Constitutive properties and plastic instabilities in the heat-affected zones of advanced high-strength steel spot welds

  • H. Rezayat
  • H. Ghassemi-Armaki
  • S. P. Bhat
  • S. Sriram
  • S. S. Babu
Metals
  • 56 Downloads

Abstract

Recent publications have shown that the load-bearing capability of advanced high-strength steel (AHSS) spot welds do not scale linearly with the tensile strength of the base metal. Although this unexpected degradation of welds has been linked to the tempering of the martensite phase in the heat-affected zone (HAZ), the detailed elastic–plastic stress–strain behavior in different regions of the HAZ has not been reported. In this research, the plastic flow behavior in samples subjected to simulative weld thermal cycles with peak temperatures (TPeak) ranging from 350 to 1250 °C was evaluated. Results from this study showed that the microstructural changes in the HAZ could result in large mechanical heterogeneity in AHSS spot welds. In addition, plastic instability in the form of yield point phenomena was observed. The yield point phenomena in these simulated HAZ samples, in contrast to base metal samples, were confirmed by the observation of Lüders band and stress fluctuations before the onset of strain hardening using digital image correlation. The local plastic instability was correlated to the chemical composition of the steel, initial microstructure, and thermal cycle. The Lüders front velocity maps revealed heterogeneous nucleation and growth of multiple Lüders bands with different front speeds. Interestingly, inter-critical (Ae1 < TPeak < Ae3) HAZ samples show minimum yield strength even though the maximum softening occurs in the subcritical HAZ (TPeak < Ae1) samples.

Notes

Acknowledgements

The authors would like to acknowledge the financial support from the ArcelorMittal Global R&D for carrying out this work. The authors also thank Sabina Kumar for the help in post-processing the DIC data and John Bohling for the help in setting up the Gleeble simulator for thermal simulations.

Compliance with ethical standards

Conflict of interest

The authors declare that they have no conflict of interest.

