Influence of multiphase on the strain hardening behavior of 60Si2CrVAT spring steel treated by a Q–P–T process
- 21 Downloads
A strong strain hardening ability in ultra-high strength spring steel 60Si2CrVAT was achieved by the design of multiphase microstructures using a quenching–partitioning–tempering process. The microstructure consisted of ~ 70% martensite/bainite and ~ 30% retained austenite, which was obtained at an optimized partitioning temperature of 380 °C. The corresponding yield strength ratio and the product of strength and elongation were 0.81 and 34,828 MPa%, respectively. Interestingly, this sample exhibited a double-stage strain hardening characteristic with a concave-down shape, which was distinct from that of the other samples. The excellent performance of the ultra-high strength spring steel was mainly due to the interactions between the multiple phases and the stability of the retained austenite during cold deformation. This paper provides a new way of obtaining a strong strain hardening ability in ultra-high strength steels, which is expected to be applicable to the cold coiling process.
The research is jointly supported by the National Natural Science Foundation of China (Grant Nos. 51461006 and 51571066), the Natural Science Foundation of the Guizhou Province, China (Grant Nos. 2003 and  6012) and the Guizhou Science and Technology Project (Grant No. (2015) 7646).
- 11.Bachmaier A, Krizan D, Hausmann K, Pichler A (2013) Development of TBF steels with 980 MPa tensile strength for automotive applications: microstructure and mechanical properties. Int Symp New Dev Adv High Strength Sheet Steels 4:413–416Google Scholar
- 18.Zhang K, Xu WZ, Guo ZH, Rong YH (2011) Effects of novel Q–P–T and traditional Q–T processes on the microstructure and mechanical properties of martensitic steels with different carbon content. Acta Metall Sin 47(4):489–496 (translated from Chinese) Google Scholar
- 25.Krauss G (1990) STEELS: heat treatment and processing principles. American Society for Metals, Metals ParkGoogle Scholar
- 26.Magee CL (1970) The nucleation of martensite, in phase transformation. American Society for Metals, Metals Park, pp 115–116Google Scholar
- 27.Ju DY, Narazaki M, Kamisugi H (2000) Computer predictions and experimental verification of residual stresses and distortion in carburizing–quenching of steel. J Shanghai Jiaotong Univ 5(1):165–172Google Scholar
- 29.Chang GL, Kim SJ, Lee TH, Lee S (2004) Effects of volume fraction and stability of retained austenite on formability in a 0.1C–1.5Si–1.5Mn–0.5Cu TRIP-aided cold-rolled steel sheet. Mater Sci Eng A 371(1):16–23Google Scholar
- 33.Ju XH, Tian ZH, Cui GB, Men Y, Cai N (2014) Stability of retained austenite in quenching and partitioning steel. Trans Mater Heat Treat 35(10):119–124 (Translated from Chinese) Google Scholar
- 37.Tang C, Zhu J, Zhang Y (1994) Effect of strain rate ε on strain hardening exponent n of some metallic materials. Acta Metall Sin 7(3):183–186Google Scholar