High-purity amorphous silica originated in rice husks via carboxylic acid leaching process

  • Junko Umeda
  • Katsuyoshi KondohEmail author
Article

Abstract

The environmentally benign, harmless to human, and economically effective process to produce high-purity amorphous SiO2 materials from rice husks has been established by using a carboxylic acid leaching, not the conventional strong acids. TG-DTA measurement and GCMS analysis indicated that the leaching was effective for the hydrolysis of celluloses and hemicelluloses contained in rice husks at 473–873 K, which produced the same results in using the conventional sulfuric acid. In particular, the formation of furfurals and levoglucosans occurred via the hydrolysis at 473 K and 673 K, respectively, when using rice husks leached by citric acid solutions. The metallic impurities could be also removed from the husks via a chelate reaction between carboxyl groups (–COOH) and the metal elements. Concerning the burning conditions of rice husks after the acid leaching, it was necessary to supply a suitable amount of air to completely combust organics; for example, it required air supplement of 50 mL/min or more. High-purity amorphous silica materials with 99 wt% or more were prepared from rice husks by applying the citric acid leaching treatment and burning process at 1073 K in air.

Keywords

Hemicellulose Furfural Rice Straw Rice Husk Acid Leaching 

Notes

Acknowledgement

This study was supported by “Research & Technology Development on Waste Management Research Grant”, Ministry of the Environment.

References

  1. 1.
    Yelcin N, Sevinc V (2001) Ceram Int 27:219CrossRefGoogle Scholar
  2. 2.
    Park BD, Wi SG, Lee KH, Singh AP, Yoon TH, Kim YS (2003) Biomass Bioenergy 25:319CrossRefGoogle Scholar
  3. 3.
    Nehdi M, Quette JD, Damatty AE (2003) Cem Concr Res 33:1203CrossRefGoogle Scholar
  4. 4.
    Krishnarao RV, Godkhindi MM (1992) Ceram Int 18:185CrossRefGoogle Scholar
  5. 5.
    Naskar MK, Chatterjee M (2004) J Eur Ceram Soc 24:3499CrossRefGoogle Scholar
  6. 6.
    Chakraverti A, Mishra P, Banergee HD (1988) J Mater Sci 23:21. doi: https://doi.org/10.1007/BF01174029 CrossRefGoogle Scholar
  7. 7.
    Rahman IA, Ismail J, Osman H (1997) J Mater Chem 7:1505CrossRefGoogle Scholar
  8. 8.
    Concha R, Maria DA, Jose MC (1996) J Am Ceram Soc 79:2012CrossRefGoogle Scholar
  9. 9.
    Venezia AM, La Parola V (2001) J Solid State Chem 161:373CrossRefGoogle Scholar
  10. 10.
    Naskar MK, Chatterjee M (2004) J Eur Ceram Soc 24:3499CrossRefGoogle Scholar
  11. 11.
    Lenz GR, Martell AE (1964) Biochemistry 3:750CrossRefGoogle Scholar
  12. 12.
    Zhu B, Fan T, Zhang D (2008) J Hazard Mater 153:300CrossRefGoogle Scholar
  13. 13.
    Wong KK, Lee CK, Low KS, Haron MJ (2003) Chemosphere 50:23CrossRefGoogle Scholar
  14. 14.
    IARC (1993) IARC monographs on the evaluation of carcinogenic risks to humans 58:41Google Scholar
  15. 15.
    Shinohara Y, Kohyama N (2004) Ind Health 42:277CrossRefGoogle Scholar
  16. 16.
    Kapur PC (1935) Powder Technol 44:63CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2008

Authors and Affiliations

  1. 1.Joining and Welding Research InstituteOsaka UniversityIbarakiJapan

Personalised recommendations