References

  1. 1.
    Kuziak R, Kawalla R, Waengler S (2008) Advanced high strength steels for automotive industry. Arch Civ Mech Eng 8:103–117CrossRefGoogle Scholar
  2. 2.
    Khan MI, Kuntz ML, Biro E, Zhou Y (2008) Microstructure and mechanical properties of resistance spot welded advanced high strength steels. Mater Trans 49:1629–1637CrossRefGoogle Scholar
  3. 3.
    Dancette S, Massardier-Jourdan V, Fabrègue D, Merlin J, Dupuy T, Bouzekri M (2011) HAZ microstructures and local mechanical properties of high strength steels resistance spot welds. ISIJ Int 51:99–107CrossRefGoogle Scholar
  4. 4.
    Kunishige K, Yamauchi N, Taka T, Nagao N (1983) Softening in weld heat affected zone of dual phase steel sheet for automotive wheel rim, SAE Technical Paper 1983Google Scholar
  5. 5.
    Biro E, McDermid JR, Embury JD, Zhou Y (2010) Softening kinetics in the subcritical heat-affected zone of dual-phase steel welds. Metall Mater Trans A 41:2348–2356CrossRefGoogle Scholar
  6. 6.
    Baltazar Hernandez VH, Panda SK, Okita Y, Zhou NY (2009) A study on heat affected zone softening in resistance spot welded dual phase steel by nanoindentation. J Mater Sci 45:1638–1647.  https://doi.org/10.1007/s10853-009-4141-0 CrossRefGoogle Scholar
  7. 7.
    Waterschoot T, Verbeken K, De Cooman BC (2006) Tempering kinetics of the martensitic phase in DP steel. ISIJ Int 46:138–146CrossRefGoogle Scholar
  8. 8.
    Xia M, Biro E, Tian Z, Zhou YN (2008) Effects of heat input and martensite on HAZ softening in laser welding of dual phase steels. ISIJ Int 48:809–814CrossRefGoogle Scholar
  9. 9.
    Speich GR (1981) Physical metallurgy of dual-phase steels. In: Fundamentals of dual-phase steels, pp 3–45Google Scholar
  10. 10.
    Rezayat H, Babu SS, Ghassemi-Armaki H (2016) Effects of heat affected zone softening extent on strength of advanced high strength steels resistance spot weld. In: Trends in welding research, proceedings of the 10th international conference, Tokyo, JapanGoogle Scholar
  11. 11.
    Hernandez VHB, Panda SK, Kuntz ML, Zhou Y (2010) Nanoindentation and microstructure analysis of resistance spot welded dual phase steel. Mater Lett 64:207–210CrossRefGoogle Scholar
  12. 12.
    Baltazar Hernandez VH, Nayak SS, Zhou Y (2011) Tempering of martensite in dual-phase steels and its effects on softening behavior. Metall Mater Trans A 42:3115–3129CrossRefGoogle Scholar
  13. 13.
    Bhadeshia HKDH (1997) Martensite and bainite in steels : transformation mechanism & mechanical properties. Le J Phys IV 07:C5-367–C5-376Google Scholar
  14. 14.
    Porter DA, Easterling KE, Sherif M (2011) Phase transformations in metals and alloys (Revised Reprint). CRC Press, Boca RatonGoogle Scholar
  15. 15.
    Rosenthal D (1941) Mathematical theory of heat distribution during welding and cutting. Weld J 20:220s–234sGoogle Scholar
  16. 16.
    Ranganathan BN, Grenga HE (1973) Field-ion microscope investigations of fine structures in as-quenched and tempered ferrous martensite. Scr Metall 7:69–71CrossRefGoogle Scholar
  17. 17.
    Krauss G, Pitsch W (1965) Fine structure and habit planes of martensite in an iron-33 wt (nickel single crystal. J Met 17:1060Google Scholar
  18. 18.
    Krauss G, Balliett TA (1976) Fine structure and the early stages of tempering in the martensite of an Fe-1.22 C alloy. Metall Trans A 7:318–320CrossRefGoogle Scholar
  19. 19.
    Speich GR, Miller RL (1980) Tempering of ferrite–martensite steels. J Met 32:45–46Google Scholar
  20. 20.
    Krauss G (2017) Tempering of lath martensite in low and medium carbon steels: assessment and challenges. Steel Res Int 88:1700038CrossRefGoogle Scholar
  21. 21.
    Babu SS, Hono K, Sakurai T (1994) Atom probe field ion microscopy study of the partitioning of substitutional elements during tempering of a low-alloy steel martensite. Metall Mater Trans A 25:499–508CrossRefGoogle Scholar
