Development of Fe3C, SiC and Al4C3 compounds during mechanical alloying

  • M. H. EnayatiEmail author
  • M. Seyed-Salehi
  • A. Sonboli
Article

Abstract

Mechanical alloying process, as a solid-state technique, is a very useful method for fabrication of high melting point compounds like metal carbides and nitrides, which additionally have nanocrystalline structure with improved properties. In this work the development of several carbides including iron, aluminium and silicon carbides by the mechanical alloying process and the effect of subsequent heat treatment were investigated. Mixtures of elemental powders of Fe–C, Si–C and Al–C were mechanically alloyed, nominally at room temperature using a laboratory planetary ball mill. Structural changes of samples were studied by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results showed that the aluminium carbide (Al4C3) could not be synthesized by mechanical alloying process alone, even after long milling times. A suitable subsequent heat treatment was required to allow Al–C reaction to take place kinetically. In contrast mechanical alloying of Fe–C as well as Si–C systems directly led to the formation of Fe3C and SiC carbides after sufficient milling time. In all cases the end product had a nanosized structure.

Keywords

Powder Particle Mechanical Alloy Milling Time Subsequent Heat Treatment Metal Carbide 

References

  1. 1.
    Toth LE (1971) In: Transition metal carbides and nitrides. Academic Press, New YorkGoogle Scholar
  2. 2.
    Calka A (1993) Key Eng 81–83:17CrossRefGoogle Scholar
  3. 3.
    Tanaka T, Ishihara KN, Shingu PH (1992) Met Trans 23A:2431CrossRefGoogle Scholar
  4. 4.
    Suryanarayana C (2001) Prog Mater Sci 46:1CrossRefGoogle Scholar
  5. 5.
    Enayati MH, Zakeri M (2004) Int J Iron Steel Soc Iran 1:24Google Scholar
  6. 6.
    Culity BD (1978) In: Elements of X-ray diffraction, 2nd edn. Addison-Welsey, Reading, p 102Google Scholar
  7. 7.
    Jangg G (1989) In: New materials by mechanical alloying technology. DGM, Oberursel, p 39Google Scholar
  8. 8.
    Wu NQ, Wu JM, Wang GX, Li ZZ (1997) J Alloys Compd 260:121CrossRefGoogle Scholar

Copyright information

© Springer Science+Business Media, LLC 2007

Authors and Affiliations

  1. 1.Department of Materials EngineeringIsfahan University of TechnologyIsfahanIran

Personalised recommendations