Abstract

The mechanical properties of Al–Si alloys are strongly related to the size, shape and distribution of eutectic silicon present in the microstructure In order to improve mechanical properties, these alloys are generally subjected to modification melt treatment, which transforms the acicular silicon morphology to fibrous one resulting in a noticeable improvement in elongation and strength. Improper melt treatment procedures, fading and poisoning of modifiers often result in the structure which is far from the desired one. Hence it is essential to assess the effectiveness of melt treatment before pouring. A much investigated reliable thermal analysis technique is generally used for this purpose. The deviation from the standard curve in thermal analysis helps in assessing the level of refinement of the Si structure. In the present review an attempt is made to discuss various aspects of modification, including mechanism, interaction of defects and non-destructive assessment by thermal analysis.

Keywords

Aluminium Silicon Alloy Eutectic Silicon Eutectic Growth Eutectic Solidification Hypereutectic Alloy 

Notes

Acknowledgement

Authors thank the Ministry of Human Resource Development (MHRD), Government of India, New Delhi for funding the project on ‘Non-destructive Microstructure Control of Al–Si Alloys’.

References

  1. 1.
    Davis JR (1990) ASM hand book (Formerly, vol 2, 10th edn, Metals hand book). ASM, Metals Park, OH, pp 123–151, 166–168Google Scholar
  2. 2.
    Dwivedi DK (2002) IE (I) Journal-MM 83(10):46Google Scholar
  3. 3.
    Hatch JE (1984) Aluminum properties and physical metallurgy. ASM, Metals Park, OH, pp 1–104, 200–241, 320–350Google Scholar
  4. 4.
    Davis JR (1988) Metals hand book, vol. 15, 9th edn. ASM, Metals Park, OH, pp 55–87, 159–168, 743–753Google Scholar
  5. 5.
    Hinojosa JAG, González CR, González GM, Houbaert Y (2003) J Mat Proc Tech 143–144(20):306Google Scholar
  6. 6.
    Ogris E, Wahlen A, Luchinger H, Uggowitzer PJ (2002) J Light Metals 2:263Google Scholar
  7. 7.
    Peña BS (2006) J A Mater Charact 57:218Google Scholar
  8. 8.
    Cornell R, Bhadeshia HKDH (2007) https://doi.org/www..msm.cam.ac.uk/phase-trans/abstracts/M7-8.html. Accessed 20 July 2007
  9. 9.
    Dinsdale T, Quested PN (2004) J Mat Sci 39:7221Google Scholar
  10. 10.
    Wang R, Lu a W, Hogan LM (2003) Mat Sci Engg A 348:289Google Scholar
  11. 11.
    Dahle AK, Nogita K, McDonald SD, Luc DL (2005) Mat Sci Engg A 413–414:243Google Scholar
  12. 12.
    Gruzleski E, Closset BM (1990) The treatment of liquid Al–Si alloys. AFS Inc., Des Plaines, IL, pp 1–68, 95–157, 213–237Google Scholar
  13. 13.
    Wang J, He S, Sun B, Shu KL, Zhou Y (2002) Mat Sci Engg A338:101Google Scholar
  14. 14.
    Ho CR, Cantor R (1995) Acta Mettal Mater 43(8):3231Google Scholar
  15. 15.
    Knuutinen A, Nogita K, McDonald SD, Dahle AK (2001) J Light Metal 1:229Google Scholar
  16. 16.
    Mulazimoglu MH, Tenekerdjiev N, Closset BM, Gruzleski JE (1993) Cast Metals 6(1):16Google Scholar
  17. 17.
    Schaffer PL, Arnberg L, Dahle AK (2006) Scripta Materialia 54:677Google Scholar
  18. 18.
    Xiufang B, Weimin W, Jingyu Q (2001) Mater Charact 46:25Google Scholar
  19. 19.
    McDonald SD, Nogita K, Dahle AK (2004) Acta Materialia 52:4273Google Scholar
  20. 20.
    Huiyuan G, Yanxiang L, Xiang C, Xue W (2005) Scripta Materialia 53:69Google Scholar
  21. 21.