  22. 22.
    Ghassemi-Armaki H, Biro E, Sadagopan S (2017) Advanced characterization of HAZ softening of AHSS for crash modeling. ISIJ Int 57:1451–1460CrossRefGoogle Scholar
  23. 23.
    Ghassemi-Armaki H, Bhat S, Kelley S, Sadagopan S (2017) Quasi-static spot weld strength of advanced high-strength sheet steels this study highlights the spot weld strength in tension–shear and cross-tension loading modes, and HAZ strength as a function of base metal strength, in sheet steels. Weld J 96:104S–112SGoogle Scholar
  24. 24.
    Yang YP, Babu SS, Orth F, Peterson W (2008) Integrated computational model to predict mechanical behaviour of spot weld. Sci Technol Weld Join 13:232–239CrossRefGoogle Scholar
  25. 25.
    AWS D8.9M (2012) Test methods for evaluating the resistance spot welding behavior of automotive sheet steel materials, 3rd edn. American Welding Society (AWS), MiamiGoogle Scholar
  26. 26.
    Vitek JM, Babu SS (2011) Multiscale characterisation of weldments. Sci Technol Weld Join 16:3–11CrossRefGoogle Scholar
  27. 27.
    Speich GR (1969) Tempering of low-carbon martensite. Trans Metall Soc AIME 245:2553–2564Google Scholar
  28. 28.
    Morito S, Adachi Y, Ohba T (2009) Morphology and crystallography of sub-blocks in ultra-low carbon lath martensite steel. Mater Trans 50:1919–1923CrossRefGoogle Scholar
  29. 29.
    Biro E, McDermid JR, Vignier S, Norman Zhou Y (2014) Decoupling of the softening processes during rapid tempering of a martensitic steel. Mater Sci Eng A 615:395–404CrossRefGoogle Scholar
  30. 30.
    Saha DC, Biro E, Gerlich AP, Zhou NY (2016) Fusion zone microstructure evolution of fiber laser welded press-hardened steels. Scr Mater 121:18–22CrossRefGoogle Scholar
  31. 31.
    Krauss G, Balliett TA (1976) Fine-structure and early stages of tempering in martensite of an Fe 1.22 C alloy. Metall Trans A Phys Metall Mater Sci 7:318–320CrossRefGoogle Scholar
  32. 32.
    Caron RN, Krauss G (1972) Tempering of Fe–C lath martensite. Metall Trans 3:2381–2389CrossRefGoogle Scholar
  33. 33.
    Hollomon JH, Jaffe LD (1945) Time-temperature relations in tempering steel. Trans Am Inst Min Metall Eng 162:223–249Google Scholar
  34. 34.
    Ziaebrahimi F, Krauss G (1983) The evaluation of tempered martensite embrittlement in 4130-steel by instrumented Charpy V-notch testing. Metall Trans A Phys Metall Mater Sci 14:1109–1119CrossRefGoogle Scholar
  35. 35.
    Mittemeher EJ, Cheng L, Van der Schaaf PJ, Brakman CM, Korevaar BM (1988) Analysis of nonisothermal transformation kinetics; tempering of iron–carbon and iron–nitrogen martensites. Metall Trans A 19:925–932CrossRefGoogle Scholar
  36. 36.
    Owen WS (1954) The effect of silicon on the kinetics of tempering. Trans Am Soc Met 46:812–829Google Scholar
  37. 37.
    Wang Y, Denis S, Appolaire B, Archambault P (2004) Modelling of precipitation of carbides during tempering of martensite. J Phys IV (Proc) 120:103–110Google Scholar
  38. 38.
    Malheiros LRC, Rodriguez EAP, Arlazarov A (2017) Mechanical behavior of tempered martensite: characterization and modeling. Mater Sci Eng A Struct Mater Prop Microstruct Process 706:38–47CrossRefGoogle Scholar
  39. 39.
    Li M, Sun FW, Barrett RA, Meade E, Li DF, O’Donoghue PE et al (2017) Influence of material inhomogeneity on the mechanical response of a tempered martensite steel. Proc Inst Mech Eng Part L J Mater-Des Appl 231:14–22CrossRefGoogle Scholar
  40. 40.
    Bhadeshia HKDH, Honeycombe RWK (2017) Tempering of martensite. In: Steels: microstructure and properties, 4th edn, pp 237–270Google Scholar
  41. 41.
    Saha DC, Biro E, Gerlich AP, Zhou Y (2016) Effects of tempering mode on the structural changes of martensite. Mater Sci Eng A Struct Mater Prop Microstruct Process 673:467–475CrossRefGoogle Scholar
