Pre-yield tensile set of a semi-crystalline polymer, its blend and composite
- 857 Downloads
Tensile set was studied at low strains on polypropylene, aliphatic polyketone, rubber toughened blends and CaCO3 particle toughened composites. The rubber in the rubber toughened blends had a particle size of 0.7 μm. The CaCO3 particles had a size of 0.7 μm and had been coated with stearic acid. Step-cyclic loading was applied in 1% strain incrementals at a strain rate of 10−2 s−1. The maximum strain applied was 20%. The temperature of the test bar was studied with an infra-red camera. Pre-yield deformation is normally assumed to take place in a nonlinear elastic manner. However, for polypropylene and polyketone elastoplastic deformation starts at low strains. For PP the onset of tensile set is at very low strains and increases with strain. The tensile set at the yield point was only 50% and at the drawing strain 100%. Polyketone had a similar tensile set development but shifted to slightly higher strains. Here too the tensile set at the yield point was about 50% and at the drawing strain 100%. The temperature of the non yielded material was found to rise in polyketone a 7 °C.
The rubber toughened blends had at low strains a higher tensile set, but after the yield strain the set was similar to the base polymer. At 5% strain the tensile set increased with rubber content. The sub micron CaCO3 particle toughened composites increased the tensile set too. The tensile set is a simple technique for studying the pre-yield behaviour of multi phase systems.
KeywordsCavitation Rubber Particle Yield Strain Rubber Content CaCO3 Particle
The mechanical behaviour of polymers strongly depends on parameters like temperature and strain rate and typically for this is the yield strength . The yield point is conventionally determined, by the Considére’s construction , at the point of maximum stress in the nominal stress strain curve. It is generally considered that below the yield strain the deformation is nonlinear elastic  and at the yield point the polymer starts to deform plastically. The plastic deformation is usually by shear yielding. Semi-crystalline polymers have a two phase morphology and the plastic deformation invariably takes place in an inhomogeneous manner. The yielding in semi crystalline polymers is very often accompanied by necking with an appreciable temperature rise [4, 5, 6, 7, 8]. For PE and PP it has been shown that the assumption that below the yield strain that the deformation in tensile is just nonlinear elastic, it too simple [9, 10, 11, 12]. In cyclic deformation tests at low strains considerable tensile set was observed. This deformation has been called elastoplastic deformation and it is strain controlled. It is thought that this deformation is due to transformations in the amorphous phase and by crystalline slip processes. If at low strains plastic deformation is taking place than the sample temperature should increase.
In toughened blends in the pre-yield strain region, cavitation of the rubber takes place. On cavitation of the rubber particles the yield strain is not changed but the yield stress is considerably lowered [7, 13]. As a consequence of this cavitation excessive shear yielding can take place. Interesting is to study whether in presence of rubber particles the pre-yield tensile set deformation is changed.
New is the toughening by sub micron sized rigid particles [14, 15, 16, 17]. The toughening mechanism here is the delamination of the rigid particles [15, 16, 17]. This toughening mechanism works well at low loadings (>20 vol%) but as yet not at high loadings [16, 17]. These composites have an increased modulus however their yield strength is considerable lowered. Interesting is to study whether in delamination of the submicron particles change the tensile set deformation in the pre-yield region.
In this paper the tensile set is studied in step-cyclic loading with 1% strain steps up to 20% strain. The materials studied are polypropylene, an aliphatic polyketone, a toughened blend of aliphatic polyketone and a toughened composite of aliphatic polyketone. The aliphatic polyketone is an interesting semi-crystalline polymer, similar in behaviour to PP however with a higher yield stress and a higher yield strain.
Polypropylene, Vestolen P7000, with an MFI at 190 °C of 2.4 dg/min, a modulus of 1,500 MPa, a yield stress of 34 MPa, a yield strain of 9% and a crystallinity of 45%, was kindly supplied by DSM.
The aPK has a glass transition temperature of approximately 15 °C and a melting temperature of 225 °C with a crystallinity of 35%.
Blends of this aPK and 0.7 μm rubber particles have been described . Rubber are in the form of core shell particles with polybutadiene core and SAN shell (Blendex 338, from GE Plastics). The aPK–CaCO3 composites used, were made with precipitated CaCO3 particles with a particle size of 0.7 mm and that had a stearic acid coating (Superflex from Mineral Technologies) .
Dumbbell shaped test samples, 4 mm thick, were obtained by injection moulding using an Arburg Allrounder 221-55-250 injection moulding machine. The barrel had a flat temperature profile with an injection pressure of 55 bar, holding pressure was kept at 45 bar and the total cycle time was approximately 22 s. For PP the barrel had a temperature of 200 °C and a mould temperature of 80 °C. The aPK materials had a barrel temperature of 240 °C and a mould temperature of 70 °C.
