Oxidation of SiC powders for the preparation of SiC/mullite/alumina nanocomposites

  • Jingyan He
  • Clive Brian Ponton
Rees Rawlings Festschrift

Abstract

The oxidation behaviour of two types of SiC powder of differing particle size and morphology distribution has been studied in the present work; one submicron-sized and the other micron-sized. It has been observed that the onset-temperature for significant oxidation of the SiC powder of smaller particle size is much lower than that for the SiC powder of larger particle size; namely, about 760 °C as compared with about 950 °C. Furthermore, the rate and extent of oxidation of the former SiC powder is much higher than that of the latter SiC powder. Interestingly, however, the SiC powder of smaller particle size exhibits more controllable oxidation behaviour in the context of the preparation of SiC/mullite/alumina nanocomposites, i.e., in terms of the extent of oxidation, and hence the amount of silica formed as an encapsulating outer layer and the resulting core SiC particle size, than the SiC powder of larger particle size. The SiO2 layer formed was amorphous when the SiC powders were oxidized below 1,200 °C, but crystalline in the form of cristobalite when they were oxidized above 1,200 °C. Since the presence of amorphous silica can accelerate the sintering of the nanocomposite, oxidation of the chosen SiC powder should thus take place below 1,200 °C.

Keywords

Boehmite Oxidation Behaviour Oxidation Temperature Cristobalite Loose Powder 

Notes

Acknowledgements

The work presented here is a part of Jingyan He’s PhD research undertaken in the Department of Metallurgy and Materials and the IRC in Materials Processing at the University of Birmingham, under the supervision of C. B. Ponton. Thus, the authors are grateful to the Department/IRC for the provision of laboratory facilities and to all the technical and academic staff therein for the help extended to Jingyan during his PhD. This work would not have been initiated by C. B. Ponton, had his own enthusiasm for materials science not been encouraged and nurtured in the direction of ceramic materials by Professor Rees Rawlings, first via undergraduate lectures and labs, then during a final-year undergraduate project that was followed by a PhD on CMAS glass-ceramics (both supervised by Rees Rawlings and Dr Philip Rogers), culminating in his doing post-doctoral research on bioactive apatite-containing glass-ceramics with Rees, after which he obtained an academic post in the IRC in Materials Processing/Department of Metallurgy and Materials at the University of Birmingham.

References

  1. 1.
    Shi Z, Lee J, Zhang D, Lee H, Gu M, Wu R (2001) J Mater Tech 110:127CrossRefGoogle Scholar
  2. 2.
    Vaughn WL, Maahs HG (1990) J Am Ceram Soc 73(6):1540CrossRefGoogle Scholar
  3. 3.
    Ramberg CE, Cruciani G, Spear KE, Tressler RE, Ramberg CF Jr (1996) J Am Ceram Soc 79(3):730Google Scholar
  4. 4.
    Ogbuji LUJT (1997) J Am Ceram Soc 80(6):1544CrossRefGoogle Scholar
  5. 5.
    Lin YJ, Chen LJ (2000) Ceram Int 26:593CrossRefGoogle Scholar
  6. 6.
    Deal BE, Grove AS (1965) J Appl Phys 36(12):3770CrossRefGoogle Scholar
  7. 7.
    Opila EJ (1994) J Am Ceram Soc 77(3):730CrossRefGoogle Scholar
  8. 8.
    Holz D, Claussen N (1995) Ceram Eng Sci Proc 16(1):252CrossRefGoogle Scholar
  9. 9.
    Wu S, Claussen N (1994) J Am Ceram Soc 77(11):2898CrossRefGoogle Scholar
  10. 10.
    Sakka Y, Bidinger DD, Aksay IA (1995) J Am Ceram Soc 78(2):479CrossRefGoogle Scholar
  11. 11.
    Carter RE (1961) J Chem Phys 34:2010CrossRefGoogle Scholar
  12. 12.
    Liu DM (1997) Ceram Int 23:425CrossRefGoogle Scholar
  13. 13.
    Costello JA, Tressler RE (1986) J Am Ceram Soc 69(9):674CrossRefGoogle Scholar
  14. 14.
    Singhal SC (1976) J Mater Soc 29:1246CrossRefGoogle Scholar
  15. 15.
    Pultz WW (1967) J Phys Chem 71(13):4556CrossRefGoogle Scholar
  16. 16.
    Villegas M, Sierra T, Lucas F, Fernández JF, Caballero AC (2007) J Euro Cer Soc 27:861–865CrossRefGoogle Scholar
  17. 17.
    Kaya C (1999) PhD thesis, University of BirminghamGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2008

Authors and Affiliations

  1. 1.Institute for Materials ResearchUniversity of LeedsLeedsUK
  2. 2.Department of Metallurgy and MaterialsUniversity of BirminghamEdgbaston, BirminghamUK

Personalised recommendations