Characterization of Bi1.6Pb0.4Sr2Ca2Cu3Oy ceramic superconductor prepared via coprecipitation method at different sintering time

  • I. Hamadneh
  • S. A. Halim
  • C. K. Lee
Article

Abstract

The Bi(Pb)-2223 superconductor has been prepared via coprecipitation (COP) method from solutions of metal acetates and 2-propanol solution of oxalic acid at low temperature (0–2 °C). The metal oxalates powder was subjected to precalcination of 12 h at 730 °C, followed by 24 h calcination at 845 °C. The pelletized powder was sintered for 24, 48 and 100 h at 850 °C. The dominance of high-TC phase was observed for all samples as evidenced in the single step transition of (R–T) curves. The TC(R = 0) for samples sintered at 24, 48 and 100 h were 102, 102 and 104 K, respectively. XRD data showed the tetragonal structure for all samples followed by the enhancement of the 2223 phase as sintering time increased. Ac magnetic susceptibility measurements showed the improvement of the grain connectivity as sintering time increased. SEM micrographs showed large flaky grains of ∼7 μm in size and randomly distributed, which belong to 2223 phase. The degree of grains alignment increased as the sintering time increased.

Keywords

Oxalic Acid Sinter Time Metal Acetate Magnetic Field Increase Ceramic Superconductor 

Notes

Acknowledgements

The financial support of the IRPA Grant vote: 4-07-05-026 (High Temperature Superconductors) from the Ministry of Science, Technology and Innovation Malaysia is gratefully acknowledged. The authors would like to express their gratitude to electron microscopy unit at Institute of Biosciences (UPM) for rendering the facility of JEOL 6400 scanning electron microscopy (SEM).

References

  1. 1.
    Rouessac V, Wang J, Provost J, Desgardin G (1996) J Mat Sci 31:3387CrossRefGoogle Scholar
  2. 2.
    Chin TS, Huang TW, Lin WT, Wa NC, Chou YH, Wu TC, Wu PT, Yen HH (1988) Mat Res Soc Symo Proc 99:261CrossRefGoogle Scholar
  3. 3.
    Ciontea L, Boffa V, Petrisor T, Bruzzese R, Perte E, Alvani C (1996) Physica C 257:304CrossRefGoogle Scholar
  4. 4.
    Mao C, Zhou L, Sun X, Wu X (1997) Physica C 281:35CrossRefGoogle Scholar
  5. 5.
    Monica P, Alina T, Liliana P, Dragan N, Maria Z (1998) J Eur Ceram Soc 18:1265CrossRefGoogle Scholar
  6. 6.
    Rama Rao GV, Swaminathan K, Sreedharan OM, Venkadesan S, Mannan SL (1998) J Mater Sci 33:1511CrossRefGoogle Scholar
  7. 7.
    Halim SA, Khawaldeh SA, Mohamed SB, Azhan H (1999) Mat Chem & Phys 61:251CrossRefGoogle Scholar
  8. 8.
    Halim SA, Khawaldeh SA, Azhan H, Mohamed SB (2000) J Mat Sci 35:3043CrossRefGoogle Scholar
  9. 9.
    Prker SP (1987) Solid state physics source book. McGraw-Hill Book Company, New York, p 151Google Scholar
  10. 10.
    Badica P, Aldica G, Bunescu MC, Nemyarovsky AV (2000) J Mater Sci Lett 19:561CrossRefGoogle Scholar
  11. 11.
    Hsueh YW, Chang SC, Liu RS, Woodall L, Gerards M (2001) Mater Res Bull 36:1653CrossRefGoogle Scholar
  12. 12.
    Driessche IV, Buekenhoudt A, Konstantinov K, Bruneel E, Hoste S (1996) Anal Appl Supercond 4:185CrossRefGoogle Scholar
  13. 13.
    Matsushita T, Suzuki A, Kishida T, Okuda M, Naito H (1994) Supercond Sci Technol 7:222CrossRefGoogle Scholar
  14. 14.
    Emmen JH, Barbers VAM, De Jonge WJ, Steen CVD, Dalderop JHJ, Geppart PMA, Kopinga K (1989) J Less Common Metals 151:63CrossRefGoogle Scholar
  15. 15.
    Ambegaokar V, Baratoff A (1963) Phys Rev Lett 10:486CrossRefGoogle Scholar
  16. 16.
    Azhan H (1999) Effect of Sn doping and heat treatment on Bi–Sr–Ca–Cu–O superconducting ceramics. Ph.D Thesis at Physics Department, Faculty of Science, Universiti Putra Malaysia, pp 218–221Google Scholar

Copyright information

© Springer Science+Business Media, LLC 2006

Authors and Affiliations

  1. 1.Department of ChemistryFaculty of Science, Universiti Putra MalaysiaSerdang, SelangorMalaysia
  2. 2.Department of PhysicsFaculty of Science, Universiti Putra MalaysiaSerdang, SelangorMalaysia

Personalised recommendations