, Volume 43, Issue 19, pp 6546–6555 | Cite as

Influence of processing on the microstructure of Cu–8Cr–4Nb

  • L. G. Vettraino
  • J. L. Heelan
  • C. A. Faconti
  • J. L. Walley
  • A. Garg
  • J. R. Groza
  • J. C. GibelingEmail author
Article

Abstract

The particle-strengthened Cu–8 at.%Cr–4 at.%Nb alloy is processed by consolidation of atomized powders followed by extrusion to obtain bars and rolling to produce sheets. Comparison of copper matrix grain and second-phase particle structures in both extruded and rolled Cu–8Cr–4Nb was performed. Extruded material displayed locally banded arrangements of Cr2Nb particles, while the distribution of particles was more uniform in rolled material. Mean Cr2Nb particle sizes were found to be essentially the same for both processing methods. Non-spherical particles in the extruded alloy showed some preferred orientation, whereas the rolled material displayed a more uniform particle orientation distribution. Extruded material exhibited a dual grain size distribution with smaller grains in banded regions. The mean grain size of 1.36 μm in extruded material was larger than the 0.65 μm grain size of rolled material. A [101] texture was evident in extruded material, whereas the rolled material was only slightly textured along the [001] and [111] directions. The processing differences for the rolled and extruded forms give rise to different microstructures and hence higher creep strength for the extruded material in the temperature range of 773–923 K.

Keywords

Creep Strength Extrusion Direction Interparticle Spacing Copper Matrix Rolled Material 

Notes

Acknowledgements

This work was funded as part of NASA Grant NCC3-859. The authors wish to thank Drs. David Ellis and Michael Nathal for their continuing support and advice regarding this project. The authors also wish to express their appreciation to Dr. George Kaschner of the Los Alamos National Laboratory for the kind use of the SEM/EBSD equipment, which resulted in the OIM images used in this study.

References

  1. 1.
    Anderson KR, Groza JR, Dreshfield RL, Ellis D (1993) Mater Sci Eng A 169:167–175CrossRefGoogle Scholar
  2. 2.
    Venkatraman M, Neumann JP (1986) Bull Alloy Phase Diagrams 5:462–466. doi: https://doi.org/10.1007/BF02867811 CrossRefGoogle Scholar
  3. 3.
    (a) Chakrabati DJ, Laughlin DE (1982) Bull Alloy Phase Diagrams 2:507; (b) Chakrabati DJ, Laughlin DE (1984) Bull Alloy Phase Diagrams 5:59, 99Google Scholar
  4. 4.
    Thoma DJ, Perepezko JH (1992) Mater Sci Eng A 156:97–108CrossRefGoogle Scholar
  5. 5.
    Decker MW, Groza JR, Gibeling JC (2004) Mater Sci Eng A 369:101–111CrossRefGoogle Scholar
  6. 6.
    Ellis DL, Michal GM (1999, Sep) NASA Contractor Report 185144Google Scholar
  7. 7.
    Ellis DL, Misra AK, Dreshfield RL (1996) In: Thompson AW, Moody NR (eds) Proceedings of the fifth international conference on the effect of hydrogen on the behavior of materials. TMS, Warrendale, pp 1049–1056Google Scholar
  8. 8.
    Anderson KR, Groza JR, Dreshfield RL, Ellis D (1995) Metall Mater Trans A 26:2197–2206. doi: https://doi.org/10.1007/BF02671235 CrossRefGoogle Scholar
  9. 9.
    Anderson KR, Groza JR (2001) Metall Mater Trans A 32:1211–1224. doi: https://doi.org/10.1007/s11661-001-0130-x CrossRefGoogle Scholar
  10. 10.
    Decker MW (2003) Constant stress creep properties of extruded Cu-8Cr-4Nb (GRCop-84). M.S. Thesis, University of California, DavisGoogle Scholar
  11. 11.
    Kelly PM (1973) Int Met Rev 18:31CrossRefGoogle Scholar
  12. 12.
    Shewmon PG (1983) Transformations in metals. J. Williams Book Company, Oklahoma, pp 69–125Google Scholar
  13. 13.
    Ellis DL, Garg A (to be published) Annealing behavior of GRCop-84. NASA Technical Memorandum. NASA Glenn Research Center, Cleveland, OHGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2008

Authors and Affiliations

  • L. G. Vettraino
    • 1
  • J. L. Heelan
    • 1
  • C. A. Faconti
    • 1
  • J. L. Walley
    • 1
  • A. Garg
    • 2
  • J. R. Groza
    • 1
  • J. C. Gibeling
    • 1
    Email author
  1. 1.Department of Chemical Engineering and Materials ScienceUniversity of CaliforniaDavisUSA
  2. 2.Glenn Research CenterNASAClevelandUSA

Personalised recommendations