, Volume 44, Issue 2, pp 639–646 | Cite as

Destabilization of cubic-stabilized zirconia electrolyte induced by boron oxide under reducing atmosphere

  • Haruo KishimotoEmail author
  • Natsuko Sakai
  • Katsuhiko Yamaji
  • Teruhisa Horita
  • Yue-Ping Xiong
  • Manuel E. Brito
  • Harumi Yokokawa
Article

Abstract

The stability of yttria-stabilized zirconia (YSZ) and scandia-stabilized zirconia (ScSZ) electrolytes against boron oxide was examined. Boron oxide was painted on the polished surface of YSZ and ScSZ and annealed at 1273 K for 100 h under wet hydrogen flowing condition. The X-ray diffractometry, scanning electron microscopy/energy dispersive X-ray analysis, and Raman studies revealed that formation of Y2O3 and Sc2O3 occurred on YSZ and ScSZ surfaces contacting the boron oxide, but rare earth borates were not observed. The surface of electrolytes around precipitated particles became rough and phase transformation was confirmed from the cubic to the tetragonal or the monoclinic phases due to stabilizer removal from cubic zirconia. It has been also verified that small amounts of zirconium and yttrium were transported from the electrolyte to the gas phase via boron component. This destabilization effect induced by boron oxide was more serious for ScSZ than for YSZ. A destabilization mechanism under wet hydrogen atmosphere is proposed based on pseudo ternary phase diagrams for the YO1.5–BO1.5–ZrO2 system and the ScO1.5–BO1.5–ZrO2 system and thermodynamic considerations.

Keywords

B2O3 Scandium Monoclinic Phase Rare Earth Oxide Vanadium Oxide 

Notes

Acknowledgement

This study was supported by the New Energy and Industrial Technology Development Organization (NEDO) of Japan.

References

  1. 1.
    Abriata JP, Garces J, Versaci R (1986) Bull Alloy Phase Diagr 7:116CrossRefGoogle Scholar
  2. 2.
    Wang WE, Olander DR (1993) J Nucl Mater 201:231CrossRefGoogle Scholar
  3. 3.
    Minh NQ, Takahashi T (1995) In: Science and technology of ceramic fuel cells. Elsevier, Amsterdam, p 69CrossRefGoogle Scholar
  4. 4.
    Ishihara T, Sammes NM, Yamamoto O (2003) In: Singhal SC, Kendall K (eds) High temperature solid oxide fuel cells—fundamentals, design and applications. Elsevier, Oxford, p 83Google Scholar
  5. 5.
    Mizutani Y, Tamura M, Kawai M, Yamamoto O (1994) Solid State Ion 72:271CrossRefGoogle Scholar
  6. 6.
    Yokokawa H, Horita T, Yamaji K, Kishimoto H, Xiong YP, Brito ME (2008) In: Steinberger-Wilckens R (ed) Proceedings of 8th European solid oxide fuel cell forum, B1004Google Scholar
  7. 7.
    Toriz FC, Thakker AB, Gupta SK (1989) Surf Coat Technol 39/40:161CrossRefGoogle Scholar
  8. 8.
    Susnitzky DW, Hertl W, Barry Carter C (1988) J Am Ceram Soc 71:992CrossRefGoogle Scholar
  9. 9.
    Hertl W (1988) J Appl Phys 63:5514CrossRefGoogle Scholar
  10. 10.
    Jones RL (1990) High Temp Sci 27:369Google Scholar
  11. 11.
    Yokokawa H, Sakai N, Kawada T, Dokiya M (1993) In: Badwal SPS, Bannister MJ, Hannink RHJ (eds) Science and technology of zirconia V. The Tenomic Publication Co. Inc., Lancaster, PA, USA, p 752Google Scholar
  12. 12.
    Buchanan RC, Sircar A (1983) Comm Am Ceram Soc Feb:C-20Google Scholar
  13. 13.
    Ananthapadmanabhan PV, Menon SB, Venkatramani N, Rohatgi VK (1989) J Mater Sci 24:4432CrossRefGoogle Scholar
  14. 14.
    Guo X (1996) J Mater Sci Lett 15:38CrossRefGoogle Scholar
  15. 15.
    de Florio DZ, Muccillo R (2004) Mater Res Bull 39:1539CrossRefGoogle Scholar
  16. 16.
    Calculated with the thermodynamic database MALT for windows and the programs gem and CHD, Kagaku gijutsu-Sha, Japan. https://doi.org/ww.kagaku.com/malt/
  17. 17.
    Fujimori H, Yashima M, Kakihana M, Yoshimura M (1998) J Am Ceram Soc 81:2885CrossRefGoogle Scholar
  18. 18.
    Levin EM (1967) J Am Ceram Soc 50:53CrossRefGoogle Scholar
  19. 19.
    Figure 4390 (1975) In: Levin EM, McMurdie HF (eds) Phase diagrams for ceramists. The American Ceramic Society, Inc., p 140Google Scholar
  20. 20.
    Yokokawa H, Sakai N, Kawada T, Dokiya M (1993) In: Badwal SPS, Bannister MJ, Hannink RHJ (eds) Science and technology of zirconia V. Tenomic Publication Co. Inc., Lancaster, PA, USA, p 592Google Scholar

Copyright information

© Springer Science+Business Media, LLC 2008

Authors and Affiliations

  • Haruo Kishimoto
    • 1
    Email author
  • Natsuko Sakai
    • 1
  • Katsuhiko Yamaji
    • 1
  • Teruhisa Horita
    • 1
  • Yue-Ping Xiong
    • 1
  • Manuel E. Brito
    • 1
  • Harumi Yokokawa
    • 1
  1. 1.National Institute of Advanced Industrial Science and Technology (AIST)TsukubaJapan

Personalised recommendations