Laser bonding and characterization of Kapton® FN/Ti and Teflon® FEP/Ti systems
- 189 Downloads
Kapton® FN and Teflon® FEP (fluorinated ethylene propylene) polymers are resistant to most chemical solvents, heat sealable, and have low moisture uptake, which make them attractive as packaging materials for electronics and implantable devices. Kapton® FN/Ti and Teflon® FEP/Ti microjoints were fabricated by using focused infrared laser irradiation. Laser-bonded samples were tested with a micro-testing machine under lap shear load and the bond strength was determined. The bond strength for the Kapton® FN/Ti and Teflon® FEP/Ti systems was found to be 3.32 and 8.48 N/mm2, respectively. The failure mode of the mechanically tested samples was studied by using optical microscopy and scanning electron microscopy coupled with energy dispersive X-ray spectroscopy. Chemical interactions during laser bonding of Kapton® FN to titanium were studied by using X-ray photoelectron spectroscopy (XPS). The XPS results give evidence for the formation of Ti–F bonds in the interfacial region.
KeywordsPolyimide Titanium Foil Energy Dispersive Spectroscopy Spectrum TiF3 Chemical Bond Formation
We would like to acknowledge the assistance of Dr. Eric McCullen and the SSIM characterization laboratory in the XPS measurements. We would like to thank Dr. Yi Liu for his assistance in the SEM-EDS experiments. We also acknowledge Dr. Frank Jones for suggesting that we investigate KaptonFN. This work has been supported by Michigan Economic Development Corporation (MEDC). Grant # 06-1-P1-0219 (January 2007–December 2009).
- 1.Kim ET, Seo JM, Zhou JA, Jung H, Kim SJ (2004) IEEE international workshop on biomedical circuits & systems, p 12Google Scholar
- 3.Massey LK (2003) Permeability properties of plastics and elastomers: a guide to packaging and barrier materials, 2nd edn. Plastics Design LibraryGoogle Scholar
- 4.Bauer I, Russek UA, Herfurth H, Witte R, Heinemann S, Newaz G, Mian A, Georgiev D, Auner G (2004) Proceedings of SPIE—Photonics West LASE 2004: lasers and applications in science and engineering conference, vol 5339, p 454Google Scholar
- 14.Sultana T, Newaz G, Georgiev GL, Baird RJ, Auner GW, Patwa R, Herfurth HJ (2008) J Mater Sci (submitted)Google Scholar