Synthesis of Fe–4.6 wt% B alloy via electro-deoxidation of mixed oxides

  • Taylan Örs
  • Serdar Tan
  • Tayfur ÖztürkEmail author
  • İshak Karakaya
Article

Abstract

Fe–4.6 wt% B alloy was synthesized via electro-deoxidation of the mixed oxide precursor. The oxides, Fe2O3 and B2O3, mixed in suitable proportions were sintered at 900 °C yielding pellets with a two-phase structure; Fe2O3 and Fe3BO6. The sintered pellets, connected as cathode, were then electro-deoxidized in molten CaCl2 or in CaCl2–NaCl eutectic, against a graphite anode at 3.1 V. The electrolysis at 850 °C has successfully yielded a powder mixture of Fe and Fe2B. Sequence of changes during the electrolysis was followed by interrupted experiments conducted at 850 °C. This has shown that iron is extracted quite early during the electrolysis through the depletion of oxygen from the starting oxide; Fe2O3, forming the other iron oxides in the process. Boron follows a more complicated route. Fe3BO6, the initial boron-bearing phase, was depleted in the early stages due to its reaction with molten salt. This gave rise to the formation of calcium borate. Boron was extracted from calcium borate in later stages of electrolysis, which appeared to have reacted in situ with the iron forming compound Fe2B.

Keywords

Fe2O3 B2O3 Molten Salt Sintered Pellet Graphite Anode 
These keywords were added by machine and not by the authors. This process is experimental and the keywords may be updated as the learning algorithm improves.

Notes

Acknowledgement

This work is supported by Scientific and Technological Council of Turkey (TUBITAK MAG 105M352).

References

  1. 1.
    Fray DJ, Chen GZ (2004) Mater Sci Technol 20:295CrossRefGoogle Scholar
  2. 2.
    Fray DJ (2001) JOM 53:26CrossRefGoogle Scholar
  3. 3.
    Chen GZ, Fray DJ, Farthing TW (2000) Nature 407:361CrossRefGoogle Scholar
  4. 4.
    Suzuki RO, Tatemoto K, Kitagawa H (2004) J Alloys Compd 385:173CrossRefGoogle Scholar
  5. 5.
    Gordo E, Chen GZ, Fray DJ (2004) Electrochim Acta 49:2195CrossRefGoogle Scholar
  6. 6.
    Centeno-Sanchez RL, Fray DJ, Chen GZ (2007) J Mater Sci 42:7494. doi: https://doi.org/10.1007/s10853-007-1588-8 CrossRefGoogle Scholar
  7. 7.
    Dring K, Bhagat R, Jackson M, Dashwood R, Inman D (2006) J Alloys Compd 419:103CrossRefGoogle Scholar
  8. 8.
    Qiu G, Wang D, Ma M, Jin X, Chen GZ (2006) J Electroanal Chem 589:139CrossRefGoogle Scholar
  9. 9.
    Jiang K, Hu X, Ma M, Wang D, Qiu G, Jin X, Chen GZ (2006) Angew Chem 45:428CrossRefGoogle Scholar
  10. 10.
    Wang SL, Xue Y, Sun H (2006) J Electroanal Chem 595:109CrossRefGoogle Scholar
  11. 11.
    Yan XY, Fray DJ (2005) J Electrochem Soc 152:E308CrossRefGoogle Scholar
  12. 12.
    Tan S, Örs T, Aydinol MK, Öztürk T, Karakaya I (2009) J Alloys Compd 475:368. doi: https://doi.org/10.1016/j.jallcom.2008.07.018 CrossRefGoogle Scholar
  13. 13.
    Makram H, Touron L, Loriers J (1972) J Cryst Growth 13–14:585CrossRefGoogle Scholar
  14. 14.
    Cam I, Timuçin M (2004) In: Proceedings of the 2nd international boron symposium, Chamber of Mining Engineers of Turkey, Eskisehir, 2004, p 195Google Scholar
  15. 15.
    Tripathy PK, Gauthier M, Fray DJ (2007) Metall Mater Trans B 38:893CrossRefGoogle Scholar
  16. 16.
    Barin I, Knacke O, Kubaschewski O (1973) Thermochemical properties of inorganic substances, 2nd edn. Springer, BerlinGoogle Scholar
  17. 17.
    Bale CW, Chartrand P, Degterov SA, Eriksson G, Hack K, Ben Mahfoud R, Melançon J, Pelton AD, Petersen S (2002) Calphad 26:189CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2009

Authors and Affiliations

  • Taylan Örs
    • 1
  • Serdar Tan
    • 1
  • Tayfur Öztürk
    • 1
    Email author
  • İshak Karakaya
    • 1
  1. 1.Department of Metallurgical and Materials EngineeringMiddle East Technical UniversityAnkaraTurkey

Personalised recommendations