Ultraporous monoliths of alumina prepared at room temperature by aluminium oxidation
- 255 Downloads
The oxidation of aluminium through a mercury film usually leads to unorganized filaments or fibrous powders of hydrated alumina. Here, we show that the addition of a small amount of silver in the mercury considerably modifies the growth process, and that large sized monoliths can be obtained through a new process. Regular growth can be maintained at a typical rate of 2.1 μm s−1 (∼0.75 cm/h) for several hours. The samples consist of tangled nanometric fibres and have an open porosity of 99%. The influence of various parameters has been studied and optimal conditions for regular growth have been determined. Anhydrous alumina monoliths with a nanometric microstructure and a high-specific area are obtained after thermal treatments that remove water.
KeywordsAluminium Plate Porous Alumina Hydrated Alumina Alumina Fiber Liquid Mercury
The authors are grateful to Mr. Dubos and Mr. Leroy from the Centre de Recherche Pechiney-Alcan (Voreppe, France) and Mr. Fernandez (Alcan, Mercus, France) for supplying us with high-purity and doped aluminium samples.
- 1.Wislicenus H (1908) Kolloid-Z 2:11Google Scholar
- 3.Bodle WW, Attari A, Serauskaus R (1986) In: Proceedings of sixth international conference on liquified natural gas, Kyoto, Japan, p 1Google Scholar
- 4.Pinnel MR, Bennet JE (1972) J Mater Sci 7:1016, doi: https://doi.org/10.1007/BF00550065
- 8.Beauvy M, Vignes J-L, Michel M, Mazerolles L, Frappart C, Di Costanzo T, patent (CNRS-CEA) n°FR2847569, 28-05-2004Google Scholar
- 11.Badkar PA, Bailley JE (1976) J Mater Sci 11:1794, doi: https://doi.org/10.1007/BF00708257
- 13.Massalski TB (1990) Binary alloy phase diagrams, 2nd edn. A.S.M. Int. Materials Park, Ohio, vol 3, p 2138, vol 1, p 43Google Scholar
- 15.Mazerolles L, Michel D, Di Costanzo T, Vignes J-L (2002) Ceram Trans 135:227Google Scholar
- 28.Livage J, Coradin T, Roux C (2001) J Phys: Cond Matter 13:R673Google Scholar