vitro evaluation of the biocompatibility and bioactivity of plasma electrolyte oxidized titania/calcium phosphate nanocoatings on Ti
- 1.1k Downloads
In this study, monolayer and two-layer composite coatings of titania and calcium phosphate were fabricated via plasma electrolyte oxidation technique on titanium substrates. The calcium phosphate layers were produced by using an electrolyte containing calcium acetate and β-glycerophosphate. In order to study and compare their biocompatibility and bioactivity properties MTT, cell adhesion, and soaking in SBF solution tests were performed on both coatings. According to the XPS and AFM analysis results, two-layer coatings have a higher Ca/P proportion on their surface and rougher surface. Higher cell proliferation rate was observed on two-layer specimen’s surface. An appropriate cell adhesion was observed in both coatings. Higher amount of hydroxyapatite (HAp) nanocrystals were observed on coatings with two-layer in comparison with monolayer after being soaked in SBF solution for 28 days. Besides, the proportion of HAp to calcium triphosphate after soaking in SBF solution was higher in two-layer coating.
The authors would like to thank S.M.M. Mirhosseini, A. Ziaee and S. Bonakdar for their kind helps and useful comments. The authors would like to express their sincere appreciations to all personnel working in the Ceramics Synthesis Laboratory at Iran University of Science and Technology. Meanwhile, financial support of Iran National Science Foundation (INSF) is highly appreciated.
- 7.Mihailescu IN, Torricelli P, Bigi A, Mayer I, Iliescu M, Werckmann J, Socol G, Miroiu F, Cuisinier F, Elkaim R, Hildebrand G (2005) Calcium phosphate thin films synthesized by pulsed laser deposition: physico-chemical characterization and in vitro cell response. Appl Surf Sci 248:344–348CrossRefGoogle Scholar
- 17.Zhao X, Cai Q, Li D, He J, Luo Q, Li X, Sun W (2010) Preparation and characterization of bio-ceramic coatings on the surface of pure titanium by plasma electrolytic oxidation-alkali and heat treatment. J Ceram Process Res 11:575–580Google Scholar
- 23.Ratner BD, Hoffman AS, Schoen FJ, lemons JE (eds) (2012) Biomaterials science: an introduction to materials in medicine, ISBN: 978-008-087-780-8Google Scholar
- 24.Vandrovcová M, Bačáková l (2011) Adhesion, growth and differentiation of osteoblasts on surface modified materials developed for bone implants. Physiol Res 60:403–417Google Scholar
- 25.Anil S, Anand PS, Alghamdi H, Jansen JA, Turkyilmaz I (Ed.) Dental implant surface enhancement and osseointegration, implant dentistry—a rapidly evolving practice, ISBN: 978-953-307-658-4 (2011)Google Scholar
- 29.Chang HI, Wang Y, Eberli D (eds) (2011) cell responses to surface and architecture of tissue engineering scaffolds, regenerative medicine and tissue engineering—cells and biomaterials, ISBN: 978-953-307-663-8Google Scholar
- 32.Ferraz MP, Monteiro FJ, Manuel CM (2004) Hydroxyapatite nanoparticles: a review of preparation methodologies. J Appl Biomater Biomech 2:74–80Google Scholar