The test bars were dried at 80 °C under vacuum for 15 h, and kept under vacuum at room temperature after this drying step. Because of the physical ageing behaviour of polyketone, the aPK test samples were every 10th day heated to 80 °C for half an hour to rejuvenate the physical ageing. After this treatment the test bars were cooled down in a controlled manner in the oven and kept under vacuum. These test samples were not used in the first 2 days after a heat treatment since the physical ageing process is very fast in this period.
Normal tensile tests were conducted on dumbbell shaped specimens with a Zwick tensile Z02 tester. Test speed was 60 mm/min, which means a strain rate of 10−2 s−1. The strain was monitored with extensometers attached on the specimen. Standard engineering curves were obtained, the modulus was determined in the strain regime of 0.1–0.25% strain, the yield stress was taken at the first point were dε/dσ = 0.
Step-Cycle Testing experiments were conducted on a Zwick tensile tester type Z02, equipped with an extensometer. Staircase loading cycles were performed with cycles of 1% strain at a strain rate of 10−2 s−1. The cycles followed each other directly. After each cycle the tensile set of that cycle was calculated.
The temperature rise during fracture of specimens of thickness 4 mm was monitored using an infrared camera as specified elsewhere .
Results and discussion
In studying the temperature development during a tensile test a warming of the sample in the unnecked region was observed, suggesting a plastic deformation. Tensile set experiments were conducted to get more insight in this.
The tensile set (TS) increases steadily with strain. At the yield strain for PP at 9% and aPK at 13%, the TS is about 50% and a small transition is apparent. A 100% tensile set is reacted for PP at 22% and aPK at 34% strain and this is after the neck was fully developed. The differences tensile set between PP and aPK are small, the aPK has a higher yield and higher draw strains. The average tensile set once the sample has formed a neck is about 50%. The observed temperature increase in the unnecked part of the sample (Fig. 1) suggests that the deformation in the pre-yield region is elastoplastic. The tensile set values below the yield point are remarkable high but at the yield point not very high. Only at the drawing strain the deformation becomes fully plastic.
It is commonly assumed that below the yield point the deformation is elastic and above the yield threshold all the deformation is plastic. It is shown here that both assumptions are for the tensile test too simple. The tensile set is continuously rising from very small strains up to the where the drawing starts and at the yield point only a small change in tensile set is observed. From this it is clear that there is no real transition at the yield point. As the tensile set is accompanied with a temperature rise of the sample a plastic deformation is taking place. The plastic deformation can be due to the deformation of the crystalline domains and/or the amorphous phase [9, 10, 11, 12].
The TS of the blends increases with rubber content and this particular up to a 10% strain. The Increased TS suggests that on cavitation of the rubber, the matrix around the cavitated particles is locally extra deformed and the more rubber is present the stronger the effect is. Remarkable is that above a strain of 10% the blends behave similar to the homo polymer. Thus the special effects of the blends are at low strains, well below the yield strain of 13% and near the onset of cavitation (4%) as measured by the stress whitening.
As the TS values increases with rubber content this suggest that the amount of matrix material which is affected by the cavitation process is increased with rubber content.
The 16 vol% CaCO3 composite has a high toughness, however the 32 vol% not. This difference of toughness behaviour cannot be explained by the TS results as the TS at high contents does not show unusual behaviour. The TS increases stronger for the rubber blend than for the CaCO3 composite. This suggests that the cavitation of the rubber is more effective in changing the deformation behaviour than the delamination of the CaCO3 particles. This TS method is a useful in studying the effects of cavitation in blends and delamination in composites on the deformation behavior.
Tensile set test with 1% strain steps gives interesting information about the deformation at low strains. Well before the yield point is reached, the tensile set values increases and at the same time the temperature of the sample increases. At the yield point a small change in tensile set was observed, and a 100% tensile set was observed at the drawing strain. During drawing the deformation is fully plastic. A blend of aPK-rubber cavitates on straining, with as a result an increase in plastic deformation. The onset of cavitation is at low strains and increasing the rubber content increases the plastic strain. aPK–CaCO3 composites debond on straining with as a result a small increase in tensile set. This effect was strongest at 5–10% strain. The tensile set effects are stronger for the rubber blends than for the sub micron particles composites. The tensile set test is a sensitive method in studying the deformation processes at low strains.
This research was financed by Shell Research and Technology Centre Amsterdam. The authors would like to thank P.J. Fennis and dr. A.A. Smaardijk for their contribution and helpful discussions.
- 1.Ferry JD (1980) In: Viscoelastic Properties of Polymers. Wiley & Sons, NYGoogle Scholar
- 2.Kinloch AJ, Young RJ (1983) In: Fracture Behaviour of Polymers. Elsevier, LondonGoogle Scholar
- 3.Oleynik EF (1991) In: High Performance Polymers: Structure, Properties, Composites, Fibers. Hanser, Munich, p 79Google Scholar
- 4.Marshall I, Thompson AB (1954) Proc Roy Soc A 221:541Google Scholar
- 5.Müller FH (1952) Kolloidzeitschrift 126:65Google Scholar