Thermodynamically modeling the interactions of hydrogen, stress and anodic dissolution at crack-tip during near-neutral pH SCC in pipelines
- 367 Downloads
A thermodynamic model was developed to clarify the interactions of hydrogen, stress and anodic dissolution at crack-tip during near-neutral pH stress corrosion cracking in pipelines by comprehensively considering the electrochemical reactions occurring in the pipeline steel in deoxygenated, near-neutral pH solution. By analyzing the change of the free-energy of steel due to the presence of hydrogen and stress, it is demonstrated that a synergism of hydrogen and stress promotes the cracking of steel. The enhanced hydrogen concentration in the stressed steel significantly accelerates the crack growth. An exact expression of the hydrogen concentration factor, i.e., the dependence of anodic dissolution rate of steel at crack-tip on the hydrogen concentration, is essential at the quantitative prediction of the crack growth rate.
KeywordsCrack Growth Rate Stress Corrosion Crack Anodic Dissolution Pipeline Steel Stress Corrosion Crack Susceptibility
This work was supported by Canada Research Chairs Program and Natural Science and Engineering Research Council of Canada (NSERC).
- 1.Parkins RN (2000) In Corrosion’ 2000, Paper no. 363, Nace, HoustonGoogle Scholar
- 2.National Energy Board (1996) Report of public inquiry concerning stress corrosion cracking on Canadian Oil and Gas Pipelines, MH-2–95, NovemberGoogle Scholar
- 4.Fang BY, Atrens A, Wang JQ, Han EH, Zhu ZY, Ke W (2003) J Mater Sci 38:127, DOI: 10/1023/A:1021126202539Google Scholar
- 5.Cheng YF, Yang L, King F (2002) In International pipeline conference, Asme, CalgaryGoogle Scholar
- 6.King F, Jack TR, Chen W, Wang SH, Elboujdaini M, Revie W, Worthingham R, Dusek P, In Corrosion’ 2001, Paper no. 1214, NACE, HoustonGoogle Scholar
- 7.Parkins RN (1996) Delanty BS, In Proceedings of the ninth symposium on pipeline research, Catalogue no. L51746, PRCI, p 19-1Google Scholar
- 8.Plumtree A, Lambert SB, Sutherby R (1996) In Corrosion-deformation interactions CDI’ 96, European Federation of Corrosion Publications, The Institute of Materials Research, Nice, France, p 263Google Scholar
- 15.LI JCM, Oriani RA, Darken LS (1966) J Phys Chem 49:271Google Scholar