  42. 42.
    Shi ZM, Gong W, Tomota Y, Harjo S, Li J, Chi B et al (2015) Study of tempering behavior of lath martensite using in situ neutron diffraction. Mater Charact 107:29–32CrossRefGoogle Scholar
  43. 43.
    Li H, Gao S, Tian Y, Terada D, Shibata A, Tsuji N (2015) Influence of tempering on mechanical properties of ferrite and martensite dual phase steel. Mater Today Proc 2:667–671CrossRefGoogle Scholar
  44. 44.
    Cvetkovski K, Ahlstrom J, Persson C (2014) Rapid thermomechanical tempering of iron–carbon martensite. Mater Sci Technol 30:1832–1834CrossRefGoogle Scholar
  45. 45.
    Kang S, Lee SJ (2014) Prediction of tempered martensite hardness incorporating the composition-dependent tempering parameter in low alloy steels. Mater Trans 55:1069–1072CrossRefGoogle Scholar
  46. 46.
    Ohlund CEIC, Schlangen E, Offerman SE (2013) The kinetics of softening and microstructure evolution of martensite in Fe–C–Mn steel during tempering at 300 °C. Mater Sci Eng A Struct Mater Prop Microstruct Process 560:351–357CrossRefGoogle Scholar
  47. 47.
    Sun L, Zhao ZY, Yang XZ, Xue RD (2013) Effect of tempering process on residual stress in hot rolled low carbon martensite high-strength steel strip. Mater Des Process Appl Parts 1–4 690–693:222–226Google Scholar
  48. 48.
    Di Schino A, Alleva L, Guagnelli M (2012) Microstructure evolution during quenching and tempering of martensite in a medium C steel. Recryst Grain Growth IV 715–716:860–865Google Scholar
  49. 49.
    Hernandez VHB, Nayak SS, Zhou Y (2011) Tempering of martensite in dual-phase steels and its effects on softening behavior. Metall Mater Trans A Phys Metall Mater Sci 42a:3115–3129CrossRefGoogle Scholar
  50. 50.
    Mazur J (1949) Structure of tempered martensite. Nature 164:230–231CrossRefGoogle Scholar
  51. 51.
    Michel A (1946) The structure of tempered martensite. J Iron Steel Inst 154:P152–P153Google Scholar
  52. 52.
    Cottrell AH, Bilby BA (1949) Dislocation theory of yielding and strain ageing of iron. Proc Phys Soc Lond Sect A 62:49–62CrossRefGoogle Scholar
  53. 53.
    Hall E (2012) Yield point phenomena in metals and alloys. Springer, BerlinGoogle Scholar
  54. 54.
    Waterschoot T, De AK, Vandeputte S, De Cooman BC (2003) Static strain aging phenomena in cold-rolled dual-phase steels. Metal Mater Trans A Phys Metall Mater Sci 34a:781–791CrossRefGoogle Scholar
  55. 55.
    Ahn TH, Oh CS, Lee K, George EP, Han HN (2012) Relationship between yield point phenomena and the nanoindentation pop-in behavior of steel. J Mater Res 27:39–44CrossRefGoogle Scholar
  56. 56.
    Conrad H, Schoeck G (1960) Cottrell locking and the flow stress in iron. Acta Metall 8:791–796CrossRefGoogle Scholar
  57. 57.
    Gerberich WW, Venkataraman S, Nelson J, Huang H, Lilleodden E, Bonin W (1995) Yield point phenomena and dislocation velocities underneath indentations into BCC crystals. Thin Films Stress Mech Prop V 356:629–644Google Scholar
  58. 58.
    Hahn GT (1962) Model for yielding with special reference to yield-point phenomena of iron and related bcc metals. Acta Metall 10:727–738CrossRefGoogle Scholar
  59. 59.
    Tsuchida N, Tomota Y, Nagai K, Fukaura K (2006) A simple relationship between Luders elongation and work-hardening rate at lower yield stress. Scr Mater 54:57–60CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC, part of Springer Nature 2019

Authors and Affiliations

  1. 1.Mechanical, Aerospace and Biomedical EngineeringUniversity of Tennessee – KnoxvilleKnoxvilleUSA
  2. 2.Automotive Product ResearchArcelorMittal Global R&DEast ChicagoUSA
  3. 3.Manufacturing Demonstration FacilityOak Ridge National LaboratoryOak RidgeUSA

Personalised recommendations