    Nogita K, Dahle AK (2003) Scripta Materialia 48:307Google Scholar
  22. 22.
    Qiyang L, Qingchun L, Qiful L (1991) Acta Metallurgica 39(11):2497Google Scholar
  23. 23.
    Guthy HV (2002) Evolution of the eutectic microstructure in chemically modified and unmodified aluminum silicon alloys. M.Sc. Thesis, Worcester Polytechnic Institute, p 34Google Scholar
  24. 24.
    Shankar S, Riddle YW, Makhlouf MM (2004) Met Trans A 35a:3038Google Scholar
  25. 25.
    Dinnis CM, Taylor JA, Dahle AK (2005) Scripta Materialia 53:955Google Scholar
  26. 26.
    Dahle AK, Hillert M (2006) Met Trans.A 37A:1353Google Scholar
  27. 27.
    Shankar S, Makhlouf MM (2006) Met Trans A 37A:1353Google Scholar
  28. 28.
    Shankar S, Riddle YW, Makhlouf MM (2004) Acta Materialia 52:4447Google Scholar
  29. 29.
    Krai MV, Nakashima PNH, Mitchell DRG (2006) Met Trans A 37A:1987Google Scholar
  30. 30.
    Nogita K, McDonald SD, Dahle AK (2004) Philos Mag 84(17):1683Google Scholar
  31. 31.
    Nogita K, McDonald SD, Dahle AK (2004) Mater Forum 28:945Google Scholar
  32. 32.
    McDonald SD, Dahle AK, Taylor JA, Suohn DH (2004) Met Trans A 35A:1829Google Scholar
  33. 33.
    Kumar G, Hegde S, Prabhu KN (2007) J Mat Proc Tech 182:152Google Scholar
  34. 34.
    Nogita K, Yasuda H, Yoshida K, Uesugi K, Takeuchi A, Suzukic Y, Dahle AK (2006) Scripta Materialia 55:787Google Scholar
  35. 35.
    Dinnis CM, Dahle AK, Taylor JA (2005) Mat Sci Engg A 392:440Google Scholar
  36. 36.
    McDonald SD, Nogita K, Dahle AK (2006) J Alloy Compd 422(1–2):184Google Scholar
  37. 37.
    Martinez EJ, Cisneros MA, Valtierra S, Lacaze J (2005) Scripta Materialia 52:439Google Scholar
  38. 38.
    Lu SZ, Hellawell A (1987) Met Trans A 18A:1721Google Scholar
  39. 39.
    Hanna HO, Lu SZ, Hellawell A (1984) Met Trans A 15A:459Google Scholar
  40. 40.
    Gruzleski JE (1992) AFS Trans 64:673Google Scholar
  41. 41.
    Denton JR, Spittle JA (1985) Mat Sci Tech 1:305Google Scholar
  42. 42.
    Kim CB, Heine RW (1964) J Inst Metals 92:367Google Scholar
  43. 43.
    Criado AJ, Martinez JA, Calabres R (1997) Scripta Materialia 56(no. 1):47Google Scholar
  44. 44.
    Nogita K, Dahle AK (2001) Mater Charact 46:305Google Scholar
  45. 45.
    Heiberg G, Arnberg L (2001) J Light Metals 1:43Google Scholar
  46. 46.
    Heiberg G, Nogita K, Dahle AK, Arnberg L (2002) Acta Materialia 50:2537Google Scholar
  47. 47.
    Gowri S (1994) AFS Transactions 102(29):503Google Scholar
  48. 48.
    Mulazimoglu MH, Zaluska A, Paray F, Gruzleski JE (1997) Met Trans A 28A:1289Google Scholar
  49. 49.
    Suárez-Pen B, Lozano JA (2006) Scripta Materialia 54:1543Google Scholar
  50. 50.
    Tash M, Samuel FH, Mucciardi F, Doty HW (2007) Mat Sci Engg A 443:185Google Scholar
  51. 51.
    Cao X, Campbell J (2003) Met Trans A 34A:1403Google Scholar
  52. 52.
    McDonald SD, Dahle AK, Taylor JA, St.John DH (2004) Met Trans B 35B:1097Google Scholar
  53. 53.
    Dinnis CM, Taylor JA, Dahle AK (2006) Mat Sci Engg A 425:286Google Scholar
  54. 54.
    Dinnis CM, Taylor JA, Dahle AK (2006) Met Trans A 37A:3283Google Scholar
  55. 55.
    Dinnis CM, Otte MO, Dahle AK, Taylor JA (2004) Met Trans A 35A:3531Google Scholar
  56. 56.
    Knuutinen A, Nogita K, McDonald SD, Dahle AK (2001) J Light Metals 1:241Google Scholar
  57. 57.
    Liu L, Samuel M, Samuel FH, Doty HW, Valtierra S (2003) J Mat Sci 38:1255Google Scholar
  58. 58.
    Lee PD, Sridhar S (2000) Int J Cast Metals Res 13:185Google Scholar
