Pb(Zr0.95Ti0.05)O3 powders prepared by aqueous Pechini method using one-step pyrolysis process: characterization and porous ceramics
- 134 Downloads
Zr-riched lead zirconate titanate, Pb(Zr0.95Ti0.05)O3 (PZT 95/5) powders were prepared using lead acetate, zirconium oxynitrate, and titanium sulfate by aqueous Pechini method. The chelation behaviors of metallic ions and citric acid were investigated and the development of the phase formation of perovskite structure was detected. PZT 95/5 powders were obtained directly from the as-synthesized gels by one-step pyrolysis process at 450 °C for 10 h. Perovskite phase was formed at about 450 °C and no distinct intermediates were obtained. There were some carbonates as impurities but they did not affect the formation of the complete perovskite phase of PZT 95/5 ceramics after sintering at 1,100–1,150 °C for 2 h. The decomposition of few organic residues among the one-step pyrolyzed powders could form uniform porous structure and the formation mechanism of porous ceramics was also presented.
KeywordsOrganic Residue Lead Acetate Lead Zirconate Porous Ceramic Pechini Method
This work was supported by the fund of the State Key Laboratory of Solidification Processing in Northwestern Polytechnical University (NPU), China.
- 5.Pechini MP (1967) USP 3 330 697Google Scholar
- 6.Lessing PA (1989) Am Ceram Soc Bull 68:1002Google Scholar
- 9.Kakegawa K, Arai K, Sasaki Y, Tomizawa T (1988) J Am Ceram Soc 71:C49Google Scholar
- 16.Petrykin V, Kakihana M (2005) Handbook of sol–gel science and technology. Processing, characterization and applications, vol I, Sol–Gel processing. Kluwer Academic Publishers, p 85Google Scholar
- 19.Nakamoto K (1986) Infrared and Raman spectra of inorganic and coordination compounds, 4th edn. Wiley, New York, p 231Google Scholar
- 23.Yang P, Moore RH, Lockwood SJ, Tuttle BA, Voigt JA, Scofield TW (2003) SAND 2003–3866Google Scholar