Microstructure and magnetic properties of SmCo7/Co nanocomposite powders prepared by mechanical alloying
- 23 Downloads
SmCo7/Co nanocomposite powders were prepared by high-energy ball milling of SmCo5 modified by adding Co and annealed at different temperatures. The phase evolution, microstructure and magnetic properties of the nanocomposite powders were analyzed. The results have shown that the annealing temperature and the addition of Co significantly affected the phase structures and magnetic properties of the powders. The nanocomposite powders were completely composed of the SmCo7 phase and the face-centered cubic Co phase. When annealing the SmCo5 powder at 750 °C, the SmCo7 phase decomposed into Th2Zn17-type Sm2Co17 and CaCu5-type SmCo5 phases with an average grain size of 13.9 nm, and the maximum energy product and remanence had maximum values of 10.51 MGOe and 77.92 emu/g, respectively. However, adding 28 wt% Co effectively prevented growth of the grain (11.5 nm) and enhanced the decomposition temperature (850 °C), resulting in a higher maximum magnetic energy product, coercivity, and remanence. The SmCo7 lattice contracted as Co content increased.
This work was supported by National Natural Science Foundation of China (51201191), Chongqing Research Program of Basic Research and Frontier Technology (Nos. cstc2015jcyjA50004, cstc2016jcyjA0232), Scientific and Technological Research Program of Chongqing Municipal Education Commission (KJ1709202), Program for Innovation Teams in University of Chongqing (No. CXTDX201601032), Research Foundation of Chongqing University of Science and Technology (CK2017ZKZD003).
- 5.Zhang Y, Zeng Q, Hadjipanayis GC (2005) Microstructure characterization of ball milled Sm(CoCuFeZr) 2:17 powders. J Appl Phys 97:1350Google Scholar
- 6.Hadjipanayis GC, Zhang Y, Tang W, Chui ST, Liu JF, Chen C, Kronmüller H (2001) High temperature 2:17 magnets: relationship of magnetic properties to microstructure and processing. Cheminform 32(29):3382–3387Google Scholar
- 14.Guo Y, Li W, Feng W, Luo J, Liang JK, He QJ, Yu XJ (2005) Structural stability and magnetic properties of SmCo7−xGax. Appl Phys Lett 86:1514Google Scholar
- 19.Li LY, Yi JH, Peng YD, Huang BY (2005) Recent development in preparation of nanocrystalline rare-earth permanent magnetic materials. Powder Metall Ind 15:35–40Google Scholar
- 24.Song XY, Lu N, Seyring M, Rettenmayr M, Xu WW, Zhang ZX, Zhang JX (2009) Abnormal crystal structure stability of nanocrystalline Sm2Co17 permanent magnet. Appl Phys Lett 94(2):1347Google Scholar
- 26.Pal SK, Schultz L, Gutfleisch O (2013) Effect of milling parameters on SmCo5 nanoflakes prepared by surfactant-assisted high energy ball milling. J Appl Phys 113:821Google Scholar
- 32.Zhang Z, Song X, Li D, Liu X (2013) Phase stability and phase transformation of nanocrystalline SmCo7 alloy and their effects on the magnetic performance. Rare Met Mater Eng 42(3):565–568Google Scholar
- 40.Miao WF, Li GS, Li SL, Wang JT (1992) The role of internal stress in the amorphization process during mechanical alloying. Acta Physica Sin 41(6):924–928Google Scholar