Journal of Materials Science

, Volume 46, Issue 20, pp 6726–6733 | Cite as

Influence of curing temperature on the evolution of magnesium oxychloride cement

  • Vincenzo M. SglavoEmail author
  • Francesca De Genua
  • Alexia Conci
  • Riccardo Ceccato
  • Roberto Cavallini


Hardening behaviour and strength of oxychloride cement strongly depend on the formation of Phase 3 and Phase 5 from MgO and magnesium chloride water solution, and the initial composition can be chosen accordingly within the corresponding phase diagram. A certain number of reactions occur before the final formation of P5 or P3 crystals, and several parameters influence the transformations kinetic, such as MgO reactivity and temperature. Several articles deal with the first aspect, while no indications can be found with regard to the curing temperature’s effect on the formation of noble phases. In this article the evolution of magnesium oxychloride cement pastes is analysed at various curing temperatures between 5 and 40 °C. The study is carried out to simulate typical industrial processing conditions and indicate optimal conditions for the production of high chemical and mechanical resistance oxychloride cement. It is shown that at low temperature, Phase 3 is produced in place of Phase 5, and a certain amount of MgO remains non-reacted. The corresponding cement is characterised by lower mechanical strength and higher water solubility.


Magnesium Chloride Silicone Mould Hexahydrate Magnesium Chloride Universal Mechanical Testing Machine Magnesium Oxychloride Cement 



The authors thank Deroma Spa for their financial support. The authors thank also Dr. Andrea Camporese and Dr. Marco Passerini (Ricert srl, Monte di Malo , VI, Italy) for their helpful discussions.


  1. 1.
    Sorel S (1867) C R Acad Sci France 65:102Google Scholar
  2. 2.
    P de Henau, M Dupas (1976) In Proceedings of the second international symposium on the deterioration of building stone, Athens, p 319Google Scholar
  3. 3.
    Skoulikidis Th, Papakonstantinou E, Galanos A, Doganis Y (1994) Study for the restoration of the Parthenon, vol 3. Ministry of Culture, Committee for the Preservation of the Acropolis Monuments, AthensGoogle Scholar
  4. 4.
    Maravelaki-Kalaitzaki P, Moraitou G (1999) Cem Concr Res 29:1929CrossRefGoogle Scholar
  5. 5.
    Xia S, Xing P, Gao S (1991) Thermochim Acta 183:349CrossRefGoogle Scholar
  6. 6.
    de Castellar MD, Lorente JC, Traveria A, Tura JM (1996) Cem Concr Res 26(8):1199CrossRefGoogle Scholar
  7. 7.
    Plekhanova TA, Keriene J, Gailius A, Yakovlev GI (2007) Constr Build Mater 21:1833CrossRefGoogle Scholar
  8. 8.
    Hassan SSM, Awwad NS, Aboterika AHA (2006) J Radioanal Nucl Chem 269(1):135CrossRefGoogle Scholar
  9. 9.
    Awwad NS, Daifullah AAM (2005) J Radioanal Nucl Chem 264(3):623CrossRefGoogle Scholar
  10. 10.
    Sorrell CA, Armstrong CR (1976) J Am Ceram Soc 59(1–2):51CrossRefGoogle Scholar
  11. 11.
    Matkovic B, Young IF (1973) Phys Sci 246:79Google Scholar
  12. 12.
    Matkovic B, Popovic S, Rogic V, Zunic T, Young JF (1977) J Am Ceram Soc 60(11–12):504CrossRefGoogle Scholar
  13. 13.
    Li Z, Chau CK (2007) Cem Concr Res 37:866CrossRefGoogle Scholar
  14. 14.
    Urwongse L, Sorrell CA (1980) J Am Ceram Soc 63(9–10):501CrossRefGoogle Scholar
  15. 15.
    Cole WF, Demediuk T (1955) Aust J Chem 8(2):234CrossRefGoogle Scholar
  16. 16.
    Bilinski H, Matkovic B, Mazuranic C, Zunic TB (1984) J Am Ceram Soc 67(4):266CrossRefGoogle Scholar
  17. 17.
    Dehua D, Chuanmei Z (1999) Cem Concr Res 29:1365CrossRefGoogle Scholar
  18. 18.
    Lutterotti L, Ceccato R, Dal Maschio R, Pagani E (1998) Mater Sci Forum 278–281:87CrossRefGoogle Scholar
  19. 19.
    Lutterotti L, Bortolotti M, Ischia G, Lonardelli I, Wenk H-R (2007) Z Kristallogr Suppl 26:125CrossRefGoogle Scholar
  20. 20.
    Shetty DK, Rosenfield AR, McGuire P, Bansal GK, Duckworth WH (1980) Ceram Bull 59(12):1193Google Scholar
  21. 21.
    JCPDS – Joint Committee on Powder Diffraction Standards – PDF Powder Diffraction FileGoogle Scholar
  22. 22.
    ICSD Collection Code – available on Crystallography Open Database (COD).

Copyright information

© Springer Science+Business Media, LLC 2011

Authors and Affiliations

  • Vincenzo M. Sglavo
    • 1
    Email author
  • Francesca De Genua
    • 1
  • Alexia Conci
    • 1
  • Riccardo Ceccato
    • 1
  • Roberto Cavallini
    • 2
  1. 1.DIMTI, University of TrentoTrentoItaly
  2. 2.Deroma SpaMaloItaly

Personalised recommendations