  59. 59.
    Miresmaeili SM, Campbell J, Shabestari SG, Boutorabi SMA (2005) Met Trans A 36A:2341Google Scholar
  60. 60.
    Campbell J (2006) Met Trans B 37B:857Google Scholar
  61. 61.
    Fox S, Campbell J (2000) Scripta mater 43:881Google Scholar
  62. 62.
    Divandari M, Campbell J (2004) Int J Cast Met Res Vl17(3):182Google Scholar
  63. 63.
    Haquea MM, Ismail AF (2005) Journal of Mat Pros Tech 162–163:312Google Scholar
  64. 64.
    Moustafa MA, Lepage C, Samuel FH, Doty HW (2003) Int J Cast Metals Res 15:609Google Scholar
  65. 65.
    Haque MM, Maleque MA (1998) Mat Pros Tech 77:122Google Scholar
  66. 66.
    Lua L, Nogita K, Dahle AK (2005) Mat Sci Engg A 399:244Google Scholar
  67. 67.
    Lua L, Dahle AK (2006) Mat Sci Engg A 435–436:288Google Scholar
  68. 68.
    Liao H, Sun G (2003) Scripta Materialia 48:1035Google Scholar
  69. 69.
    Liu X, Wu Y, Bian X (2005) J Alloy Compd 391(1–2):90Google Scholar
  70. 70.
    Wang W, Gruzleski JE (1989) Mat Sci Tech 5:471Google Scholar
  71. 71.
    Gruzleski JE, Closset BM (1990) The treatment of liquid Al-Si alloys. AFS Inc., Des Plaines, IL, p 39Google Scholar
  72. 72.
    Lu SZ, Hellawell A (1995) JOM 47(2):38Google Scholar
  73. 73.
    Morice J, Portalier R (1984) In: Proceedings of the AFS/CMIConference, Illinios, Dec 11–12, p 37Google Scholar
  74. 74.
    Hernández FCR, Sokolowski JH (2006) J Alloy Compd 419(1–2):180Google Scholar
  75. 75.
    Valdes AF, Agullar MER, Bocardo JCE (1993) Mat Des 14(4):223Google Scholar
  76. 76.
    Tuttle BL (1984) In: Proceedings of the AFS/CMI Conference, IL p 1Google Scholar
  77. 77.
    Chen X, Geng H, Li Y (2006) Mat Sci Engg A419:283Google Scholar
  78. 78.
    Prabhu KN, Karanth S, Udupa KR (1999) Indian Foundry J 45(9):177Google Scholar
  79. 79.
    Gruzleski JE, Closset BM (1990) The treatment of liquid Al-Si alloys. AFS Inc., Des Plaines, IL, pp 1–68, 95–157, 213–237Google Scholar
  80. 80.
    Hernandez FCR, Djurdjevic MB, Kierkus WT, Sokolowsk JH (2005) Mat Sci Engg A 396:271Google Scholar
  81. 81.
    Closset B, Pirie K, Gruzleski JE (1984) AFS Trans 92(27):123Google Scholar
  82. 82.
    Bamberger M, Weiss BZ, Stupel MM (1987) Mat Sci Tech 3:49Google Scholar
  83. 83.
    Apelian D, Sigworth GK, Whaler KR (1984) AFS Trans 92:297Google Scholar
  84. 84.
    Hegde S, Kumar G, Prabhu KN (2006) Int J Cast Metals Res 19(4):254Google Scholar
  85. 85.
    Djurdjevic M, Jiang H, Sokolowski J (2001) Mater Charact 46:31Google Scholar
  86. 86.
    Heusler L, Schneider W (2002) J Light Metals 2:17Google Scholar
  87. 87.
    Apelian D, Cheng JJA (1984) AFS Trans 92(27):797Google Scholar
  88. 88.
    Samuel AM, Quellet P, Samuel FH, Doty HW (1997) AFS Trans 156:951Google Scholar
  89. 89.
    Ananthanarayanan L, Samuel FH (1992) AFS Trans 100(141):383Google Scholar
  90. 90.
    Ceylan M, Akaoy I, Kuzucu V, Balo SN (1997) Mat Pros Tech 65:31Google Scholar
  91. 91.
    Gowri S (1994) AFS Trans 102(29):503Google Scholar
  92. 92.
    Piasentini F, Bonollo F, Tiziani A (2006) Met Sci Tech 23(2):11Google Scholar
  93. 93.
    Dioszegi A, Svensson IL (2005) Trans Ind Inst Met 58(4):611Google Scholar

Copyright information

© Springer Science+Business Media, LLC 2008

Authors and Affiliations

  1. 1.Department of Metallurgical & Materials EngineeringNational Institute of Technology KarnatakaSurathkalIndia

Personalised recommendations